Method of preparing high quality vinylidene fluoride polymer in aqueous emulsion
Assignee: Arkema Inc
•
Filing: 1981-08-31
•
Granted: 1982-11-23
•
Expires: 2001-08-31
Abstract
Abstract Vinylidene fluoride polymers of high quality are prepared consistently by an emulsion polymerization process in which the monomer, chain transfer agent (isopropyl alcohol), and an aqueous emulsion of the initiator (diisopropylperoxydicarbonate) containing a fluoro surfactant of a limited class are fed incremently to an aqueous reaction medium containing a fluoro surfactant.
Inventors
- 👤 Julius E. Dohany
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:56
CPC Classifications
C; C08; C08F; C08F14/00; C08F14/18; C08F14/22
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
104 words
In a process for preparing high molecular weight vinylidene fluoride polymer by emulsion polymerization of monomer in a stirred aqueous reaction medium containing a fluoroalkyl surfactant emulsifier, the improvement which comprises using diisopropyl peroxydicarbonate as the polymerization initiator and isopropyl alcohol as the chain transfer agent and wherein monomer, initiator and chain transfer agent are added separately but simultaneously to the system, incrementally or continuously over the polymerization cycle, the initiator being added as the emulsified component of an aqueous emulsion in which a fluorosurfactant, readily soluble in cold water and capable of emulsifying the initiator for the duration of the polymerization is used.
Claim 2
Dependent Claim
104 words
In a process for preparing high molecular weight vinylidene fluoride polymer by emulsion polymerization of monomer in a stirred aqueous reaction medium containing a fluoroalkyl surfactant emulsifier, the improvement which comprises using diisopropyl peroxydicarbonate as the polymerization initiator and isopropyl alcohol as the chain transfer agent and wherein monomer, initiator and chain transfer agent are added separately but simultaneously to the system, incrementally or continuously over the polymerization cycle, the initiator being added as the emulsified component of an aqueous emulsion in which a fluorosurfactant, readily soluble in cold water and capable of emulsifying the initiator for the duration of the polymerization is used.
Claim 3
Dependent Claim
44 words
The process of claim 1 wherein the fluorosurfactant used to emulsify the initiator is a surfactant of the formula X(CF.sub.2).sub.n COOH wherein n is an integer from 6 to 20 and X is hydrogen or fluorine and salts thereof of alkali metals of ammonia.
Claim 4
Dependent Claim
46 words
The process of claim 2 wherein the initiator fed to the system is an emulsion in deionized water containing 0.1 to 0.5 percent by weight fluoro surfactant and 5 to 10 percent by weight of initiator, said percentages being based on the weight of said emulsion.
Claim 5
Dependent Claim
16 words
The process of claim 3 wherein the vinylidene fluoride polymer is the homopolymer of vinylidene fluoride.
Claim 6
Dependent Claim
38 words
The process of claim 2 wherein the chain transfer agent fed to the system is an aqueous solution containing from 1 to 10 percent by weight isopropyl alcohol, said percentage being based on the weight of said solution.
Claim 7
Dependent Claim
16 words
The process of claim 5 wherein the vinylidene fluoride polymer is the homopolymer of vinylidene fluoride.
Claim 8
Dependent Claim
27 words
The process of claim 6 wherein the polymerization is conducted at a temperature between 60° and 90° C. and at a pressure between 300 to 1000 psig.
Claim 9
Dependent Claim
17 words
The process of claim 2 wherein the vinylidene fluoride polymer contains up to 25 mol percentage tetrafluoroethylene.
Claim 10
Dependent Claim
17 words
The process of claim 2 wherein the vinylidene fluoride polymer contains up to 13 mol percentage hexafluoropropene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-22 | 1986-05-24 | 1986-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-22 | 1990-05-24 | 1990-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-22 | 1994-05-24 | 1994-11-23 | $7700.00 | Window Closed / Lapsed |