Claim 1

Independent Claim 201 words

A method for preparing Group VIII metal-phosphorus compounds supported on a high surface area solid support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals and mixtures thereof, wherein the Group VIII metal-phosphorus crystallite size is about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of water soluble Group VIII metal chloride, Group VIII metal nitrate and Group VIII metal ammonia complexes; (b) impregnating said support with phosphorus by means of a phosphorus source selected from the group consisting of elemental phosphorus and at least one water soluble phosphate salt, in an amount sufficient to resalt in a phosphorus to Group VIII metal atomic ratio of about 0.3 to about 3.0; (c) reducing the reducible deposited components resultant from the completion of steps (a) and (b) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate the desired supported Group VIII metal-phosphorus compounds.

Claim 2

Independent Claim 201 words

A method for preparing Group VIII metal-phosphorus compounds supported on a high surface area solid support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals and mixtures thereof, wherein the Group VIII metal-phosphorus crystallite size is about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of water soluble Group VIII metal chloride, Group VIII metal nitrate and Group VIII metal ammonia complexes; (b) impregnating said support with phosphorus by means of a phosphorus source selected from the group consisting of elemental phosphorus and at least one water soluble phosphate salt, in an amount sufficient to resalt in a phosphorus to Group VIII metal atomic ratio of about 0.3 to about 3.0; (c) reducing the reducible deposited components resultant from the completion of steps (a) and (b) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate the desired supported Group VIII metal-phosphorus compounds.

Claim 3

Dependent Claim 22 words

The method of claim 1 wherein said solution of at least one water soluble Group VIII metal salt is an aqueous solution.

Claim 4

Dependent Claim 28 words

The method of claim 2 wherein said support is impregnated with said solution of at least one water soluble Group VIII metal salt by the incipient wetness technique.

Claim 5

Dependent Claim 43 words

The method of claim 2 wherein said support is impregnated with said solution of at least one water soluble Group VIII metal salt by the ion exchange method, wherein steps (a) and (b) are performed sequentially, step (a) first, followed by step (b).

Claim 6

Dependent Claim 39 words

The method of claim 1 wherein said water soluble Group VIII metal salts are selected from the group consisting of water soluble Group VIII noble metal chloride, Group VIII noble metal nitrate and Group VIII noble metal ammonia complexes.

Claim 7

Dependent Claim 30 words

The method of claim 5 wherein said water soluble Group VIII metal salts are selected from the group consisting of water soluble platinum chloride, platinum nitrate and platinum ammonia complexes.

Claim 8

Dependent Claim 42 words

The method of claim 1 wherein said high surface area support is selected from the group consisting of carbon, alumina, silica, silica-alumina, and mixtures thereof and the surface area of said support ranges from about 10 to about 2000 m 2 /g.

Claim 9

Dependent Claim 13 words

The method of claim 7 wherein said high surface area support is carbon.

Claim 10

Dependent Claim 30 words

The method of claim 8 wherein said water soluble Group VIII metal salt is H 2 PtCl 6 and said solution of H 2 PtCl 6 is an aqueous solution.

Claim 11

Dependent Claim 24 words

The method of claim 9 wherein said water soluble phosphate salt is ammonium phosphate and said solution of ammonium phosphate is an aqueous solution.

Claim 12

Dependent Claim 49 words

The method of claim 10 wherein steps (a) and (b) are performed sequentially, step (a) first followed by step (b) and after step (a) the composition resultant from step (a) is reduced, and the temperature of said reducing step (c) ranges from about 300° C. to about 500° C.

Claim 13

Dependent Claim 49 words

The method of claim 10 wherein steps (a) and (b) are performed sequentially, step (b) first followed by step (a), and after step (b) the composition resultant from step (b) is reduced, and the temperature of said reducing step (c) ranges from about 300° C. to about 500° C.

Claim 14

Dependent Claim 31 words

The method of claim 9 wherein steps (a) and (b) are performed sequentially in any order and said support is impregnated with phosphorus by the vapor deposition method in a vacuum.

Claim 15

Dependent Claim 13 words

The method of claim 13 wherein said support is impregnated with red phosphorus.

Claim 16

Dependent Claim 24 words

The process of claim 1 wherein said reducing atmosphere is H 2 and said temperature ranges from about 300° C. to about 500° C.

Claim 17

Dependent Claim 18 words

The method of claim 1 wherein the impregnating steps (a) and (b) are practiced sequentially, in any order.

Claim 18

Dependent Claim 15 words

The method of claim 1 wherein the impregnating steps (a) and (b) are practiced simultaneously.

Claim 19

Independent Claim 154 words

A method for preparing Group VIII metal-phosphorus compounds supported on a high surface area solid carbon support, wherein the Group VIII metal-phosphorus crystallite size is about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area carbon support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) impregnating said carbon support with phosphoric acid in an amount sufficient to result in a phosphorus to Group VIII metal atomic ratio of about 0.3 to about 3.0; (c) reducing the reducible deposited components resultant from the completion of steps (a) and (b) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate the supported Group VIII metal-phosphorus compounds.

