Mixed ethylene and propylene carbonate-containing organic polyisocyanate adhesive binder composition
Assignee: Lyondell Chemical Technology LP
•
Filing: 1981-11-19
•
Granted: 1982-11-16
•
Expires: 2001-11-19
Abstract
Abstract An adhesive binder composition is provided for the preparation of lignocellulosic composite molded articles such as flake or particle board, made from moldable compositions which comprises an organic di- or polyisocyanate and a liquid mixture of ethylene carbonate and propylene carbonate and optionally lignin, for application to the lignocellulosic material prior to the molding process to form the composite product.
Inventors
- 👤 James M. Gaul
- 👤 Tinh Nguyen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:22
CPC Classifications
C; C08; C08L; C08L97/00; C08L97/02; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/64; C08G18/6484; C08K; C08K5/00; C08K5/04; C08K5/10; C08L75/00; C08L75/04; C08L97/005; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/253; Y10T428/31504; Y10T428/31551; Y10T428/31591; Y10T428/31844; Y10T428/31848; Y10T428/31971; Y10T428/31989
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
57 words
An adhesive binder composition for the preparation of compression moldable lignocellulosic articles which comprises from about 20 to 95 percent by weight of an organic di- or polyisocyanate and from about 5 to 80 percent by weight of a liquid mixture of ethylene carbonate and propylene carbonate containing from about 5 to 80 weight percent ethylene carbonate.
Claim 2
Dependent Claim
57 words
An adhesive binder composition for the preparation of compression moldable lignocellulosic articles which comprises from about 20 to 95 percent by weight of an organic di- or polyisocyanate and from about 5 to 80 percent by weight of a liquid mixture of ethylene carbonate and propylene carbonate containing from about 5 to 80 weight percent ethylene carbonate.
Claim 3
Dependent Claim
23 words
The adhesive composition of claim 1 wherein from 0 to 60 weight percent lignin based on the total composition is added as diluent.
Claim 4
Dependent Claim
18 words
The adhesive composition of claim 2 wherein between 20 and 35 weight percent lignin is added as diluent.
Claim 5
Dependent Claim
31 words
The adhesive composition of claim 1 wherein the ethylene carbonate-propylene carbonate liquid mixtures contain between about 60 and 20 weight percent ethylene carbonate and 40 and 80 weight percent propylene carbonate.
Claim 6
Dependent Claim
24 words
The adhesive composition of claim 1 wherein the di- or polyisocyanate is a mixture of diphenylmethane diisocyanate and the higher functionality polymethylene polyphenyl isocyanates.
Claim 7
Dependent Claim
31 words
The adhesive composition of claim 1 wherein from 50 to 75 weight percent organic di- or polyisocyanate and from 50 to 25 weight percent liquid ethylene carbonate-propylene carbonate mixture is employed.
Claim 8
Dependent Claim
68 words
A compression moldable lignocellulosic composition comprising lignocellulosic particles and from about 1.5 to 12 percent by weight based on oven dried particles of an adhesive binder composition which comprises from about 20 to 95 weight percent organic di- or polyisocyanate and from about 5 to 80 weight percent of a liquid mixture of ethylene carbonate and propylene carbonate containing from about 5 to 80 weight percent ethylene carbonate.
Claim 9
Dependent Claim
68 words
A compression moldable lignocellulosic composition comprising lignocellulosic particles and from about 1.5 to 12 percent by weight based on oven dried particles of an adhesive binder composition which comprises from about 20 to 95 weight percent organic di- or polyisocyanate and from about 5 to 80 weight percent of a liquid mixture of ethylene carbonate and propylene carbonate containing from about 5 to 80 weight percent ethylene carbonate.
Claim 10
Dependent Claim
21 words
The compression moldable composition of claim 7 wherein from 2.5 to 6.5 weight percent adhesive binder is employed in the composition.
Claim 11
Dependent Claim
26 words
The compression moldable composition of claim 7 wherein from 0 to 60 weight percent lignin based on the total adhesive binder composition is added as diluent.
Claim 12
Dependent Claim
17 words
The compression moldable composition of claim 9 wherein the lignin is between 20 and 35 weight percent.
Claim 13
Dependent Claim
32 words
The compression moldable composition of claim 7 wherein the ethylene carbonate-propylene carbonate liquid mixture contains between about 60 and 20 weight percent ethylene carbonate and 40 and 80 weight percent propylene carbonate.
Claim 14
Dependent Claim
36 words
The compression moldable composition of claim 7 wherein from 50 to 75 weight percent organic di- or polyisocyanate and from 50 to 25 weight percent liquid ethylene carbonate-propylene carbonate mixture is employed in the adhesive binder.
Claim 15
Dependent Claim
16 words
The compression moldable composition of claim 7 wherein the di- or polyisocyanate is a diphenylmethane diisocyanate.
Claim 16
Dependent Claim
25 words
The compression moldable composition of claim 7 wherein the di- or polyisocyanate is a mixture of diphenylmethane diisocyanate and the higher functionality polymethylene polyphenyl isocyanates.
Claim 17
Dependent Claim
78 words
A composition board product comprising a compression molded lignocellulosic composition comprising lignocellulosic particles and from about 1.5 to 12 weight percent based on oven dried lignocellulosic particles employed of an adhesive binder composition, said binder composition being a mixture of from about 20 to 95 weight percent organic di- or polyisocyanate and from 5 to 80 weight percent of a liquid mixture of ethylene carbonate and propylene carbonate containing from about 5 to 80 weight percent ethylene carbonate.
Claim 18
Dependent Claim
78 words
A composition board product comprising a compression molded lignocellulosic composition comprising lignocellulosic particles and from about 1.5 to 12 weight percent based on oven dried lignocellulosic particles employed of an adhesive binder composition, said binder composition being a mixture of from about 20 to 95 weight percent organic di- or polyisocyanate and from 5 to 80 weight percent of a liquid mixture of ethylene carbonate and propylene carbonate containing from about 5 to 80 weight percent ethylene carbonate.
Claim 19
Dependent Claim
26 words
The composition board product of claim 15 wherein from 0 to 60 weight percent lignin based on the total adhesive binder composition is added as diluent.
Claim 20
Dependent Claim
16 words
The board product of claim 15 wherein the compression molded lignocellulosic composition is wood particle board.
Claim 21
Independent Claim
164 words
A method for the preparation of lignocellulosic composite articles comprising the steps of (a) mixing together lignocellulosic particles and from about 1.5 to 12 weight percent based on oven dried lignocellulosic particles of an adhesive binder composition comprising from 20 to 95 weight percent organic di- and polyisocyanate and from about 5 to 80 weight percent of a liquid mixture of ethylene carbonate and propylene carbonate containing from about 5 to 80 weight percent ethylene carbonate to form a moldable composition; (b) introducing said moldable composition onto a metal mold, caul plate or platen which has been sprayed or coated with a release agent; (c) compression shaping said composition at temperatures of between about 140° C. to 220° C. at pressures of from about 100 to 600 psi for a period of from about 1 to 10 minutes to form a composite article of desired shape and/or thickness; and (d) thereafter releasing said lignocellulosic composite article from said metal mold, caul plate or platen.
Claim 22
Independent Claim
164 words
A method for the preparation of lignocellulosic composite articles comprising the steps of (a) mixing together lignocellulosic particles and from about 1.5 to 12 weight percent based on oven dried lignocellulosic particles of an adhesive binder composition comprising from 20 to 95 weight percent organic di- and polyisocyanate and from about 5 to 80 weight percent of a liquid mixture of ethylene carbonate and propylene carbonate containing from about 5 to 80 weight percent ethylene carbonate to form a moldable composition; (b) introducing said moldable composition onto a metal mold, caul plate or platen which has been sprayed or coated with a release agent; (c) compression shaping said composition at temperatures of between about 140° C. to 220° C. at pressures of from about 100 to 600 psi for a period of from about 1 to 10 minutes to form a composite article of desired shape and/or thickness; and (d) thereafter releasing said lignocellulosic composite article from said metal mold, caul plate or platen.
Claim 23
Dependent Claim
85 words
A method according to claim 18 wherein 2.5 to 6.5 weight percent adhesive binder composition is employed and comprises from 50 to 75 weight percent organic di- or polyisocyanates and from 50 to 25 weight percent of a carbonate mixture containing between about 60 and 20 weight percent ethylene carbonate and 40 to 80 weight percent propylene carbonate, the release agent is a metallic soap, the compression temperature is between 160° C. to 190° C. and the time period is from 3 to 5 minutes.
Claim 24
Dependent Claim
23 words
A method according to claim 18 wherein the binder composition is a mixture of diphenylmethane diisocyanate and the higher functionality polymethylene polyphenyl isocyanates.
Claim 25
Dependent Claim
16 words
A method according to claim 18 wherein the compression molded lignocellulosic composition is wood particle board.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-15 | 1986-05-17 | 1986-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-15 | 1990-05-17 | 1990-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-15 | 1994-05-17 | 1994-11-16 | $7700.00 | Window Closed / Lapsed |