Agglomerate-free, bubble-free, high barrier vinylidene chloride polymer films and process of preparation

Claim 2

An improved process for preparing extruded vinylidene chloride copolymer film containing an effective amount of one or more inorganic particulate additives, said film being generally free of bubbles, holes and white specks, said film being made by (a) preparing a blend of (1) a dry, powdered, generally plasticizer-free, normally crystalline vinylidene chloride polymer having polymerized therein from about 70 to about 95 percent by weight vinylidene chloride and from about 30 to about 5 percent by weight of at least one monoethylenically unsaturated monomer copolymerized therewith, and (2) the inorganic particulate additives, each additive having an average particle size of greater than about 0.5 micron and less than about 40 microns, and (b) thermally fabricating said blend into film form by extrusion, the improvement which comprises making a preblend of the inorganic particulate additives with from about 0.02 to about 0.5 weight percent, based on weight of the inorganic particulate additives of an alkali metal salt of an alkylaryl sulfonic acid and admixing the preblend with the vinylidene chloride polymer.

Claim 3

The process of claim 1 wherein the normally crystalline vinylidene chloride polymer is a copolymer of vinylidene chloride and vinyl chloride.

Claim 4

The process of claim 2 wherein said polymer is a copolymer of about 85 percent by weight vinylidene chloride and 15 percent by weight vinyl chloride.

Claim 5

The process of claim 1 wherein the alkali metal salt of an alkylaryl sulfonic acid is selected from the group consisting of sodium dimethyl naphthalene sulfonate, sodium monomethyl naphthalene sulfonate and blends thereof.

Claim 6

The process of claim 1 wherein the alkali metal salt of an alkylaryl sulfonic acid is a blend of sodium monomethyl naphthalene sulfonate and sodium dimethyl naphthalene sulfonate.

Claim 7

The process of claim 1 wherein the inorganic particulate additives are selected from the group consisting of magnesium oxide, titanium dioxide, calcium carbonate and tetrasodium pyrophosphate.

Claim 8

The process of claim 1 wherein the inorganic particulate additive is magnesium oxide.

Claim 9

The process of claim 1 wherein the amount of each inorganic particulate additive is from about 0.1 to about 0.8 percent by weight, based upon weight of the vinylidene chloride copolymer.

Claim 10

The process of claim 1 wherein the amount of each inorganic particulate additive is from about 0.3 to about 0.5 percent by weight, based upon weight of the vinylidene chloride copolymer.

Claim 11

An improved process for preparing extruded vinylidene chloride copolymer film containing an effective amount of one or more inorganic particulate additives, said film being generally free of bubbles, holes and white specks, said film being made by (a) preparing a blend of (1) a dry, powdered, generally plasticizer-free, normally crystalline vinylidene chloride copolymer having polymerized therein from about 70 to about 95 percent by weight, based on copolymer weight, vinylidene chloride and from about 30 to about 5 percent by weight, based on copolymer weight, of at least one monoethylenically unsaturated monomer copolymerized therewith, and (2) the inorganic particulate additives, each additive having an average particle size of greater than about 0.5 micron and less than about 40 microns, and (b) thermally fabricating said blend into film form by extrusion, the improvement which comprises dividing the inorganic additives into a first portion and a second portion, dividing the vinylidene chloride copolymer into a first portion and a second portion, forming a concentrate, the concentrate being formed by first admixing the first portion of the inorganic additives with from about 0.02 to about 0.5 weight percent, based upon total inorganic additive weight, of an alkali metal salt of an alkylaryl sulfonic acid using a high speed mixing means, then mixing in the second portion of the inorganic additives and the first portion of the vinylidene chloride copolymer, the concentrate then being blended with the second portion of the vinylidene chloride copolymer, whereby the blend and the film made therefrom are generally free of agglomerates without the necessity of an intermediate step to remove agglomerates.

Claim 12

An improved process for preparing extruded vinylidene chloride copolymer film containing an effective amount of one or more inorganic particulate additives, said film being generally free of bubbles, holes and white specks, said film being made by (a) preparing a blend of (1) a dry, powdered, generally plasticizer-free, normally crystalline vinylidene chloride copolymer having polymerized therein from about 70 to about 95 percent by weight, based on copolymer weight, vinylidene chloride and from about 30 to about 5 percent by weight, based on copolymer weight, of at least one monoethylenically unsaturated monomer copolymerized therewith, and (2) the inorganic particulate additives, each additive having an average particle size of greater than about 0.5 micron and less than about 40 microns, and (b) thermally fabricating said blend into film form by extrusion, the improvement which comprises dividing the inorganic additives into a first portion and a second portion, dividing the vinylidene chloride copolymer into a first portion and a second portion, forming a concentrate, the concentrate being formed by first admixing the first portion of the inorganic additives with from about 0.02 to about 0.5 weight percent, based upon total inorganic additive weight, of an alkali metal salt of an alkylaryl sulfonic acid using a high speed mixing means, then mixing in the second portion of the inorganic additives and the first portion of the vinylidene chloride copolymer, the concentrate then being blended with the second portion of the vinylidene chloride copolymer, whereby the blend and the film made therefrom are generally free of agglomerates without the necessity of an intermediate step to remove agglomerates.