Process for preparing copolymers comprising α-alkyl styrene and unsaturated nitrile
Assignee: Sumika Polycarbonate Ltd
•
Filing: 1981-06-05
•
Granted: 1982-11-30
•
Expires: 2001-06-05
Abstract
Abstract In the emulsion polymerization of an α-alkylstyrene and an unsaturated nitrile copolymerizable therewith in a weight proportion of 70:30 to 80:20 in the presence of a radical initiator, an improved process wherein the monomers are introduced into the reaction system in such a manner that the concentration of the unreacted unsaturated nitrile in the reaction system is not less than 31% by weight to the entire amount of the unreacted monomers in the reaction system at the completion of the introduction of the monomers, whereby a copolymer of the α-alkylstyrene and the unsaturated nitrile having an excellent thermal resistance is produced with marked decrease in the amount of unreacted monomers.
Inventors
- 👤 Hiroyuki Minematsu
- 👤 Kojiro Matsumoto
- 👤 Tadashi Saeki
- 👤 Akira Kishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 00:45
CPC Classifications
C; C08; C08F; C08F212/00; C08F212/02; C08F212/04; C08F212/06; C08F212/12; C08F220/00; C08F220/02; C08F220/42; C08F220/44; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
150 words
A process for the production of a copolymer of an α-alkylstyrene and an unsaturated nitrile, comprising the steps of: introducing α-alkylstyrene monomers and unsaturated nitrile monomers in a reaction system in a weight ratio of 70:30 to 80:20, respectively, and copolymerizing said introduced monomers in the presence of a radical initiator in such a manner that the concentration of unreacted unsaturated nitrile in the reaction system is not less than 31% by weight of the entire amount of unreacted monomers in the reaction system at the completion of introducing the monomers into the system; and after the completion of introducing the monomers into the reaction system, further polymerizing the monomers to produce a copolymer comprising α-alkylstyrene and unsaturated nitrile monomers in a weight ratio of 70:30 to 80:20, wherein the produced copolymer has excellent thermal resistance and has 1% by weight or less of unreacted monomers at completion of polymerization.
Claim 2
Dependent Claim
150 words
A process for the production of a copolymer of an α-alkylstyrene and an unsaturated nitrile, comprising the steps of: introducing α-alkylstyrene monomers and unsaturated nitrile monomers in a reaction system in a weight ratio of 70:30 to 80:20, respectively, and copolymerizing said introduced monomers in the presence of a radical initiator in such a manner that the concentration of unreacted unsaturated nitrile in the reaction system is not less than 31% by weight of the entire amount of unreacted monomers in the reaction system at the completion of introducing the monomers into the system; and after the completion of introducing the monomers into the reaction system, further polymerizing the monomers to produce a copolymer comprising α-alkylstyrene and unsaturated nitrile monomers in a weight ratio of 70:30 to 80:20, wherein the produced copolymer has excellent thermal resistance and has 1% by weight or less of unreacted monomers at completion of polymerization.
Claim 3
Dependent Claim
35 words
The process according to claim 1, wherein polymerization is effected in such a manner that 90% by weight or more of the particles of the produced copolymer have a particle size of 0.10μ or less.
Claim 4
Dependent Claim
31 words
The process according to claim 1, wherein said monomers are introduced into said reaction system with regulation of the rate of addition of each of the α-alkylstyrene and the unsaturated nitrile.
Claim 5
Dependent Claim
28 words
The process according to claim 1, wherein said monomers are introduced into said reaction system with regulation of the mixing proportion of the α-alkylstyrene and the unsaturated nitrile.
Claim 6
Dependent Claim
35 words
The process according to claim 1, wherein said monomers are introduced into said reaction system by addition of the entire amount of the α-alkylstyrene and regulation of the rate of addition of the unsaturated nitrile.
Claim 7
Dependent Claim
66 words
The process according to claim 1, wherein during said introducing step a monomer mixture containing a larger proportion of α-alkylstyrene and a smaller proportion of unsaturated nitrile are added to the reaction system and thereafter, with regulation of the concentration of unreacted unsaturated nitrile, a monomer mixture containing a larger proportion of unsaturated nitrile and a smaller proportion of α-alkylstyrene are added to the reaction system.
