Sorbents of cellulose basis capable of forming inclusion complexes and a process for the preparation thereof
Assignee: Chinoin Private Co Ltd
•
Filing: 1981-07-31
•
Granted: 1982-11-02
•
Expires: 2001-07-31
Abstract
Abstract The invention relates to new sorbents of cellulose basis capable of forming inclusion complexes, as well as to a process for the preparation thereof. The new sorbents according to the invention are cellulose derivatives containing structural units of the general formula (I), ##STR1## wherein Cell is a group derived by removing m hydroxy groups from the glucose unit of the cellulose chain, m is an integer of 1 to 3, CD is a group derived by removing one hydroxy group from the α, β or γ-cyclodextrin molecule, n is an integer of 1 to 5, and p stands for 0 or 1, which may optionally vary even within a single chain. The cellulose derivatives according to the invention are substances of loose structure, with large specific surface area and good swelling properties, which can be applied for solving the most diverse adsorption tasks. Thus e.g. the substances can be applied for the preparation of smoke filters in cigarettes, waste water purification (de-poisoning) filters, inserts for removing solvent vapors, etc., furthermore for solving specific tasks of fractionation according to molecular dimensions.
Inventors
- 👤 Jozsef Szejtli
- 👤 Bela Zsadon
- 👤 Eva Fenyvesi
- 👤 nee Otta Horvath
- 👤 Ferenc Tudos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:44
CPC Classifications
C; C08; C08B; C08B37/00; C08B37/0006; C08B37/0009; C08B37/0012; C08B11/00; C08B11/02; C08B11/04; C08B11/08
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
78 words
A cellulose derivative containing structural units of the formula (I), ##STR6## wherein Cell is a group derived by removing m hydroxy groups from the glucose unit of the cellulose chain, m is an integer of 1 to 3, CD is a group derived by removing one hydroxy group from the α, β or γ-cyclodextrin molecule, n is an integer of 1 to 5, and p stands for 0 or 1 and can vary even within a single chain.
Claim 2
Dependent Claim
78 words
A cellulose derivative containing structural units of the formula (I), ##STR6## wherein Cell is a group derived by removing m hydroxy groups from the glucose unit of the cellulose chain, m is an integer of 1 to 3, CD is a group derived by removing one hydroxy group from the α, β or γ-cyclodextrin molecule, n is an integer of 1 to 5, and p stands for 0 or 1 and can vary even within a single chain.
Claim 3
Dependent Claim
23 words
A cellulose derivative as claimed in claim 1, wherein CD is a group derived by removing one hydroxy group from the α-cyclodextrin molecule.
Claim 4
Dependent Claim
23 words
A cellulose derivative as claimed in claim 1, wherein CD is a group derived by removing one hydroxy group from the β-cyclodextrin molecule.
Claim 5
Dependent Claim
23 words
A cellulose derivatives as claimed in claim 1, wherein DC is a group derived by removing one hydroxy group from the γ-cyclodextrin molecule.
Claim 6
Dependent Claim
27 words
A cellulose derivative as defined in claim 1, wherein CD stands for a group derived by removing one hydroxy group from an α, β or γ-cyclodextrin molecule.
Claim 7
Dependent Claim
12 words
A sorption element comprising a cellulose derivative as defined in claim 1.
Claim 8
Dependent Claim
258 words
A process for the preparation of a cellulose derivative containing structural units of the formula (I), ##STR7## wherein Cell is a group derived by removing m hydroxy groups from the glucose unit of the cellulose chain, m is an integer of 1 to 3, CD is a group derived by removing one hydroxy group from an α, β or γ-cyclodextrin molecule, n is an integer of 1 to 5, and p stands for 0 or 1 and can vary even within a single chain, comprising the steps of (a) reacting one part by weight of cellulose, regenerated cellulose or other cellulose-containing fibrous material preswollen in water with 5 to 30 parts by weight of epichlorohydrin or 1,2-bis(2,3-epoxypropoxy)-ethane in the presence of 10 to 65 parts by weight of water and 1.5 to 5 parts by weight of an alkali metal or alkaline earth metal hydroxide, and the resulting solid product is reacted with 1 to 2 parts by weight of a cyclodextrin in the presence of 1 to 40 parts by weight of an alkali metal or alkaline earth metal hydroxide and 10 to 100 parts by weight of water; or (b) reacting 1 part by weight of cellulose, regenerated cellulose or other cellulose-containing fibrous material preswollen in water and 1 to 2 parts by weight of a cyclodextrin with 15 to 40 parts by weight of epichlorohydrin or 1,2-bis(2,3-epoxypropoxy)-ethane in the presence of 40 to 65 parts by weight of water and 10 to 30 parts by weight of an alkali metal or alkaline earth metal hydroxide.
Claim 9
Dependent Claim
258 words
A process for the preparation of a cellulose derivative containing structural units of the formula (I), ##STR7## wherein Cell is a group derived by removing m hydroxy groups from the glucose unit of the cellulose chain, m is an integer of 1 to 3, CD is a group derived by removing one hydroxy group from an α, β or γ-cyclodextrin molecule, n is an integer of 1 to 5, and p stands for 0 or 1 and can vary even within a single chain, comprising the steps of (a) reacting one part by weight of cellulose, regenerated cellulose or other cellulose-containing fibrous material preswollen in water with 5 to 30 parts by weight of epichlorohydrin or 1,2-bis(2,3-epoxypropoxy)-ethane in the presence of 10 to 65 parts by weight of water and 1.5 to 5 parts by weight of an alkali metal or alkaline earth metal hydroxide, and the resulting solid product is reacted with 1 to 2 parts by weight of a cyclodextrin in the presence of 1 to 40 parts by weight of an alkali metal or alkaline earth metal hydroxide and 10 to 100 parts by weight of water; or (b) reacting 1 part by weight of cellulose, regenerated cellulose or other cellulose-containing fibrous material preswollen in water and 1 to 2 parts by weight of a cyclodextrin with 15 to 40 parts by weight of epichlorohydrin or 1,2-bis(2,3-epoxypropoxy)-ethane in the presence of 40 to 65 parts by weight of water and 10 to 30 parts by weight of an alkali metal or alkaline earth metal hydroxide.
Claim 10
Dependent Claim
20 words
A process as defined in claim 7 wherein the reaction is performed at a temperature of 40° to 80° C.
Claim 11
Dependent Claim
14 words
A process as defined in claim 7 wherein α-cyclodextrin is used as the cyclodextrin.
Claim 12
Dependent Claim
14 words
A process as defined in claim 7 wherein β-cyclodextrin is used as the cyclodextrin.
Claim 13
Dependent Claim
14 words
A process as defined in claim 7 wherein γ-cyclodextrin is used as the cyclodextrin.
Claim 14
Dependent Claim
17 words
A process as defined in claim 7 wherein viscose fibers are used as the cellulose-containing fibrous material.
Claim 15
Dependent Claim
18 words
A process as defined in claim 7 wherein shredded tissue paper is used as the cellulose-containing fibrous material.
Claim 16
Dependent Claim
18 words
A process as defined in claim 7 wherein ground oak bark is used as the cellulose-containing fibrous material.
Claim 17
Dependent Claim
16 words
A process as defined in claim 7 wherein granular cellulose is used as the cellulosic material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-01 | 1986-05-03 | 1986-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-01 | 1990-05-03 | 1990-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-01 | 1994-05-03 | 1994-11-02 | $7700.00 | Window Closed / Lapsed |