Thermoplastic elastomer blends of a nitrile rubber and a crystalline polyamide mixture

Claim 2

A process for preparing blends of a nitrile rubber and a crystalline polyamide mixture, comprising the steps of: obtaining a nitrile rubber, the amount of nitrile component in said nitrile rubber ranging from about 10 percent to about 60 percent by weight, said nitrile component being derived from monomers selected from the group consisting of acrylonitrile, methacrylonitrile, vinylidene cyanide, and fumaronitrile, the diene component of said nitrile rubber being derived from monomers selected from the group consisting of (1) conjugated dienes having from 4 to 10 carbon atoms, (2) at least two conjugated dienes having from 4 to 10 carbon atoms, (3) chloroprene, (4) vinyl substituted aromatic compounds having from 7 to 12 carbon atoms and (a) conjugated diene having from 4 to 10 carbon atoms or (b) chloroprene and combinations thereof; adding to and blending with said nitrile rubber a crystalline polyamide mixture of a first polyamide having a high melting point and a second polyamide having a lower melting point than said first polyamide, the total amount of said polyamide mixture ranging from about 80 percent to about 20 percent by weight based on said nitrile rubber and the total weight of said polyamides; and, mixing and heating said nitrile rubber and said polyamide mixture at a temperature below the melting point of said first polyamide having the higher melting point and above the melting point of said second polyamide having said lower melting point to produce a processable thermoplastic elastomer blend, said mixing temperature ranging from 185° to 220° C.

Claim 3

A process according to claim 1 wherein the amount of said high melting polyamide to said total polyamide mixture is at least 15 percent by weight, and wherein the melting point of said lower melting point polyamide is at least 5° C. below said higher melting polyamide.

Claim 4

A process according to claim 2 wherein said polyamides are selected from the group consisting of Nylon-6, Nylon-11, Nylon-12, Nylon-6-6, and a polycaprolactam copolymer having a melting point of about 142° C.

Claim 5

A process according to claim 3 wherein the amount of said nitrile component of said nitrile rubber ranges from about 15 percent to about 50 percent by weight and wherein the amount of said nitrile rubber ranges from about 50 percent to about 75 percent by weight based upon the total weight of said nitrile rubber and said polyamide mixture, and wherein said mixing temperature is from about 200° C. to about 215° C.

Claim 6

A process for preparing blends of a nitrile rubber and a crystalline polyamide mixture, comprising the steps of: obtaining a crystalline polyamide mixture of a first polyamide having a high melting point and a second polyamide having a lower melting point than said first polyamide, the total amount of said polyamide mixture ranging from about 80 percent to about 20 percent by weight based on said nitrile rubber and the total weight of said polyamides; adding to and blending with said crystalline polyamide mixture a nitrile rubber, the amount of nitrile component in said nitrile rubber ranging from about 10 percent to about 60 percent by weight, said nitrile component being derived from monomers selected from the group consisting of acrylonitrile, methacrylonitrile, vinylidene cyanide, and fumaronitrile, the diene component of said nitrile rubber being derived from monomers selected from the group consisting of (1) conjugated dienes having from 4 to 10 carbon atoms, (2) at least two conjugated dienes having from 4 to 10 carbons, (3) chloroprene, (4) vinyl substituted aromatic compounds having from 7 to 12 carbon atoms and (a) conjugated dienes having from 4 to 10 carbon atoms or (b) chloroprene, and combinations thereof; and mixing and heating said polyamide mixture and said nitrile mixture at a temperature below the melting point of said first polyamide having the higher melting point and above the melting point of said second polyamide having the lower melting point to produce a processable thermoplastic elastomer blend, said mixing temperature ranging from 185° C. to 220° C.

Claim 7

A process for preparing blends of a nitrile rubber and a crystalline polyamide mixture, comprising the steps of: obtaining a crystalline polyamide mixture of a first polyamide having a high melting point and a second polyamide having a lower melting point than said first polyamide, the total amount of said polyamide mixture ranging from about 80 percent to about 20 percent by weight based on said nitrile rubber and the total weight of said polyamides; adding to and blending with said crystalline polyamide mixture a nitrile rubber, the amount of nitrile component in said nitrile rubber ranging from about 10 percent to about 60 percent by weight, said nitrile component being derived from monomers selected from the group consisting of acrylonitrile, methacrylonitrile, vinylidene cyanide, and fumaronitrile, the diene component of said nitrile rubber being derived from monomers selected from the group consisting of (1) conjugated dienes having from 4 to 10 carbon atoms, (2) at least two conjugated dienes having from 4 to 10 carbons, (3) chloroprene, (4) vinyl substituted aromatic compounds having from 7 to 12 carbon atoms and (a) conjugated dienes having from 4 to 10 carbon atoms or (b) chloroprene, and combinations thereof; and mixing and heating said polyamide mixture and said nitrile mixture at a temperature below the melting point of said first polyamide having the higher melting point and above the melting point of said second polyamide having the lower melting point to produce a processable thermoplastic elastomer blend, said mixing temperature ranging from 185° C. to 220° C.

Claim 8

A process according to claim 5, wherein said mixing temperature ranges from about 200° to about 215° C.