Process of forming a multi-ply laminate
Assignee: BFG Glassgroup GIE
•
Filing: 1980-11-24
•
Granted: 1982-12-07
•
Expires: 2000-11-24
Abstract
Abstract When forming a multi-ply laminate having at least one thermoplastic structural ply forming an outer ply of the laminate, known processes comprise degassing and bonding steps during which gas is removed from between assembled structural plies of the laminate and the plies are heated to cause them to bond together while a moulding plate is in contact with the or each exposed thermoplastic ply. In order to reduce or eliminate optical distortion in the laminate, which may be adapted to constitute a vehicle windshield, during the degassing step, the assembled plies are subjected to a sub-atmospheric environmental pressure having an absolute valve of 150 mm Hg or less while the inter-ply space or spaces are subjected to a sub-atmospheric pressure at the edges of the assembly to degas the assembly, said edge pressure and said environmental pressure are maintained at such values as to give rise to a separation of the plies which is attributable to the mean inter-ply gas pressure being higher than the environmental pressure while the assembly of plies is heated to a temperature below that at which effective adherence commences between the thermoplastic material and an adjacent ply, the degassed assembly remains subject to sub-atmospheric edge pressure while its temperature is increased past the temperature at which said effective adherence commences and the assembly is then subjected to a bonding step in which heat and pressure conditions are such as to cause the plies to bond firmly together.
Inventors
- 👤 Pol Baudin
- 👤 Pierre Collignon
- 👤 Claude Gillieaux
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:40
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/00596; B32; B32B; B32B27/00; B32B27/06; B29D11/0073; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10009; B32B17/10018; B32B17/1055; B32B17/10688; B32B17/10807; B32B17/10816; B32B17/10825; B32B17/10834; B32B17/10844; B32B17/10889; B32B37/00; B32B37/0007; B32B37/003; B32B37/10; B60; B60J; B60J1/00; B60J1/02; B32B2307/00; B32B2307/40; B32B2307/412; B32B2309/00; B32B2309/12; B32B2315/00; B32B2315/08; B32B2398/00; B32B2398/20
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
242 words
A process of forming a multi-ply laminate which comprises at least one thermoplastic structural ply forming an outer ply of the laminate, said process comprising degassing and bonding steps during which gas is removed from between assembled structural plies of the laminate and the plies are heated to cause them to bond together while a moulding plate is in contact with the or each exposed thermoplastic ply, characterised in that during the degassing step, the assembled plies are subjected to a sub-atmospheric environmental pressure having an absolute value of 150 mm Hg or less while the inter-ply space or spaces is or are subjected to a sub-atmospheric pressure at the edges of the assembly (hereinafter called "edge pressure") to degas the assembly, said edge pressure and said environmental pressure being maintained at such values as to give rise to a separation of the plies of the assembly which is attributable to the mean inter-ply gas pressure being higher than the environmental pressure while the assembly of plies is heated to a temperature below that at which effective adherence commences between the thermoplastic material and a said adjacent ply, in that the degassed assembly remains subject to sub-atmospheric edge pressure while its temperature is increased past the temperature at which said effective adherence commences and in that the assembly is then subjected to a bonding step in which heat and pressure conditions are such as to cause the plies to bond firmly together.
Claim 2
Dependent Claim
242 words
A process of forming a multi-ply laminate which comprises at least one thermoplastic structural ply forming an outer ply of the laminate, said process comprising degassing and bonding steps during which gas is removed from between assembled structural plies of the laminate and the plies are heated to cause them to bond together while a moulding plate is in contact with the or each exposed thermoplastic ply, characterised in that during the degassing step, the assembled plies are subjected to a sub-atmospheric environmental pressure having an absolute value of 150 mm Hg or less while the inter-ply space or spaces is or are subjected to a sub-atmospheric pressure at the edges of the assembly (hereinafter called "edge pressure") to degas the assembly, said edge pressure and said environmental pressure being maintained at such values as to give rise to a separation of the plies of the assembly which is attributable to the mean inter-ply gas pressure being higher than the environmental pressure while the assembly of plies is heated to a temperature below that at which effective adherence commences between the thermoplastic material and a said adjacent ply, in that the degassed assembly remains subject to sub-atmospheric edge pressure while its temperature is increased past the temperature at which said effective adherence commences and in that the assembly is then subjected to a bonding step in which heat and pressure conditions are such as to cause the plies to bond firmly together.
Claim 3
Dependent Claim
36 words
A process according to claim 1, characterised in that while the assembly is so heated in the degassing step, said environmental pressure is or is reduced to an absolute value of 100 mm Hg or less.
Claim 4
Dependent Claim
36 words
A process according to claim 2, characterised in that while the assembly is so heated in the degassing step, said environmental pressure is or is reduced to an absolute value of 30 mm Hg or less.
Claim 5
Dependent Claim
36 words
A process according to claim 3, characterised in that while the assembly is so heated in the degassing step, said environmental pressure is or is reduced to an absolute value of 10 mm Hg or less.
Claim 6
Dependent Claim
40 words
A process according to claim 4, characterised in that while the assembly is so heated in the degassing step, said edge pressure and said environmental pressure are, or are reduced to an absolute value of 10 mm Hg or less.
Claim 7
Dependent Claim
33 words
A process according to claim 1, 2, 3, 4 or 5, characterised in that, before firm bonding takes place, said environmental pressure is released while said edge pressure remains at a sub-atmospheric level.
Claim 8
Dependent Claim
32 words
A process according to claim 6, characterised in that said environmental pressure is released when the temperature of the assembly is within 10° C. of the temperature at which effective bonding commences.
Claim 9
Dependent Claim
41 words
A process according to claim 1, 2, 3, 4 or 5, characterised in that, in said bonding step, the assembly is heated to a maximum temperature of between 20° C. and 80° C. above the temperature at which effective bonding commences.
Claim 10
Dependent Claim
25 words
A process according to claim 1, 2, 3, 4 or 5, characterised in that at least one said ply is constituted by a vitreous sheet.
Claim 11
Dependent Claim
33 words
A process according to claim 9, characterised in that the or at least one said vitreous sheet is coated prior to assembly with a primer which promotes its adhesion to the thermoplastic ply.
Claim 12
Dependent Claim
18 words
A process according to claim 10, characterised in that said primer comprises one or more silicon organo-functional silanes.
Claim 13
Dependent Claim
34 words
A process according to claim 1, 2, 3, 4 or 5, characterised in that said moulding plate is a glass sheet coated with a substance which inhibits adhesion between it and the thermoplastic ply.
Claim 14
Dependent Claim
33 words
A process according to claim 1, 2, 3, 4 or 5, characterised in that the surface of said molding plate which contacts the thermoplastic ply is smooth and nonadherent to the thermoplastic ply.
References Cited (Backward Citations)
US4180426A
Cited
US4192701A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-06 | 1986-06-07 | 1986-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-06 | 1990-06-07 | 1990-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-06 | 1994-06-07 | 1994-12-07 | $7700.00 | Window Closed / Lapsed |