Process for reducing melt fracture during extrusion of a molten narrow molecular weight distribution, linear, ethylene copolymer
Assignee: Union Carbide Corp
•
Filing: 1981-04-01
•
Granted: 1982-11-23
•
Expires: 2001-04-01
Abstract
Abstract A process for reducing melt fracture formed during extrusion of a molten narrow molecular weight distribution, linear, ethylene polymer, which comprises extruding said polymer through a die having a discharge outlet defining an exit die gap formed by opposing die lip surfaces and wherein one surface of the die lip and/or die land in contact with the molten polymer extends beyond the opposing surface of the die lip and/or die land in the direction of the axis of flow of the molten polymer through the die exit and wherein said extended die lip has a groove extending around said extended die lip, said groove being disposed opposite the leading edge of the opposing die lip surface whereby melt fracture is reduced on both surfaces of the polymer leaving said die exit.
Inventors
- 👤 Stuart J. Kurtz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:35
CPC Classifications
B; B29; B29C; B29C48/00; B29C48/25; B29C48/30; B29C48/32; B29C48/022; B29C48/03; B29C48/07; B29C48/08; B29C48/09; B29C48/10; B29C48/305; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/0608; B29K2023/0633
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
146 words
A process for reducing melt fracture formed during extrusion of a molten narrow molecular weight distribution, linear, ethylene polymer, under conditions of flow rate and melt temperature which would otherwise produce higher levels of melt fracture which comprises extruding said polymer through a die having a discharge outlet defining an exit die gap formed by opposing die lip surfaces and wherein one surface of the die lip and/or die land in contact with the molten polymer extends beyond the opposing surface of the die lip and/or die land in the direction of the axis of flow of the molten polymer through the die exit, said extended die lip having a groove extending around said extended die lip, said groove being disposed opposite the surface of the opposing die lip whereby melt fracture is reduced on the surface of the film leaving the extended die lip surface.
Claim 2
Dependent Claim
146 words
A process for reducing melt fracture formed during extrusion of a molten narrow molecular weight distribution, linear, ethylene polymer, under conditions of flow rate and melt temperature which would otherwise produce higher levels of melt fracture which comprises extruding said polymer through a die having a discharge outlet defining an exit die gap formed by opposing die lip surfaces and wherein one surface of the die lip and/or die land in contact with the molten polymer extends beyond the opposing surface of the die lip and/or die land in the direction of the axis of flow of the molten polymer through the die exit, said extended die lip having a groove extending around said extended die lip, said groove being disposed opposite the surface of the opposing die lip whereby melt fracture is reduced on the surface of the film leaving the extended die lip surface.
Claim 3
Dependent Claim
26 words
A process according to claim 1 wherein said extended die lip extends from about 0.010 inch to about 0.400 inch beyond said opposing die lip surface.
Claim 4
Dependent Claim
24 words
A process according to claim 2 wherein said groove has a leading edge which coincides with the leading edge of said extended die lip.
Claim 5
Dependent Claim
34 words
A process according to claim 3 wherein the length of said groove extends from the leading edge of said extended die lip to a point below the leading edge of said opposed die lip.
Claim 6
Dependent Claim
15 words
A process according to claim 4 wherein said groove is of a generally trapezoidal configuration.
Claim 7
Dependent Claim
40 words
A process according to claim 5 wherein the distance between said leading edge of said opposed die lip surface and the furthermost inward distance of said die groove in line with said leading edge is about 0.03 to 0.250 inch.
Claim 8
Dependent Claim
15 words
A process as in claim 1 wherein the ethylene polymer is formed into blown film.
Claim 9
Dependent Claim
15 words
A process as in claim 1 wherein the ethylene polymer is slot cast into film.
Claim 10
Dependent Claim
14 words
A process as in claim 1 wherein the ethylene polymer is formed into pipe.
Claim 11
Dependent Claim
18 words
A process as in claim 1 wherein the ethylene polymer is a linear low density ethylene hydrocarbon copolymer.
Claim 12
Dependent Claim
36 words
A process as in claim 10 in which said copolymer is a copolymer of ethylene and at least one C 3 to C 8 alpha olefin having a melt index of about ≧0.1 to about ≦20.
Claim 13
Dependent Claim
33 words
A process as in claim 11 in which said copolymer is a copolymer of ≧90 mol percent ethylene and ≦10 mol percent of at least one C 3 to C 8 alpha olefin.
Claim 14
Dependent Claim
33 words
A process as in claim 12 in which said copolymer has a molecular weight distribution of about ≧2.7 to ≦6.0 and a total unsaturation content of about ≧0.1 to ≦0.3 C═C/1000 C atoms.
References Cited (Backward Citations)
US3125620A
Cited
US2813301A
Cited
US3038209A
Cited
US3133313A
Cited
US3618167A
Cited
US3859017A
Cited
US3920782A
Cited
US3876740A
Cited
US3879158A
Cited
US3947214A
Cited
US4112166A
Cited
US4021170A
Cited
US4187269A
Cited
US4243619A
Cited
US4267146A
Cited
US4282177A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-22 | 1986-05-24 | 1986-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-22 | 1990-05-24 | 1990-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-22 | 1994-05-24 | 1994-11-23 | $7700.00 | Window Closed / Lapsed |