Abstract Biaxially oriented low cost polyolefin bottles of improved optical clarity, gloss, and strength, and useful for packaging materials such as liquid detergents, shampoos, pharmaceuticals and intravenous solutions, are prepared by stretch blow molding polypropylene homopolymer co-polymer and allomer parisons or preforms which are formed from low temperature melts at temperatures just above the melting points of the polymers and allomers, and are injected at constant rates against cold polished mold surfaces at relatively low pressures and at slow rates to avoid melt fractures. Melt temperatures of from 490° to 700° F. are preferred for polypropylene blow mold type polymers and allomers. Polished beryllium copper mold surfaces are desired for high luster gloss finishes. Mold temperatures of from 30° to 80° F. are preferred. Injection molding with a high compression ratio of 3 to 3.5 for insuring a homogeneous melt is preferred with a relatively slow injection rate to fil the mold cavity of about 3 to 10 seconds. The low temperature molding limits the size and increases the number of spherulites that form as the melt cools and solidifies thus minimizing crystallinity in the parison. The low mold temperatures provide faster molding cycles, increasing production and reducing costs but the injection rate is sufficiently slow to avoid melt fracture. The strength blow molding is preferably conducted at temperatures just below the amorphous flow temperature of the parison with temperatures of about 295° F. being sufficient for the polypropylene copolymer and about 325° F. below satisfactory for the polypropylene homopolymer.
A method for making a blow-molded clear polypropylene bottle; comprising working and heating crystalline polypropylene so as to form a melt, causing a sample of said melt to fall and while falling determining the appearance of the sample, controlling said working and heating so as to provide said melt with a temperature not substantially higher than causes said sample to change from a cloudy appearance to a clear appearance, flowing said melt while at said temperature onto a polished cold surface having a temperature no higher than room temperature so as to form a parison, said melt being flowed at a rate slower than one causing said melt to fracture during said flowing, allowing said parison to cool so as to solidify and removing it from said cold surface, heating said parison to a stretch blow molding temperature just below its amorphous flow temperature and no higher than the minimum permitting stretch blow molding of the parison, placing the parison in a stretch blow molding die having a temperature no higher than room temperature and having a cavity shaped to form said bottle, the cavity having a bottom for forming the bottle's bottom, and stretch blow molding the parison by stretching it first completely to the cavity's said bottom while at the same time blowing the parison only so as to cause it to only partially fit said cavity, and only thereafter completely blowing the parison so as to cause it to completely fit said cavity and form said bottle, and removing the bottle from said cavity.
Claim 2
Independent Claim
257 words
A method for making a blow-molded clear polypropylene bottle; comprising working and heating crystalline polypropylene so as to form a melt, causing a sample of said melt to fall and while falling determining the appearance of the sample, controlling said working and heating so as to provide said melt with a temperature not substantially higher than causes said sample to change from a cloudy appearance to a clear appearance, flowing said melt while at said temperature onto a polished cold surface having a temperature no higher than room temperature so as to form a parison, said melt being flowed at a rate slower than one causing said melt to fracture during said flowing, allowing said parison to cool so as to solidify and removing it from said cold surface, heating said parison to a stretch blow molding temperature just below its amorphous flow temperature and no higher than the minimum permitting stretch blow molding of the parison, placing the parison in a stretch blow molding die having a temperature no higher than room temperature and having a cavity shaped to form said bottle, the cavity having a bottom for forming the bottle's bottom, and stretch blow molding the parison by stretching it first completely to the cavity's said bottom while at the same time blowing the parison only so as to cause it to only partially fit said cavity, and only thereafter completely blowing the parison so as to cause it to completely fit said cavity and form said bottle, and removing the bottle from said cavity.