Method of manufacturing abrasive articles
Assignee: BARRISTO INTERNATIONAL Inc A CORP OF IL
•
Filing: 1980-08-12
•
Granted: 1983-01-18
•
Expires: 2000-08-12
Abstract
Abstract Nail files and other abrasive articles have a structural base, such as a steel strip, coated with a slurry of a resin, such as an epoxide, and abrasive particles or grits, such as aluminum oxide, granules with sharp peaks and corners, of selected size and covered with one or more layers of electroplated metal, such as copper, nickel and chromium, forming a sheath surrounding the coated base and firmly anchoring the particles around the base. The electroplated metal has relative thick valley portions covering the bases of the particles but only has relatively thin films over the peaks of the particles. In use, the thin coatings over the peaks of the particles are broken off, exposing the tip ends of the abrasive particles for effective abrasion of surfaces, such as fingernails, rubbed thereover. The thermosetting resin material provides the initial positioning and preliminary anchoring of the abrasive particles on the base, but the sheath of electroplated metals overlying the resin coating provides the permanent anchor for the particles. The particle sizes of the abrasive granules can be controlled so that opposite faces of the file or different portions of the same face can have regulated fine or coarse abrading action.
Inventors
- 👤 Harry P. Van Roeyen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:48
CPC Classifications
C; C25; C25D; C25D7/00; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1633; C23C18/1646; C23C18/165; C23C18/1653; C25D15/00
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
174 words
The method of making nail files which comprises stamping a steel sheet to form a blank with a header strip having a plurality of spaced fingers depending therefrom and connected thereto by narrow nibs, stripping oil and grease from the fingers, successively spray coating opposite faces of the fingers with slurries of abrasive granules in epoxide resins, skin curing each coating, stacking the thus coated skin cured blanks between paper sheets, finish curing the coatings on the blanks in the stack, cleaning the cured blanks, acid etching the cleaned blanks, rinsing the etched blanks, immersing the thus rinsed blanks in a stannous chloride accelerator bath, again rinsing the blanks, depositing an electroless thin nickel coating on the blanks, rinsing the nickel coated blanks, copper plating the rinsed nickel coated blanks, rinsing the copper coated blanks, nickel plating the rinsed copper plated blanks, chrome plating the rinsed nickel plated blanks, rinsing the chrome plated blanks, severing the nibs to remove the fingers from the header, and mounting handles on the nib ends of the blanks.
Claim 2
Independent Claim
174 words
The method of making nail files which comprises stamping a steel sheet to form a blank with a header strip having a plurality of spaced fingers depending therefrom and connected thereto by narrow nibs, stripping oil and grease from the fingers, successively spray coating opposite faces of the fingers with slurries of abrasive granules in epoxide resins, skin curing each coating, stacking the thus coated skin cured blanks between paper sheets, finish curing the coatings on the blanks in the stack, cleaning the cured blanks, acid etching the cleaned blanks, rinsing the etched blanks, immersing the thus rinsed blanks in a stannous chloride accelerator bath, again rinsing the blanks, depositing an electroless thin nickel coating on the blanks, rinsing the nickel coated blanks, copper plating the rinsed nickel coated blanks, rinsing the copper coated blanks, nickel plating the rinsed copper plated blanks, chrome plating the rinsed nickel plated blanks, rinsing the chrome plated blanks, severing the nibs to remove the fingers from the header, and mounting handles on the nib ends of the blanks.
Claim 3
Dependent Claim
47 words
The method of claim 1 wherein the spray coatings on the opposite faces of the fingers are effected by first coating one side of the fingers, then skin curing the coated side of the fingers, and next coating and skin curing the opposite side of the fingers.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein the electroless nickel coating is limited to a thickness of not more than 0.00002 inches.
Claim 5
Dependent Claim
24 words
The method of claim 1 wherein the copper plating is limited to form a copper strike coating of not more than about 0.00003 inches.
Claim 6
Independent Claim
80 words
The method of making abrasive articles which comprises stamping sheet material to form a blank with a header strip having a plurality of spaced fingers depending therefrom, coating the fingers with a slurry of abrasive granules and flowable plastics material adhesive, curing the coating to anchor the particles to the fingers, depositing an electroless thin nickel coating on the fingers, copper plating the nickel coated fingers, nickel plating the copper plated fingers, and severing the fingers from the header strip.