Claim 8
Dependent Claim
67 words
The process according to claim 1, wherein during said introducing step a monomer mixture containing a larger proportion of α-alkylstyrene and a smaller proportion of unsaturated nitrile are continuously added to the reaction system and thereafter, with regulation of the concentration of unreacted unsaturated nitrile, a monomer mixture containing a larger proportion of unsaturated nitrile and a smaller proportion of α-alkylstyrene are added to the reaction system.
Claim 9
Dependent Claim
52 words
The process according to claim 1, wherein during said introducing step a monomer mixture containing a larger proportion of α-alkylstyrene and a smaller proportion of unsaturated nitrile are added to the reaction system and thereafter, with regulation of the concentration of unreacted unsaturated nitrile, unsaturated nitrile is added to the reaction system.
Claim 10
Dependent Claim
20 words
The process according to claim 1, wherein said α-alkylstyrene is selected from the group consisting of α-methylstyrene, α-ethylstyrene and methyl-α-methylstyrene.
Claim 11
Dependent Claim
21 words
The process according to claim 1, wherein said unsaturated nitrile is selected from the group consisting of acrylonitrile, methacrylonitrile and ethacrylonitrile.
Claim 12
Dependent Claim
36 words
The process according to claim 1, wherein said α-alkylstyrene is selected from the group consisting of α-methylstyrene, α-ethylstyrene and methyl-α-methylstyrene and wherein said unsaturated nitrile is selected from the group consisting of acrylonitrile, methacrylonitrile and ethacrylonitrile.
Claim 13
Dependent Claim
11 words
The process according to claim 1, wherein said α-alkylstyrene is α-methylstyrene.
Claim 14
Dependent Claim
12 words
The process according to claim 1, wherein said unsaturated nitrile is acrylonitrile.
Claim 15
Dependent Claim
17 words
The process according to claim 1, wherein said α-alkylstyrene is α-methylstyrene and said unsaturated nitrile is acrylonitrile.
Claim 16
Dependent Claim
149 words
A process for the production of a copolymer of an α-alkylstyrene and an unsaturated nitrile, consisting essentially of: introducing α-alkylstyrene monomers and unsaturated nitrile monomers in a reaction system in a weight ratio of 70:30 to 80:20, respectively, and copolymerizing said introduced monomers in the presence of a radical initiator in such a manner that the concentration of unreacted unsaturated nitrile in the reaction system is not less than 31% by weight of the entire amount of unreacted monomers in the reaction system at the completion of introducing the monomers into the system; and after the completion of introducing the monomers into the reaction system, further polymerizing the monomers to produce a copolymer comprising α-alkylstyrene and unsaturated nitrile monomers in a weight ratio of 70:30 to 80:20, wherein the produced copolymer has excellent thermal resistance and has 1% by weight or less of unreacted monomers at completion of polymerization.
Claim 17
Dependent Claim
149 words
A process for the production of a copolymer of an α-alkylstyrene and an unsaturated nitrile, consisting essentially of: introducing α-alkylstyrene monomers and unsaturated nitrile monomers in a reaction system in a weight ratio of 70:30 to 80:20, respectively, and copolymerizing said introduced monomers in the presence of a radical initiator in such a manner that the concentration of unreacted unsaturated nitrile in the reaction system is not less than 31% by weight of the entire amount of unreacted monomers in the reaction system at the completion of introducing the monomers into the system; and after the completion of introducing the monomers into the reaction system, further polymerizing the monomers to produce a copolymer comprising α-alkylstyrene and unsaturated nitrile monomers in a weight ratio of 70:30 to 80:20, wherein the produced copolymer has excellent thermal resistance and has 1% by weight or less of unreacted monomers at completion of polymerization.
Claim 18
Dependent Claim
35 words
The process according to claim 15, wherein polymerization is effected in such a manner that 90% by weight or more of the particles of the produced copolymer have a particle size of 0.10μ or less.
Claim 19
Dependent Claim
11 words
The process according to claim 15, wherein said α-alkylstyrene is α-methylstyrene.
Claim 20
Dependent Claim
12 words
The process according to claim 15, wherein said unsaturated nitrile is acrylonitrile.
Claim 21
Dependent Claim
17 words
The process according to claim 15, wherein said α-alkylstyrene is α-methylstyrene and said unsaturated nitrile is acrylonitrile.
References Cited (Backward Citations)
US4169195A
Cited
US4200593A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-29 | 1986-05-31 | 1986-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-29 | 1990-05-31 | 1990-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-29 | 1994-05-31 | 1994-11-30 | $7700.00 | Window Closed / Lapsed |