Process for making solar cell base material
Assignee: HELIOTRONIC FORSCHUNGS-UND ENTWICKLUNGS-GESELLSCHAFT fur SOLARZELLEN-GRUDSTOFFE MBH
•
Filing: 1980-01-25
•
Granted: 1982-12-28
•
Expires: 2000-01-25
Abstract
Abstract Competitive current generation by the exploitation of solar energy requires cheap solar cells. A process is described which makes it possible to manufacture from silicon a base material for solar cells of this type in an economical manner and in large quantities. This is achieved by bringing silicon from a supply container into contact with a non-elemental lubricating melt, which is immiscible with silicon but will not wet silicon and has a melting point below that of silicon, and by drawing off a silicon film, sliding on this lubricating melt, and solidifying the silicon continuously by cooling to below its' melting point.
Inventors
- 👤 Gerhard Ast
- 👤 Josef Dietl
- 👤 Dieter Helmreich
- 👤 Hans-Dieter Miller
- 👤 Erhard Sirtl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:20
CPC Classifications
C; C30; C30B; C30B15/00; C30B15/02; C30B15/06
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
136 words
In a process for the manufacture of granular crystalline silicon sheets of preferred orientation, having a thickness of between 0.2 and 2 mm and suitable for use as a base material for solar cells, wherein a silicon melt is brought into contact with a second molten phase and is subsequently allowed to solidify, the improvement comprising the steps of: charging a pulling vessel with molten elemental silicon and a non-elemental lubricating melt which is immiscible with silicon but will wet silicon and has a melting point below that of silicon; supercooling at least one wall of said pulling vessel to 5° to 100° C. below the melting point of silicon; and continuously drawing off an elemental silicon film solidifying on said cooled wall but separated from said wall by a thin layer of the lubricating melt.
Claim 2
Dependent Claim
136 words
In a process for the manufacture of granular crystalline silicon sheets of preferred orientation, having a thickness of between 0.2 and 2 mm and suitable for use as a base material for solar cells, wherein a silicon melt is brought into contact with a second molten phase and is subsequently allowed to solidify, the improvement comprising the steps of: charging a pulling vessel with molten elemental silicon and a non-elemental lubricating melt which is immiscible with silicon but will wet silicon and has a melting point below that of silicon; supercooling at least one wall of said pulling vessel to 5° to 100° C. below the melting point of silicon; and continuously drawing off an elemental silicon film solidifying on said cooled wall but separated from said wall by a thin layer of the lubricating melt.
Claim 3
Dependent Claim
31 words
The process according to claim 1, wherein the molten silicon is fed from said supply vessel into said pulling vessel by means of a capillary system according to the syphon principle.
Claim 4
Dependent Claim
55 words
The process according to claim 1, additionally including the step of adding an effective amount of at least one suitable additive to the lubricating melt so that the interfacial tension between the silicon and the lubricating melt is reduced and so that the molten silicon can spread out more readily to form a thin film.
Claim 5
Dependent Claim
27 words
The process according to claim 3, wherein sulphidic additives are added to the lubricating melt to reduce the interfacial tension between the silicon and the lubricating melt.
Claim 6
Dependent Claim
42 words
The process according to claim 1, wherein a melt comprising alkaline earth metal fluorides in admixture with 10 to 90 mole % of alkaline earth metal silicates and having a melting point below that of silicon is used as said lubricating melt.
Claim 7
Dependent Claim
30 words
The process according to claim 1, wherein the level of said melt in the pulling vessel is maintained constant by controlling the inflow of molten silicon from a supply vessel.
Claim 8
Dependent Claim
28 words
The process according to claim 1, wherein said silicon film is drawn off said cooled wall at an angle between -90° and +90° with respect to the horizontal.
Claim 9
Dependent Claim
27 words
The process according to claim 3, wherein a silicon film is continuously drawn off in a vertically upward direction off a vertical wall of the pulling vessel.
Claim 10
Dependent Claim
42 words
The process according to claim 1, additionally including the step of charging said pulling vessel with an effective amount of said lubricating melt so that the entire surface of said molten silicon is covered by a thin film of said lubricating melt.
Claim 11
Dependent Claim
22 words
The process according to claim 1, wherein said silicon film is drawn at an average pulling speed between 1 and 200 cm/minute.
Claim 12
Dependent Claim
154 words
In a process for the manufacture of granular crystalline silicon sheets of preferred orientation having a thickness of between 0.2 and 2 mm and suitable for use as a base material for solar cells, wherein a silicon melt is brought into contact with a second molten phase and is subsequently allowed to solidify, the improvement comprising the steps of: charging a pulling vessel with molten silicon and a non-elemental lubricating melt which is immiscible with silicon but will wet silicon and has a melting point below that of silicon, said lubricating melt comprising alkaline earth metal flourides in admixture with 10 to 90 mole% of alkaline earth metal silicates; supercooling at least one wall of said pulling vessel to 50° to 100° C. below the melting point of silicon; and continuously drawing off a silicon film solidifying on said cooled wall but separated from said wall by a thin layer of the lubricating melt.
Claim 13
Dependent Claim
154 words
In a process for the manufacture of granular crystalline silicon sheets of preferred orientation having a thickness of between 0.2 and 2 mm and suitable for use as a base material for solar cells, wherein a silicon melt is brought into contact with a second molten phase and is subsequently allowed to solidify, the improvement comprising the steps of: charging a pulling vessel with molten silicon and a non-elemental lubricating melt which is immiscible with silicon but will wet silicon and has a melting point below that of silicon, said lubricating melt comprising alkaline earth metal flourides in admixture with 10 to 90 mole% of alkaline earth metal silicates; supercooling at least one wall of said pulling vessel to 50° to 100° C. below the melting point of silicon; and continuously drawing off a silicon film solidifying on said cooled wall but separated from said wall by a thin layer of the lubricating melt.
Claim 14
Dependent Claim
48 words
The process according to claim 7 or 11, additionally including the step of adding an effective amount of a surface-tension-reducing additive to said lubricating melt so that the surface of the silicon melt and the entire silicon film are covered with a thin layer of said lubricating melt.
References Cited (Backward Citations)
US2872299A
Cited
US3218143A
Cited
US3899304A
Cited
US4058418A
Cited
US4022652A
Cited
DE2633961A1
Cited
US4036595A
Cited
JPS5261180A
Cited
US4226834A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-27 | 1986-06-28 | 1986-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-27 | 1990-06-28 | 1990-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-27 | 1994-06-28 | 1994-12-28 | $7700.00 | Window Closed / Lapsed |