Claim 7
Independent Claim
80 words
The method of making abrasive articles which comprises stamping sheet material to form a blank with a header strip having a plurality of spaced fingers depending therefrom, coating the fingers with a slurry of abrasive granules and flowable plastics material adhesive, curing the coating to anchor the particles to the fingers, depositing an electroless thin nickel coating on the fingers, copper plating the nickel coated fingers, nickel plating the copper plated fingers, and severing the fingers from the header strip.
Claim 8
Dependent Claim
11 words
The method of claim 5 wherein the sheet material is steel.
Claim 9
Dependent Claim
13 words
The method of claim 5 wherein the coatings form sheaths around the fingers.
Claim 10
Dependent Claim
14 words
The method of claim 5 wherein the flowable plastics material is an epoxide resin.
Claim 11
Dependent Claim
23 words
The method of claim 5 wherein opposite faces of the fingers are coated with separate slurries having abrasive granules of different size ranges.
Claim 12
Independent Claim
98 words
The method of making abrasive devices which comprises coating abrasive granules and adhesive resin on a base, curing the resin to hold the granules on the base with peaks of the granules projecting from the base, electroless plating a thin metal layer on the cured coating, electroplating a thin metal layer over the electroless plated metal, and controlling said plating steps to produce an undulating multi-layer crust on the cured coating which is thin and frangible at the projecting peaks of the granules to break off during use of the devices for exposing the peaks of the granules.
Claim 13
Independent Claim
98 words
The method of making abrasive devices which comprises coating abrasive granules and adhesive resin on a base, curing the resin to hold the granules on the base with peaks of the granules projecting from the base, electroless plating a thin metal layer on the cured coating, electroplating a thin metal layer over the electroless plated metal, and controlling said plating steps to produce an undulating multi-layer crust on the cured coating which is thin and frangible at the projecting peaks of the granules to break off during use of the devices for exposing the peaks of the granules.
Claim 14
Dependent Claim
29 words
The method of claim 10 wherein the crust is relatively thick in the valleys between the peaks to firmly retain the granules in fixed locked position on the base.
Claim 15
Dependent Claim
26 words
The method of claim 10 including the added step of forming a metal strike coating over the electroless plated metal prior to forming the electroplated layer.
Claim 16
Dependent Claim
12 words
The method of claim 12 wherein the metal strike coating is copper.
Claim 17
Independent Claim
113 words
The method of making abrasive devices which comprises forming a metal sheet into the shape of an article with a surface, cleaning said surface, forming a coating of abrasive granules and flowable plastics material resin on said cleaned surface, settling the resin constituent of the coating on the surface to project peaks of the granules above the main layer of resin, curing the resin to hold the granules on the surface, and plating a plurality of thin layers of metal on the cured coating to form a multi-layer crust which is relatively thin at the peaks of the granules and sufficiently frangible to break off during an abrading action for exposing the granules.
Claim 18
Independent Claim
113 words
The method of making abrasive devices which comprises forming a metal sheet into the shape of an article with a surface, cleaning said surface, forming a coating of abrasive granules and flowable plastics material resin on said cleaned surface, settling the resin constituent of the coating on the surface to project peaks of the granules above the main layer of resin, curing the resin to hold the granules on the surface, and plating a plurality of thin layers of metal on the cured coating to form a multi-layer crust which is relatively thin at the peaks of the granules and sufficiently frangible to break off during an abrading action for exposing the granules.
Claim 19
Dependent Claim
15 words
The method of claim 14 wherein the first metal layer is deposited by electroless plating.
Claim 20
Dependent Claim
28 words
The method of claim 15 wherein the electroless plated layer is covered with a metal strike and a second metal layer is plated on the metal strike layer.
Claim 21
Dependent Claim
11 words
The method of claim 14 wherein the metal layers are nickel.
Claim 22
Dependent Claim
17 words
The method of claim 17 including the step of forming a copper strike between the nickel layers.
Claim 23
Dependent Claim
30 words
The method of claim 14 including the steps of plating all surfaces of the coated metal article to form a sheath of plated metal around the article encasing the coating.
