Method for recovery of terephthalic acid from polyester scrap
Assignee: Individual
•
Filing: 1981-04-06
•
Granted: 1982-10-19
•
Expires: 2001-04-06
Abstract
Abstract Polyester scrap such as film (plain or silver-bearing), fabric, yarn or bottles, based primarily on polyethylene terephthalate, is depolymerized at room temperature and atmospheric pressure with a mixture of concentrated sulfuric acid and water to form crude terephthalic acid which is purified by dissolving in alkali solution, filtering to remove impurities, acidifying the filtrate to recover terephthalic acid in high yield with a purity of at least 99%.
Inventors
- 👤 Stephen F. Pusztaszeri
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 07:27
CPC Classifications
C; C07; C07C; C07C51/00; C07C51/09; C08; C08J; C08J11/00; C08J11/04; C08J11/10; C08J11/16; C08J2367/00; C08J2367/02; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
171 words
A method for the recovery of purified terephthalic acid from terephthalate polyester scrap substantially free of metals, said method comprising the steps of: (a) dissolving the polyester in a mixture of sulfuric acid and water in a volume ratio of 8.5-13 to 2 for a period of up to 30 minutes to form a precipitate of crude terephthalic acid; (b) diluting the reaction mixture from step (a) with at least an equal volume of water and separating the crude terephthalic acid; (c) treating the crude terephthalic acid from step (b) with water and a base selected from the group consisting of potassium hydroxide, sodium hydroxide and ammonium hydroxide to form a solution of a water-soluble salt of the acid; (d) filtering the solution from step (c) to remove solid impurities; (e) acidifying the filtrate from step (d) with acid to form a precipitate of purified terephthalic acid; (f) separating the purified terephthalic acid from step (e); and (g) washing the terephthalic acid from step (f) until it is acid- and salt-free.
Claim 2
Independent Claim
171 words
A method for the recovery of purified terephthalic acid from terephthalate polyester scrap substantially free of metals, said method comprising the steps of: (a) dissolving the polyester in a mixture of sulfuric acid and water in a volume ratio of 8.5-13 to 2 for a period of up to 30 minutes to form a precipitate of crude terephthalic acid; (b) diluting the reaction mixture from step (a) with at least an equal volume of water and separating the crude terephthalic acid; (c) treating the crude terephthalic acid from step (b) with water and a base selected from the group consisting of potassium hydroxide, sodium hydroxide and ammonium hydroxide to form a solution of a water-soluble salt of the acid; (d) filtering the solution from step (c) to remove solid impurities; (e) acidifying the filtrate from step (d) with acid to form a precipitate of purified terephthalic acid; (f) separating the purified terephthalic acid from step (e); and (g) washing the terephthalic acid from step (f) until it is acid- and salt-free.
Claim 3
Dependent Claim
18 words
The method according to claim 1, wherein step (a) is carried out at room temperature and atmospheric pressure.
Claim 4
Dependent Claim
13 words
The method according to claim 1, wherein said ratio is 11 to 2.
Claim 5
Dependent Claim
22 words
The method according to claim 1, wherein sufficient base is added in step (c) to obtain a pH of 6 to 13.
Claim 6
Dependent Claim
11 words
The method according to claim 4, wherein the pH is 11.
Claim 7
Dependent Claim
20 words
The method according to claim 4, wherein sufficient acid is added in step (e) to obtain a pH of 0-3.
Claim 8
Independent Claim
30 words
The method according to any one of claims 1, 4 and 6, wherein the polyester scrap is in the form of a film from which silver has previously been removed.
Claim 9
Independent Claim
38 words
The method according to any one of claims 1, 4 and 6, wherein the polyester scrap is in the form of a film which includes 0 to 10% by weight of paper, acetate, or vinylidene chloride as impurities.
Claim 10
Independent Claim
25 words
The method according to any one of claims 1, 4 and 6, wherein the polyester scrap is in the form of yarn or textile material.
Claim 11
Independent Claim
22 words
The method according to any one of claims 1, 4 and 6, wherein the polyester scrap is in the form of bottles.
Claim 12
Independent Claim
45 words
A method for liquefying terephthalate polyester scrap, said method comprising the step of dissolving the polyester in a mixture of sulfuric acid and water in a volume ratio of 8.5-13 to 2 to effect depolymerization of the polyester to form terephthalic acid and ethylene glycol.
Claim 13
Independent Claim
45 words
A method for liquefying terephthalate polyester scrap, said method comprising the step of dissolving the polyester in a mixture of sulfuric acid and water in a volume ratio of 8.5-13 to 2 to effect depolymerization of the polyester to form terephthalic acid and ethylene glycol.
References Cited (Backward Citations)
CA523222A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-18 | 1986-04-19 | 1986-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-18 | 1990-04-19 | 1990-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-18 | 1994-04-19 | 1994-10-19 | $7700.00 | Window Closed / Lapsed |