Claim 20

Independent Claim 154 words

A method for preparing Group VIII metal-phosphorus compounds supported on a high surface area solid carbon support, wherein the Group VIII metal-phosphorus crystallite size is about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area carbon support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) impregnating said carbon support with phosphoric acid in an amount sufficient to result in a phosphorus to Group VIII metal atomic ratio of about 0.3 to about 3.0; (c) reducing the reducible deposited components resultant from the completion of steps (a) and (b) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate the supported Group VIII metal-phosphorus compounds.

Claim 21

Dependent Claim 30 words

The method of claim 18 wherein said water soluble Group VIII metal salts are selected from the group consisting of water soluble platinum chloride, platinum nitrate and platinum ammonia complexes.

Claim 22

Dependent Claim 30 words

The method of claim 19 wherein said water soluble Group VIII metal salt is H 2 PtCl 6 and said solution of H 2 PtCl 6 is an aqueous solution.

Claim 23

Dependent Claim 49 words

The method of claim 20 wherein steps (a) and (b) are performed sequentially, step (a) first followed by step (b), and after step (a) the composition resultant from step (a) is reduced, and the temperature of said reducing step (c) ranges from about 300° C. to about 500° C.

Claim 24

Dependent Claim 49 words

The method of claim 20 wherein steps (a) and (b) are performed sequentially, step (b) first followed by step (a), and after step (b) the composition resultant from step (b) is reduced, and the temperature of said reducing step (c) ranges from about 300° C. to about 500° C.

Claim 25

Independent Claim 166 words

A method for preparing Group VIII metal-phosphorus compounds supported on a high surface area solid support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals and mixtures thereof wherein said support contains a chemical species selected from the group consisting of a reducible phosphorus-containing compound and elemental phosphorus, wherein the Group VIII metal-phosphorus crystallite size is about 300 A or less wherein the process consists of the steps of; (a) impregnating said high surface area support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) reducing the composition resultant from the completion of step (a) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate the desired supported Group VIII metal-phosphorus compounds.

Claim 26

Independent Claim 166 words

A method for preparing Group VIII metal-phosphorus compounds supported on a high surface area solid support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals and mixtures thereof wherein said support contains a chemical species selected from the group consisting of a reducible phosphorus-containing compound and elemental phosphorus, wherein the Group VIII metal-phosphorus crystallite size is about 300 A or less wherein the process consists of the steps of; (a) impregnating said high surface area support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) reducing the composition resultant from the completion of step (a) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate the desired supported Group VIII metal-phosphorus compounds.

Claim 27

Dependent Claim 29 words

The method of claim 23 wherein said water soluble Group VIII metal salts are selected from the group consisting of water soluble platinum chloride, platinum nitrate and platinum-ammonia complexes.

Claim 28

Dependent Claim 14 words

The method of claim 24 wherein said high surface area support is activated carbon.

Claim 29

Dependent Claim 30 words

The method of claim 25 wherein said water soluble Group VIII metal salt is H 2 PtCl 6 and said solution of H 2 PtCl 6 is an aqueous solution.

Claim 30

Independent Claim 196 words

A method for preparing a Group VIII metal-arsenic compound supported on a high surface area support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals, and mixtures thereof wherein the Group VIII metal-arsenic compound has a crystallite size of about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) impregnating said support with a chemical species selected from the group consisting of arsenic and a water soluble arsenite salt in an amount sufficient to result in an arsenic to Group VIII metal atomic ratio of about 0.3 to about 3.0; (c) reducing the reducible deposited components resultant from the completion of steps (a) and (b) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate the desired supported Group VIII metal-arsenic compounds. pg,38

Claim 31

Independent Claim 196 words

A method for preparing a Group VIII metal-arsenic compound supported on a high surface area support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals, and mixtures thereof wherein the Group VIII metal-arsenic compound has a crystallite size of about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) impregnating said support with a chemical species selected from the group consisting of arsenic and a water soluble arsenite salt in an amount sufficient to result in an arsenic to Group VIII metal atomic ratio of about 0.3 to about 3.0; (c) reducing the reducible deposited components resultant from the completion of steps (a) and (b) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate the desired supported Group VIII metal-arsenic compounds. pg,38

Claim 32

Dependent Claim 212 words

A process for preparing Group VIII metals supported on a high surface area solid support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals and mixtures thereof, wherein the Group VIII metals crystallite size is about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area support with solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) impregnating said support with phosphorus by means of a phosphorus source selected from the group consisting of elemental phosphorus and at least one water soluble phosphate salt; (c) reducing the reducible deposited components resultant from the completion of steps (a) and (b) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate a supported Group VIII metal-phosphorus compound having a crystallite size of about 300 A or less; (d) decomposing said Group VIII metal-phosphorus compound such that the Group VIII metal crystallite size is not substantially increased, and the supported Group VIII metal is formed.

