US4363677A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for treating an electromagnetic steel sheet and an electromagnetic steel sheet having marks of laser-beam irradiation on its surface
Assignee: Nippon Steel Corp
•
Filing: 1981-01-22
•
Granted: 1982-12-14
•
Expires: 2001-01-22
Abstract
Abstract A process of providing electromagnetic steel strips or sheet with excellent magnetic properties. The process comprises the steps of: irradiating with a laser-beam the surface of an electromagnetic steel sheet which has been finally annealed, thereby locally forming marks of the laser-beam irradiation on the surface of the steel, and; subsequently, subjecting the steel sheet to the formation of an insulating film on the sheet surface at a temperature of the sheet not exceeding 600 DEG C.
Inventors
- 👤 Tadashi Ichiyama
- 👤 Shigehiro Yamaguchi
- 👤 Tohru Iuchi
- 👤 Motoharu Nakamura
- 👤 Yozo Suga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:41
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/12; C21D8/1294; C21D1/00; C21D1/06; C21D1/09; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/14766; H01F1/14775; H01F1/14783; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12903; Y10T428/12917; Y10T428/12924
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
108 words
A method for treating an electromagnetic steel sheet to reduce its watt loss after completion of its final heat treatment, and comprising irradiating at least one surface of the finally heat-treated sheet with a laser beam having an energy density of from 0.01 to 1000 J/cm 2 so as to mark the sheet's surface and cause a substantial reduction in the sheet's watt loss, and thereafter a liquid insulating film-forming agent requiring treating at temperatures not higher than 600° C. is coated on the surface and the coated sheet is treated at temperatures not higher than 600° C. so as to form an insulating film on the surface.
Claim 2
Independent Claim
108 words
A method for treating an electromagnetic steel sheet to reduce its watt loss after completion of its final heat treatment, and comprising irradiating at least one surface of the finally heat-treated sheet with a laser beam having an energy density of from 0.01 to 1000 J/cm 2 so as to mark the sheet's surface and cause a substantial reduction in the sheet's watt loss, and thereafter a liquid insulating film-forming agent requiring treating at temperatures not higher than 600° C. is coated on the surface and the coated sheet is treated at temperatures not higher than 600° C. so as to form an insulating film on the surface.
Claim 3
Dependent Claim
16 words
The method of claim 1 in which the treating temperature is not higher than 550° C.
Claim 4
Dependent Claim
16 words
The method of claim 1 in which the treating temperature is not higher than 500° C.
Claim 5
Dependent Claim
15 words
The method of claim 1 in which the agent is substantially free from colloidal silica.
Claim 6
Dependent Claim
26 words
The method of claim 1 in which the agent is coated on the sheet's surface in an amount of from 2 to 3 g/m 2 .
Claim 7
Dependent Claim
22 words
The method of claim 1 in which at the time of the irradiating the sheet's surface is free from a glass film.
Claim 8
Dependent Claim
46 words
The method of claim 1 in which at the time of the irradiating the sheet's surface is coated with a thin film of a substance selected from the class consisting of steel blueing, chromic acid solution and copper and through which the laser beam can penetrate.
Claim 9
Dependent Claim
40 words
The method of claim 7 in which the thin film is steel blueing and is formed by exposing the sheet at temperatures of at least 600° C. to oxidizing conditions, and enhances the sheet's absorption of the laser beam irradiation.
References Cited (Backward Citations)
US3192078A
Cited
US3647575A
Cited
US3856568A
Cited
US3947296A
Cited
US3932236A
Cited
US3990923A
Cited
US4063063A
Cited
US4130447A
Cited
US4242155A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-13 | 1986-06-14 | 1986-12-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-13 | 1990-06-14 | 1990-12-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-13 | 1994-06-14 | 1994-12-14 | $7700.00 | Window Closed / Lapsed |