Claim 24
Independent Claim
79 words
The method of making articles with friction surfaces which comprises forming a sheath of plastics material having granules anchored therein completely around a base, coating the sheath with a solution containing a palladium salt, cleaning the thus coated sheathed base, immersing the coated sheathed base in an accelerator, depositing an electroless nickel sheath coating on the accelerator treated coated sheathed base, copper plating the resulting electroless nickel coated surface on the base, and nickel plating the copper plated surface.
Claim 25
Independent Claim
79 words
The method of making articles with friction surfaces which comprises forming a sheath of plastics material having granules anchored therein completely around a base, coating the sheath with a solution containing a palladium salt, cleaning the thus coated sheathed base, immersing the coated sheathed base in an accelerator, depositing an electroless nickel sheath coating on the accelerator treated coated sheathed base, copper plating the resulting electroless nickel coated surface on the base, and nickel plating the copper plated surface.
Claim 26
Independent Claim
90 words
A method of making articles with friction surfaces which comprises providing a metal base with a clean surface, coating a slurry of abrasive granules and flowable plastics material adhesive on said surface, setting said plastics material to anchor the granules to the base, etching the set plastics material in an acid bath containing a palladium salt, immersing the etched surface in a stannis chloride accelerator bath, depositing an electroless thin nickel coating on the accelerator treated surface, copper plating the electroless thin nickel coating, and nickel plating the copper coating.
Claim 27
Independent Claim
90 words
A method of making articles with friction surfaces which comprises providing a metal base with a clean surface, coating a slurry of abrasive granules and flowable plastics material adhesive on said surface, setting said plastics material to anchor the granules to the base, etching the set plastics material in an acid bath containing a palladium salt, immersing the etched surface in a stannis chloride accelerator bath, depositing an electroless thin nickel coating on the accelerator treated surface, copper plating the electroless thin nickel coating, and nickel plating the copper coating.
Claim 28
Independent Claim
77 words
The method of making articles with friction surfaces which comprises forming a sheath of granules containing plastics material adhesive around a base, setting the plastics material adhesive to anchor the granules to the base, depositing an electroless metal coating sheath around the set adhesive sheath, depositing a sheath of electroplated metal around the electroless metal sheath, and controlling the thicknesses of the metal coatings to expose peaks of the granules when the article is subjected to friction.
Claim 29
Independent Claim
77 words
The method of making articles with friction surfaces which comprises forming a sheath of granules containing plastics material adhesive around a base, setting the plastics material adhesive to anchor the granules to the base, depositing an electroless metal coating sheath around the set adhesive sheath, depositing a sheath of electroplated metal around the electroless metal sheath, and controlling the thicknesses of the metal coatings to expose peaks of the granules when the article is subjected to friction.
Claim 30
Dependent Claim
24 words
The method of claim 20 including the step of acid etching the plastics material sheath for anchoring the palladium salt to the plastics material.
Claim 31
Dependent Claim
12 words
The method of claim 20 wherein the palladium salt is palladium chloride.
Claim 32
Dependent Claim
11 words
The method of claim 20 wherein the accelerator is stannis chloride.
Claim 33
Dependent Claim
14 words
The method of claim 21 wherein the coatings form sheaths completely around the base.
Claim 34
Dependent Claim
20 words
The method of claim 21 wherein the metal base is shaped into a finished article before receiving the coatings thereon.
Claim 35
Dependent Claim
26 words
The method of claim 21 wherein the plastics material settles on the base to expose peaks of the abrasive granules prior to setting the plastics material.
Claim 36
Dependent Claim
30 words
The method of claim 22 including the added step of settling the plastics material around the base to expose the peaks of the granules prior to setting the plastics material.
References Cited (Backward Citations)
US1955572A
Cited
US2694647A
Cited
US2858256A
Cited
US2820746A
Cited
US3023490A
Cited
US3061525A
Cited
US3377264A
Cited
US4154276A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-17 | 1986-07-19 | 1987-01-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-17 | 1990-07-19 | 1991-01-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-17 | 1994-07-19 | 1995-01-18 | $7700.00 | Window Closed / Lapsed |