US4369231A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of application, and product thereof
Assignee: Reeves Brothers Inc
•
Filing: 1981-08-04
•
Granted: 1983-01-18
•
Expires: 2001-08-04
Abstract
Abstract The present invention relates to a unique chemical formulation used in the manufacture of substantially wind-resistant, water-repellent fabrics. The formulation comprises a silicone polymer catalyzed with a tin compound and optionally includes acetic acid and an aromatic solvent. A method for treating fabrics includes depositing the unique formulation on a taut fabric, uniformly distributing it across the width of the fabric and curing that product. Either before or after that treatment, the fabric is padded with or dipped in a bath of silicone or hydrofluorocarbon. Excess solution is removed. Last, the multicoated fibers of the fabric are compressively shrunk. A substantially wind and water-resistant fabric is produced that is not only porous and soft but also durable.
Inventors
- 👤 George C. West
- 👤 William F. Polfus
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:38
CPC Classifications
D; D06; D06M; D06M15/00; D06M15/19; D06M15/37; D06M15/643; C; C09; C09D; C09D183/00; C09D183/04; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/3154; Y10T428/31652; Y10T428/31663; Y10T442/00; Y10T442/20; Y10T442/2164; Y10T442/218; Y10T442/2213
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
179 words
A process for coating substrates characterized by: (a) depositing on a taut substrate a composition comprising (1) a poly dimethyl siloxane being present in an amount about 95.3 percent by weight of the composition, (2) a dibutyl tin dilaurate catalyst being present in an amount about 0.7 percent by weight of the composition, (3) acetic acid being present in an amount about 1.0 percent by weight of the composition, and (4) an aromatic solvent being present in an amount about 3.0 percent by weight of the composition, or (1) a poly dimethyl siloxane being present in an amount from about 93 to about 99% by weight of the composition, and (2) a tin catalyst being present in an amount from about 0.5 to about 1.5% by weight of the composition, (b) uniformly distributing the deposited composition on one surface of the substrate, (c) curing the substrate from (b), (d) padding the substrate with a solution selected from a silicone or a fluorocarbon solution, and (e) compressing the substrate whereby it is substantially wind-resistant, water-repellent and has a good handle.
Claim 2
Dependent Claim
179 words
A process for coating substrates characterized by: (a) depositing on a taut substrate a composition comprising (1) a poly dimethyl siloxane being present in an amount about 95.3 percent by weight of the composition, (2) a dibutyl tin dilaurate catalyst being present in an amount about 0.7 percent by weight of the composition, (3) acetic acid being present in an amount about 1.0 percent by weight of the composition, and (4) an aromatic solvent being present in an amount about 3.0 percent by weight of the composition, or (1) a poly dimethyl siloxane being present in an amount from about 93 to about 99% by weight of the composition, and (2) a tin catalyst being present in an amount from about 0.5 to about 1.5% by weight of the composition, (b) uniformly distributing the deposited composition on one surface of the substrate, (c) curing the substrate from (b), (d) padding the substrate with a solution selected from a silicone or a fluorocarbon solution, and (e) compressing the substrate whereby it is substantially wind-resistant, water-repellent and has a good handle.
Claim 3
Dependent Claim
19 words
The process of claim 1 further characterized in that the substrate is padded before the composition is deposited thereon.
Claim 4
Dependent Claim
19 words
The process of claim 1 further characterized in that the composition is deposited on both sides of the substrate.
Claim 5
Dependent Claim
16 words
The process of claim 1 further characterized in that the substrate is a closely woven fabric.
Claim 6
Dependent Claim
27 words
The process of claim 4 further characterized in that the fabric has a warf of at least about 90 and a weft of at least about 68.
Claim 7
Dependent Claim
18 words
The process of claim 4 further characterized in that the substrate is a blend of polyester and cotton.
Claim 8
Dependent Claim
8 words
A product from the process of claim 1.
Claim 9
Dependent Claim
116 words
A process for coating a woven fabric comprising the steps of: (a) Depositing on a taut fabric a coating composition having a viscosity up to about 100,000 cps and consisting essentially of: 1. a dimethyl siloxane component present in an amount from about 93 to 99 percent by weight of the composition, and 2. a tin catalyst present in an amount from about 0.5 to about 1.5 percent by weight of the composition, (b) uniformly distributing the deposited coating composition on the surface of the fabric, (c) curing the fabric from b, and (d) padding the fabric with a solution selected from a silicone or a fluorocarbon solution, whereby the fabric is substantially wind-resistant and water-repellent.
Claim 10
Dependent Claim
116 words
A process for coating a woven fabric comprising the steps of: (a) Depositing on a taut fabric a coating composition having a viscosity up to about 100,000 cps and consisting essentially of: 1. a dimethyl siloxane component present in an amount from about 93 to 99 percent by weight of the composition, and 2. a tin catalyst present in an amount from about 0.5 to about 1.5 percent by weight of the composition, (b) uniformly distributing the deposited coating composition on the surface of the fabric, (c) curing the fabric from b, and (d) padding the fabric with a solution selected from a silicone or a fluorocarbon solution, whereby the fabric is substantially wind-resistant and water-repellent.
Claim 11
Dependent Claim
20 words
The process of claim 8 wherein the padding of the fabric is accomplished before the coating composition is deposited thereon.
Claim 12
Dependent Claim
16 words
The process of claim 8 wherein the composition is deposited on both sides of the fabric.
Claim 13
Dependent Claim
13 words
The process of claim 8 wherein the fabric is a closely woven fabric.
Claim 14
Dependent Claim
22 words
The process of claim 11 wherein the fabric has a warf of at least about 90 and a weft of about 68.
Claim 15
Dependent Claim
15 words
The process of claim 11 wherein the fabric is a blend of polyester and cotton.
Claim 16
Dependent Claim
54 words
The process of claim 8 wherein the composition deposited on the substrate consists essentially of: 1. a dimethyl siloxane component present in the amount of about 90.3 percent by weight of the composition; and 2. a dibutyl tin dilaurate catalyst being present in an amount of about 0.7 percent by weight of the composition.
Claim 17
Dependent Claim
32 words
The process of claim 8 wherein the coating composition deposited on the fabric further contains: 3. acetic acid being present in an amount of about 1.0 percent by weight of the composition.
References Cited (Backward Citations)
US3418162A
Cited
US4007305A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-17 | 1986-07-19 | 1987-01-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-17 | 1990-07-19 | 1991-01-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-17 | 1994-07-19 | 1995-01-18 | $7700.00 | Window Closed / Lapsed |