Abstract An improved method of making a silver chloride and copper chloride-containing electrode comprises forming a minimum melting point mixture of about 47% by weight of silver chloride and about 53% by weight of cuprous chloride and melting this mixture e.g. at about 255° C., cooling the resulting eutectic, as by casting the same, to form solid pieces, and then grinding the eutectic to a powder of e.g. about 100 mesh. This powdered eutectic is then uniformly mixed with a predetermined desired amount of additional particulate cuprous chloride and the resulting mixture is heated in a mold to above the melting point of the eutectic therein to cause the eutectic to melt and bind the particles of cuprous chloride together. Normally the eutectic is in a concentration of about 10% by weight and the additional particulate cuprous chloride is in a concentration of about 90% by weight of this mixture. The mixture can then be cooled to solidification in the mold to provide a strong electrode in an inexpensive rapid improved manner. The mold can contain, if desired, a metallic grid current collector of copper or the like to which the electrode mixture adheres.
An improved method of making a silver chloride and copper chloride-containing electrode, said method comprising the steps of: a. forming a minimum melting point eutectic of silver chloride and cuprous chloride; b. heating said eutectic to above the melting point thereof, then cooling, solidifying and powdering said eutectic; c. uniformly mixing said eutectic together with additional particulate cuprous chloride to reduce the concentration of silver chloride of the resulting mixture to about 1-10 percent by weight; and, d. forming the resulting mixture into an improved strong electrode.
Claim 2
Dependent Claim
87 words
An improved method of making a silver chloride and copper chloride-containing electrode, said method comprising the steps of: a. forming a minimum melting point eutectic of silver chloride and cuprous chloride; b. heating said eutectic to above the melting point thereof, then cooling, solidifying and powdering said eutectic; c. uniformly mixing said eutectic together with additional particulate cuprous chloride to reduce the concentration of silver chloride of the resulting mixture to about 1-10 percent by weight; and, d. forming the resulting mixture into an improved strong electrode.
Claim 3
Dependent Claim
40 words
The improved method of claim 1 wherein said eutectic is formed by mixing together about 47 percent by weight of silver chloride and about 53 percent by weight of cuprous chloride and melting the same at least about 255° C.
Claim 4
Dependent Claim
19 words
The improved method of claim 2 wherein said molten eutectic is cast, then solidified and ground to fine powder.
Claim 5
Dependent Claim
38 words
The improved method of claim 2 wherein said resulting mixture is heated to above the melting point of said eutectic but below the melting point of cuprous chloride, then cooled to solidification to provide said improved strong electrode.
Claim 6
Dependent Claim
28 words
The improved method of claim 4 wherein said heating of said resulting mixture takes place in a mold at a temperature not in excess of about 300° C.