US4369211A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing a hot dip galvanized steel strip
Assignee: Nippon Steel Corp
•
Filing: 1981-01-26
•
Granted: 1983-01-18
•
Expires: 2001-01-26
Abstract
Abstract A hot dip galvanized steel strip in which the zinc based alloy coating exhibits a satisfactory appearance and is firmly fixed to the strip substrate, which strip is produced by a process which comprises coating at least one surface of a steel strip with a melted zinc based alloy controlling the weight of the melted zinc based alloy coating and; solidifying the melted zinc based alloy coating and which process is characterized in that the zinc based alloy contains 0.1 to 2.0% by weight of magnesium and in at least a portion of a stage in which the melted zinc based alloy coating is still in the fluid state, the zinc based alloy coating is exposed to an oxygen-controlled atmosphere containing 1000 ppm or less of molecular oxygen, the controlling procedure for the weight of the melted zinc based alloy coating being carried out in the oxygen-controlled atmosphere.
Inventors
- 👤 Hajime Nitto
- 👤 Kango Sakai
- 👤 Katushi Saito
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:23
CPC Classifications
C; C23; C23C; C23C2/00; C23C2/04; C23C2/06; C23C2/26; C23C2/261
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
118 words
A process for producing a hot dip galvanized sheet strip comprising the steps of: coating at least one surface of a steel strip with a melt of a zinc-based alloy containing 0.1 to 2% by weight of magnesium; controlling the weight of the melted zinc-based alloy coating formed on said steel strip surface; and solidifying said melted zinc-based alloy coating, in which process in at least a portion of a stage in which said melted zinc-based alloy coating is still in the liquid state, said melted zinc-based alloy coating is exposed to an oxygen-controlled atmosphere containing 50 to 1000 ppm of molecular oxygen and the weight of said melted zinc-based alloy coating is controlled in said oxygen-controlled atmosphere.
Claim 2
Dependent Claim
118 words
A process for producing a hot dip galvanized sheet strip comprising the steps of: coating at least one surface of a steel strip with a melt of a zinc-based alloy containing 0.1 to 2% by weight of magnesium; controlling the weight of the melted zinc-based alloy coating formed on said steel strip surface; and solidifying said melted zinc-based alloy coating, in which process in at least a portion of a stage in which said melted zinc-based alloy coating is still in the liquid state, said melted zinc-based alloy coating is exposed to an oxygen-controlled atmosphere containing 50 to 1000 ppm of molecular oxygen and the weight of said melted zinc-based alloy coating is controlled in said oxygen-controlled atmosphere.
Claim 3
Dependent Claim
40 words
The process as claimed in claim 1, wherein said coating procedure comprises immersing said steel strip into a bath consisting of said melted zinc based alloy and, then, upwardly removing said steel strip from said melted zinc based alloy bath.
Claim 4
Dependent Claim
39 words
The process as claimed in claim 1, wherein said controlling procedure of the weight of said zinc based alloy coating comprises jetting a stream of said oxygen controlled atmosphere onto said melted zinc based alloy coating through wiping nozzles.
Claim 5
Dependent Claim
52 words
The process as claimed in claim 2, wherein said oxygen-controlled atmosphere is formed in a region having a height of at least one meter from the upper surface of the melted zinc based alloy bath and surrounding the path of said steel strip removed upwardly from said melted zinc based alloy bath.
Claim 6
Dependent Claim
53 words
The process as claimed in claim 1, wherein after passing through said oxygen-controlled atmosphere, said steel strip with said melted zinc based alloy coating is introduced into another oxygen-controlled atmosphere containing molecular oxygen in a content of 1000 ppm or more but not exceeding the content of molecular oxygen in the ambient atmosphere.
Claim 7
Dependent Claim
27 words
The process as claimed in claim 1, wherein said zinc based alloy comprises 0.1 to 2.0% by weight of magnesium and the balance consisting essentially of zinc.
Claim 8
Dependent Claim
32 words
The process as claimed in claim 1, wherein said zinc based alloy comprises 0.1 to 2.0% by weight of magnesium, 0.5% or less of aluminum and the balance consisting essentially of zinc.
Claim 9
Dependent Claim
22 words
The process as claimed in claim 7, wherein the content of aluminum is in a range of 0.1 to 0.5% by weight.
Claim 10
Dependent Claim
16 words
The process as claimed in claim 1, wherein said zinc based alloy contains substantially no aluminum.
Claim 11
Dependent Claim
33 words
The process as claimed in claim 1, wherein said zinc based alloy comprises 0.1to 2.0% by weight of magnesium, 0.1 to 0.8% by weight of tin and the balance consisting essentially of zinc.
Claim 12
Dependent Claim
65 words
The process as claimed in claim 1, wherein said zinc based alloy comprises (A) 0.1 to 2.0% by weight of magnesium, (B) 0.1% to 5.0% by weight of aluminum, (C) tin in a content of from 0.1% by weight to an upper limit A satisfying the equation: A(%)=1.07-1.33×B wherein B represents a content in % of aluminum and (0) the balance consisting essentially of zinc.
Claim 13
Dependent Claim
40 words
The process as claimed in claim 10, wherein at least a portion of said tin to be contained in said zinc based alloy is replaced by at least one member selected from the group consisting of bismuth, antimony and silicon.
Claim 14
Dependent Claim
40 words
The process as claimed in claim 11, wherein at least a portion of said tin to be contained in said zinc based alloy is replaced by at least one member selected from the group consisting of bismuth, antimony and silicon.
References Cited (Backward Citations)
US3320040A
Cited
US3505042A
Cited
US3993482A
Cited
US4107357A
Cited
US4029478A
Cited
US4082868A
Cited
US4172911A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-17 | 1986-07-19 | 1987-01-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-17 | 1990-07-19 | 1991-01-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-17 | 1994-07-19 | 1995-01-18 | $7700.00 | Window Closed / Lapsed |