Method of field annealing an amorphous metal core by means of induction heating
Assignee: Electric Power Research Institute
•
Filing: 1981-04-20
•
Granted: 1982-10-19
•
Expires: 2001-04-20
Abstract
Abstract A magnetic core is disclosed herein along with associated electrical coils which together with the core form part of an overall electrical inductive apparatus such as a transformer. The core itself is one which is initially formed from a continuous strip of amorphous metal wound about itself to form a closed loop of adjacent laminations. Thereafter but before the core is annealed causing it to lose its ductility and flexibility, one section thereof is provided with a joint which is flexed open to receive the electrical coils. Once the coils have been suitably assembled around the core, the latter is annealed by means of induction heating. More specifically, one of the coils is energized at a relatively high frequency for inducing a current through the core sufficient to heat the latter to satisfactory annealing temperatures for a prescribed period of time.
Inventors
- 👤 Kou C. Lin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 02:02
CPC Classifications
H; H01; H01F; H01F41/00; H01F41/02; H01F41/0206; C; C21; C21D; C21D1/00; C21D1/34; C21D1/42; C21D9/00; C21D9/52; C21D9/54; Y; Y02; Y02P; Y02P10/00; Y02P10/25; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/4902; Y10T29/49075; Y10T29/49078
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
148 words
In an electrical transformer including a core initially formed from a continuous strip of amorphous metal wound about itself to form a closed-loop and at least one insulation coated transformer coil located around one circumferential section of said core, the material making up said coil being selected to have substantially lower electrical resistivity than said amorphous metal core, a method of annealing said core after said transformer coil has been positioned around said core section, said method comprising the step of placing said core and transformer coil in close proximity to an induction coil, exciting said induction coil with an alternating current for inducing current through said core and transformer coil to heat the core to satisfactory annealing temperatures for a period of time sufficient to anneal said core without heating said transformer coil to a temperature sufficient to damage its insulation coating during said period of time.
Claim 2
Dependent Claim
148 words
In an electrical transformer including a core initially formed from a continuous strip of amorphous metal wound about itself to form a closed-loop and at least one insulation coated transformer coil located around one circumferential section of said core, the material making up said coil being selected to have substantially lower electrical resistivity than said amorphous metal core, a method of annealing said core after said transformer coil has been positioned around said core section, said method comprising the step of placing said core and transformer coil in close proximity to an induction coil, exciting said induction coil with an alternating current for inducing current through said core and transformer coil to heat the core to satisfactory annealing temperatures for a period of time sufficient to anneal said core without heating said transformer coil to a temperature sufficient to damage its insulation coating during said period of time.
Claim 3
Dependent Claim
34 words
A method according to claim 1 wherein said annealing temperature is between 260° C. and 320° C. at the outer core when the latter is a one-half pound core wound from 2605SC METGLAS material.
Claim 4
Dependent Claim
17 words
A method according to claim 2 wherein said period of time is between 1 and 3 hours.
Claim 5
Dependent Claim
38 words
A method according to claim 1, including the step of exciting said transformer coil around said core for producing a magnetic field during the time said induction coil is excited sufficient to develop magnetic anisotropy in said core.
Claim 6
Dependent Claim
34 words
A method according to claim 1 including the step of thermally insulating said transformer coil including its insulation coating from said core sufficient to prevent heat from the core from damaging said insulation coating.
Claim 7
Dependent Claim
201 words
In an electrical transformer including an amorphous metal core having a closed-loop shape and an insulator coated transformer coil located around one section of said core, the material making up said coil being selected to have substantially lower electrical resistivity than said amorphous metal core, a method of forming and annealing said core comprising the steps of winding a continuous strip of flexible, non-annealed amorphous metal into said closed-loop shape core, cutting said core across a circumferential section prior to annealing thereof whereby to gain access to said one core section for positioning said insulation coated transformer coil around said one section, thereafter positioning said insulation coated transformer coil around said one section, with a layer of thermal insulation directly therebetween, and subsequently placing said core and transformer coil within an induction coil and exciting said induction coil with an alternating current for inducing currents through said core to heat the latter to a satisfactory annealing temperature for a period of time sufficient to anneal said core without heating said transformer coil to a temperature sufficient to damage its insulation coating during said period of time and without causing the heat from the core to damage the immediately adjacent insulation coating.
Claim 8
Dependent Claim
201 words
In an electrical transformer including an amorphous metal core having a closed-loop shape and an insulator coated transformer coil located around one section of said core, the material making up said coil being selected to have substantially lower electrical resistivity than said amorphous metal core, a method of forming and annealing said core comprising the steps of winding a continuous strip of flexible, non-annealed amorphous metal into said closed-loop shape core, cutting said core across a circumferential section prior to annealing thereof whereby to gain access to said one core section for positioning said insulation coated transformer coil around said one section, thereafter positioning said insulation coated transformer coil around said one section, with a layer of thermal insulation directly therebetween, and subsequently placing said core and transformer coil within an induction coil and exciting said induction coil with an alternating current for inducing currents through said core to heat the latter to a satisfactory annealing temperature for a period of time sufficient to anneal said core without heating said transformer coil to a temperature sufficient to damage its insulation coating during said period of time and without causing the heat from the core to damage the immediately adjacent insulation coating.
Claim 9
Dependent Claim
35 words
A method according to claim 6 including the step of exciting said transformer coil for producing a magnetic field during the time said induction coil is excited sufficient to develop magnetic anisotropy in said core.
References Cited (Backward Citations)
US2002696A
Cited
US2688573A
Cited
US4116728A
Cited
US4116728B1
Cited
US4236230A
Cited
US4281234A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-18 | 1986-04-19 | 1986-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-18 | 1990-04-19 | 1990-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-18 | 1994-04-19 | 1994-10-19 | $7700.00 | Window Closed / Lapsed |