Photochromic glass suitable for microsheet and simultaneous heat treatment and shaping

Claim 1

A photochromic glass composition consisting essentially, as analyzed in weight percent on the oxide basis, of SiO 2 --55-60 Al 2 O 3 --9-10 B 2 O 3 --19-20.5 Li 2 O--2-2.5 Na 2 O--2-3 K 2 O--6-7 PbO--0.1-0.25 Ag--0.1-0.15 Cl--0.3-0.5 Br--0.05-0.15 CuO--0.0065-0.01 demonstrating long term stability against devitrification at temperatures corresponding to glass viscosities in the range of 10 4 -10 6 poises, an opalization liquidus temperature-glass viscosity relationship such that phase separation does not occur as glass is drawn into sheet, excellent chemical durability, and the capability of being chemically strengthened to modulus of rupture values in excess of 30,000 psi with a depth of compression layer in excess of 0.025 inch, said glass, in a cross section of about 1.5 mm, exhibiting the following photochromic properties: (a) a clear luminous transmittance in the vicinity of 90% when free from tint; (b) a darkened luminous transmittance at 20° C. below 25% when the glass is free from tint, and below 20% when the glass is tinted to a level of at least 75%; (c) a fading rate at 20° C. such that the glass demonstrates a faded luminous transmittance of at least twice that of the darkened transmittance after a five-minute fading interval from the darkened state; (d) a darkened luminous transmittance at 40° C. below 45% when the glass is free from tint, and below 40% when the glass is tinted to a level of at least 75%; and (e) a fading rate at 40° C. such that the glass demonstrates a faded luminous transmittance of at least 1.75 times that of the darkened transmittance after a five-minute fading interval from the darkened state.

Claim 5

A method for forming glass sheet from potentially photochromic glass and thereafter simultaneously shaping articles from said glass sheet and developing photochromic properties therein which comprises the steps of: (a) melting a batch for a glass consisting essentially, as analyzed in weight percent on the oxide basis, of SiO 2 --55-60 Al 2 O 3 --9-10 B 2 O 3 --19-20.5 Li 2 O--2-2.5 Na 2 O--2-3 K 2 O--6-7 PbO--0.1-0.25 Ag--0.1-0.15 Cl--0.3-0.5 Br--0.05-0.15 CuO--0.0065-0.01 (b) adjusting the temperature of at least one region of the glass melt to provide a viscosity therein of about 10 4 -10 6 poises; (c) drawing the glass melt at a viscosity of about 10 4 -10 6 poises to produce potentially photochromic drawn glass sheet of optical quality; (d) cooling the glass sheet below the softening point of the glass and cutting articles of desired geometries therefrom; (e) edge supporting said articles on alveolated molds; and then (f) subjecting heating said articles at a temperature between about 650°-675° C. for a period of time sufficient to simultaneously sag the glass to a desired curvature into the concave portions of the alveolated molds, but not into contact with the inner surface of said molds, and develop photochromic properties in the glass; said glass demonstrating long term stability against devitrification at temperatures corresponding to glass viscosities in the range of 10 4 -10 6 poises, an opalization liquidus temperature-glass viscosity relationship such that phase separation does not occur as glass is drawn into sheet, excellent chemical durability, the capability of being chemically strengthened to modulus of rupture values in excess of 30,000 psi with a depth of compression layer in excess of 0.025 inch, and, in a cross section of about 1.5 mm, exhibiting the following photochromic properties: (a) a clear luminous transmittance in excess of 90% when free from tint; (b) a darkened luminous transmittance at 20° C. below 25% when the glass is free from tint, and below 20% when the glass is tinted to a level of at least 75%; (c) a fading rate at 20° C. such that the glass demonstrates a faded luminous transmittance of at least twice that of the darkened transmittance after a five-minute fading interval from the darkened state; (d) a darkened luminous transmittance at 40° C. below 45% when the glass is free from tint, and below 40% when the glass is tinted to a level of at least 75%; and (e) a fading rate at 40° C. such that the glass demonstrates a faded luminous transmittance of at least 1.75 times that of the darkened transmittance after a five-minute fading interval from the darkened state.

Claim 6

A method for forming glass sheet from potentially photochromic glass and thereafter simultaneously shaping articles from said glass sheet and developing photochromic properties therein which comprises the steps of: (a) melting a batch for a glass consisting essentially, as analyzed in weight percent on the oxide basis, of SiO 2 --55-60 Al 2 O 3 --9-10 B 2 O 3 --19-20.5 Li 2 O--2-2.5 Na 2 O--2-3 K 2 O--6-7 PbO--0.1-0.25 Ag--0.1-0.15 Cl--0.3-0.5 Br--0.05-0.15 CuO--0.0065-0.01 (b) adjusting the temperature of at least one region of the glass melt to provide a viscosity therein of about 10 4 -10 6 poises; (c) drawing the glass melt at a viscosity of about 10 4 -10 6 poises to produce potentially photochromic drawn glass sheet of optical quality; (d) cooling the glass sheet below the softening point of the glass and cutting articles of desired geometries therefrom; (e) edge supporting said articles on alveolated molds; and then (f) subjecting heating said articles at a temperature between about 650°-675° C. for a period of time sufficient to simultaneously sag the glass to a desired curvature into the concave portions of the alveolated molds, but not into contact with the inner surface of said molds, and develop photochromic properties in the glass; said glass demonstrating long term stability against devitrification at temperatures corresponding to glass viscosities in the range of 10 4 -10 6 poises, an opalization liquidus temperature-glass viscosity relationship such that phase separation does not occur as glass is drawn into sheet, excellent chemical durability, the capability of being chemically strengthened to modulus of rupture values in excess of 30,000 psi with a depth of compression layer in excess of 0.025 inch, and, in a cross section of about 1.5 mm, exhibiting the following photochromic properties: (a) a clear luminous transmittance in excess of 90% when free from tint; (b) a darkened luminous transmittance at 20° C. below 25% when the glass is free from tint, and below 20% when the glass is tinted to a level of at least 75%; (c) a fading rate at 20° C. such that the glass demonstrates a faded luminous transmittance of at least twice that of the darkened transmittance after a five-minute fading interval from the darkened state; (d) a darkened luminous transmittance at 40° C. below 45% when the glass is free from tint, and below 40% when the glass is tinted to a level of at least 75%; and (e) a fading rate at 40° C. such that the glass demonstrates a faded luminous transmittance of at least 1.75 times that of the darkened transmittance after a five-minute fading interval from the darkened state.