Claim 33

Dependent Claim 212 words

A process for preparing Group VIII metals supported on a high surface area solid support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals and mixtures thereof, wherein the Group VIII metals crystallite size is about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area support with solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) impregnating said support with phosphorus by means of a phosphorus source selected from the group consisting of elemental phosphorus and at least one water soluble phosphate salt; (c) reducing the reducible deposited components resultant from the completion of steps (a) and (b) in a gaseous reducing atmosphere at a temperature in the range of about 200° C. to about 650° C. for a time sufficient to generate a supported Group VIII metal-phosphorus compound having a crystallite size of about 300 A or less; (d) decomposing said Group VIII metal-phosphorus compound such that the Group VIII metal crystallite size is not substantially increased, and the supported Group VIII metal is formed.

Claim 34

Dependent Claim 40 words

The process of claim 28 wherein said Group VIII metal-phosphorus compound is decomposed by calcining in air said highly dispersed, supported Group VIII metal-phosphorus compound at a temperature in the range of from about 100° C. to about 300° C.

Claim 35

Dependent Claim 28 words

The process of claim 28 wherein said Group VIII metal-phosphorus compound is decomposed by decomposing said highly dispersed, supported Group VIII metal-phosphorus compound in water at room temperature.

Claim 36

Dependent Claim 45 words

The process of claim 29 wherein said Group VIII metal salt is H 2 PtCl 6 , said support is carbon, said solution of H 2 PtCl 6 is an aqueous solution and said highly dispersed, supported Group VIII metal-phosphorus compound is PtP 2 .

Claim 37

Dependent Claim 45 words

The process of claim 30 wherein said Group VIII metal salt is H 2 PtCl 6 , said support is carbon, said solution of H 2 PtCl 6 is an aqueous solution and said highly dispersed, supported Group VIII metal-phosphorus compound is PtP 2 .

Claim 38

Dependent Claim 18 words

The method of claim 18 wherein the impregnating steps (a) and (b) are practiced sequentially, in any order.

Claim 39

Dependent Claim 15 words

The method of claim 18 wherein the impregnating steps (a) and (b) are practiced simultaneously.

Claim 40

Dependent Claim 18 words

The method of claim 27 wherein the impregnating steps (a) and (b) are practiced sequentially, in any order.

Claim 41

Dependent Claim 15 words

The method of claim 27 wherein the impregnating steps (a) and (b) are practiced simultaneously.

Claim 42

Dependent Claim 18 words

The method of claim 28 wherein the impregnating steps (a) and (b) are practiced sequentially, in any order.

Claim 43

Dependent Claim 15 words

The method of claim 28 wherein the impregnating step (a) and (b) are practiced simultaneously.

Claim 44

Independent Claim 156 words

A method for preparing a Group VIII metal-phosphorus compound supported on a high surface area solid support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals and mixtures thereof, wherein the Group VIII metal-phosphorus compound has a crystallite size of about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) reducing the supported Group VIII metal salt of (a) to a supported Group VIII metal at a temperature in the range of about 200° to about 650° C.; and (c) impregnating the material of step (b) with phosphorus by means of the vapor deposition method in a vacuum.

Claim 45

Independent Claim 156 words

A method for preparing a Group VIII metal-phosphorus compound supported on a high surface area solid support selected from the group consisting of carbon, alumina, silica, silica-alumina, zeolite, kieselguhr, vermiculite, the refractory oxides of Group IVb and Vb transition metals and mixtures thereof, wherein the Group VIII metal-phosphorus compound has a crystallite size of about 300 A or less, wherein the process consists of the steps of: (a) impregnating said high surface area support with a solution of at least one water soluble Group VIII metal salt selected from the group consisting of Group VIII metal chlorides, Group VIII metal nitrates and Group VIII metal ammonia complexes; (b) reducing the supported Group VIII metal salt of (a) to a supported Group VIII metal at a temperature in the range of about 200° to about 650° C.; and (c) impregnating the material of step (b) with phosphorus by means of the vapor deposition method in a vacuum.

Claim 46

Dependent Claim 39 words

The method of claim 39 wherein the water soluble Group VIII metal salts are selected from the group consisting of water soluble Group VIII noble metal chlorides, Group VIII noble metal nitrates and Group VIII noble metal ammonia complexes.

Claim 47

Dependent Claim 27 words

The method of claim 39 wherein the Group VIII noble metal salts are selected from the group consisting of platinum chloride, platinum nitrate and platinum ammonia complexes.

Claim 48

Dependent Claim 38 words

The method of claim 39 wherein the support is selected from the group consisting of carbon, alumina, silica-alumina and mixtures thereof and the surface area of the support ranges from about 10 to about 2000 m 2 /g.

Claim 49

Dependent Claim 10 words

The method of claim 42 wherein the support is carbon.

Claim 50

Dependent Claim 17 words

The method of claim 39 wherein the phosphorus deposited by the vapor deposition method is red phosphorus.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1985-11-15	1986-05-17	1986-11-16	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1989-11-15	1990-05-17	1990-11-16	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1993-11-15	1994-05-17	1994-11-16	$7700.00	Window Closed / Lapsed

Highly dispersed supported group VIII metal-phosphorus compounds, and highly dispersed, supported group VIII metal-arsenic and a process for making said compounds

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag