Method of producing microporous joints in metal bodies
Assignee: United States Department of Energy
•
Filing: 1967-09-12
•
Granted: 1982-12-07
•
Expires: 1987-09-12
Abstract
Abstract Tungsten is placed in contact with either molybdenum, tantalum, niobium, vanadium, rhenium, or other metal of atoms having a different diffusion coefficient than tungsten. The metals are heated so that the atoms having the higher diffusion coefficient migrate to the metal having the lower diffusion rate, leaving voids in the higher diffusion coefficient metal. Heating is continued until the voids are interconnected.
Inventors
- 👤 Joseph C. Danko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:30
CPC Classifications
G; G21; G21D; G21D7/00; G21D7/04; B; B22; B22F; B22F7/00; C; C21; C21D; C21D3/00; Y; Y02; Y02E; Y02E30/00; Y10; Y10S; Y10S148/00; Y10S148/902
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
178 words
A process for making a microporous vent at the interface of a joint between two metals having different diffusion coefficients comprising the steps of : forming an intimate contact interface joint between two metals, one of the two metals having a higher diffusion coefficient than the other of the two metals and selected from the group consisting of molybdenum, tantalum, niobium, vanadium, rhenium, molybdenum-50 weight % rhenium, and niobium-vanadium, the other metal of the two metals having a lower diffusion coefficient being selected from the group consisting of tungsten and tungsten-25 weight % rhenium, heating the thus joined metals to a temperature below their melting point but high enough to cause atoms of the one of the two metals having the higher diffusion coefficient to migrate into the other of the two metals having the lower diffusion coefficient, and maintaining the joint metals in the heated condition for a period of time sufficient for voids resulting from the migration of atoms to become interconnected, thereby producing microporous vents at the interface of the joint between the two metals.
Claim 2
Dependent Claim
178 words
A process for making a microporous vent at the interface of a joint between two metals having different diffusion coefficients comprising the steps of : forming an intimate contact interface joint between two metals, one of the two metals having a higher diffusion coefficient than the other of the two metals and selected from the group consisting of molybdenum, tantalum, niobium, vanadium, rhenium, molybdenum-50 weight % rhenium, and niobium-vanadium, the other metal of the two metals having a lower diffusion coefficient being selected from the group consisting of tungsten and tungsten-25 weight % rhenium, heating the thus joined metals to a temperature below their melting point but high enough to cause atoms of the one of the two metals having the higher diffusion coefficient to migrate into the other of the two metals having the lower diffusion coefficient, and maintaining the joint metals in the heated condition for a period of time sufficient for voids resulting from the migration of atoms to become interconnected, thereby producing microporous vents at the interface of the joint between the two metals.
Claim 3
Dependent Claim
58 words
The process as claimed in claim 1, wherein the one of the two metals having the higher diffusion coefficient is molybdenum-50 weight % rhenium, and the other of the two metals having the lower diffusion coefficient is tungsten-25 weight % rhenium, and wherein the temperature is maintained for about 25 hours in the rangee of about 2400°-2600° C.
Claim 4
Dependent Claim
49 words
The process as claimed in claim 1, wherein the step of forming the intimate contact joint between the two metals is accomplished by a bonding technique selected from the group consisting of brazing, friction welding, compression welding, and coextrusion, to provide a bonded interface joint between the two metals.
References Cited (Backward Citations)
US3188732A
Cited
US3158732A
Cited
US3197858A
Cited
US3157539A
Cited
US3170234A
Cited
US3259971A
Cited
US3205573A
Cited
US3261724A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-06 | 1986-06-07 | 1986-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-06 | 1990-06-07 | 1990-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-06 | 1994-06-07 | 1994-12-07 | $7700.00 | Window Closed / Lapsed |