Safety laminate and process for production thereof
Assignee: Sekisui Chemical Co Ltd
•
Filing: 1980-08-25
•
Granted: 1982-11-09
•
Expires: 2000-08-25
Abstract
Abstract A process for producing a safety laminate comprising at least two plates bonded to each other through an adhesive interlayer, which comprises (1) applying an adhesiveness-imparting agent being liquid at ambient temperature and substantially non-adhesive to said plates to at least one of (a) the surface of each of said plates and (b) each surface to be bonded to said surface (a) of a sheet-like adhesive material which is substantially non-adhesive, and only latently adhesive, to said plates, said adhesiveness-imparting agent being capable of developing the latent adhesiveness of said sheet-like adhesive material; and (2) sandwiching said sheet-like adhesive material as an interlayer between two of said plates to bond said plates through the interlayer of said sheet-like adhesive material having its adhesiveness developed; and a safety laminate produced by aforesaid process.
Inventors
- 👤 Eisuke Masuda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 06:46
CPC Classifications
B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/1055; B32B17/10697; B32B17/10009; B32B17/10018; B32B17/10036; B32B17/10605; B32B17/10688; B32B17/10743; B32B17/10761; B32B17/10788; B32B2367/00; B32B7/00; B32B7/04; B32B7/12; C; C09; C09J; C09J5/00; C09J5/04; B32B2327/00; B32B2327/06; B32B2333/00; B32B2333/04; B32B2333/08; B32B2369/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31616; Y10T428/31623; Y10T428/31627; Y10T428/3163
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
165 words
A process for producing a safety laminate comprising at least two plates bonded to each other through an adhesive interlayer, which comprises applying an adhesiveness-imparting agent which is liquid at ambient temperature and is substantially non-adhesive to said plates to at least one of (a) the surface of each of said plates and (b) each surface to be bonded to said surface of said plates of a sheet-like adhesive material which is substantially non-adhesive, but which is latently adhesive, to said plates, said adhesiveness-imparting agent being a plasticizer capable of developing the latent adhesiveness of said sheet-like adhesive material to render it adhesive and wherein said sheet-like adhesive material is composed of a material selected from the group consisting of acrylic resins, polyvinylbutyral resins and polyester resins; and sandwiching said sheet-like adhesive material as an interlayer between two of said plates at ambient temperature to bond said plates through the interlayer of said sheet-like adhesive material when the adhesiveness is developed by the adhesiveness-imparting agent.
Claim 2
Dependent Claim
165 words
A process for producing a safety laminate comprising at least two plates bonded to each other through an adhesive interlayer, which comprises applying an adhesiveness-imparting agent which is liquid at ambient temperature and is substantially non-adhesive to said plates to at least one of (a) the surface of each of said plates and (b) each surface to be bonded to said surface of said plates of a sheet-like adhesive material which is substantially non-adhesive, but which is latently adhesive, to said plates, said adhesiveness-imparting agent being a plasticizer capable of developing the latent adhesiveness of said sheet-like adhesive material to render it adhesive and wherein said sheet-like adhesive material is composed of a material selected from the group consisting of acrylic resins, polyvinylbutyral resins and polyester resins; and sandwiching said sheet-like adhesive material as an interlayer between two of said plates at ambient temperature to bond said plates through the interlayer of said sheet-like adhesive material when the adhesiveness is developed by the adhesiveness-imparting agent.
Claim 3
Dependent Claim
11 words
The process of claim 1 wherein said plates are glass sheets.
Claim 4
Dependent Claim
20 words
The process of claim 1 wherein at least one of said plates is a plate of an organic synthetic resin.
Claim 5
Dependent Claim
34 words
The process of claim 1 wherein said sheet-like adhesive material is composed of a material which is substantially non-adhesive and has a tack number of 3 or less determined by the tack testing method.
Claim 6
Dependent Claim
26 words
The process of claim 4 wherein said sheet-like adhesive material is composed of a material which is only latently adhesive and is non-tacky at ambient temperature.
Claim 7
Dependent Claim
54 words
The process of claim 1 wherein said sheet-like adhesive material consists of a film substrate having a tensile strength of at least 100 kg/cm 2 and an elongation of at least 100% and formed on both surfaces thereof, a layer of a material which is substantially non-adhesive, and only latently adhesive, to said plates.
Claim 8
Dependent Claim
20 words
The process of claim 1 wherein said adhesiveness-imparting agent has a viscosity of 1 to 500 centipoises at ambient temperature.
Claim 9
Dependent Claim
54 words
The process of claim 1 wherein said latently adhesive sheet-like adhesive material is made of an acrylic resin, and said adhesiveness-imparting agent is at least one member liquid at ambient temperature which is selected from the group consisting of phthalic esters, trimellitic esters, sebacic esters, glycerin esters, orthophosphoric esters, fumaric esters and maleic esters.
Claim 10
Dependent Claim
48 words
The process of claim 1 wherein said latently adhesive sheet-like adhesive material is made of a polyvinylbutyral resin, and said adhesiveness-imparting agent is at least one member liquid at ambient temperature which is selected from the group consisting of phthalic esters, ricinoleic esters, orthophthalic esters and glycol esters.
Claim 11
Dependent Claim
50 words
The process of claim 1 wherein said latently adhesive sheet-like adhesive material is made of a polyester resin, and said adhesiveness-imparting agent is at least one member liquid at ambient temperature which is selected from the group consisting of phthalic esters, orthophthalic esters, glycol esters, maleic esters and fumaric esters.
References Cited (Backward Citations)
US3388034A
Cited
US3388032A
Cited
US3539412A
Cited
US3458388A
Cited
GB1219630A
Cited
US4020217A
Cited
US4277538A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-08 | 1986-05-10 | 1986-11-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-08 | 1990-05-10 | 1990-11-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-08 | 1994-05-10 | 1994-11-09 | $7700.00 | Window Closed / Lapsed |