Process for the manufacture of a composite fiber component
Assignee: Airbus Defence and Space GmbH
•
Filing: 1981-01-12
•
Granted: 1982-10-12
•
Expires: 2001-01-12
Abstract
Abstract A method for the manufacture of a composite fiber component having a high rface quality wherein a glass mold having a smooth surface is coated with a separating layer which can be loosened from the surface, and then this layer is coated with a hardenable composite fiber material. This material is hardened and then separated from the mold and the separating layer. Products obtained by the process are also disclosed.
Inventors
- 👤 Wilhelm G. Grimm
- 👤 Rudolf Schindler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 07:32
CPC Classifications
B; B29; B29C; B29C33/00; B29C33/42; B29C33/56; B29C33/60; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/42; B29C70/44; B29C35/00; B29C35/02; B29C35/0227; B29C43/00; B29C43/02; B29C43/10; B29C43/12; B29K; B29K2909/00; B29K2909/08; B29L; B29L2009/00; B32; B32B; B32B38/00; B32B2038/0052; B32B2038/0064; Y; Y10; Y10T; Y10T428/00; Y10T428/30
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
98 words
A process for the manufacture of a composite heat hardenable fiber component having a high surface quality comprising coating the surface of a glass mold, having a smoothly worked surface, uniformly with a thin coating of a separating agent which can be detached from the mold surface, the thickness of the coating being not greater than the maximum surface roughness of the composite fiber component, applying the hardenable composite fiber material onto the coating, hardening the hardenable material and then removing the hardenable component and the coating of the separating agent from the surface of the glass mold.
Claim 2
Dependent Claim
98 words
A process for the manufacture of a composite heat hardenable fiber component having a high surface quality comprising coating the surface of a glass mold, having a smoothly worked surface, uniformly with a thin coating of a separating agent which can be detached from the mold surface, the thickness of the coating being not greater than the maximum surface roughness of the composite fiber component, applying the hardenable composite fiber material onto the coating, hardening the hardenable material and then removing the hardenable component and the coating of the separating agent from the surface of the glass mold.
Claim 3
Dependent Claim
98 words
A process for the manufacture of a composite heat hardenable fiber component having a high surface quality comprising coating the surface of a glass mold, having a smoothly worked surface, uniformly with a thin covering of a separating layer which can be loosened from the mold surface, applying a hardenable composite fiber material in the unhardened state onto the separating layer, hardening the composite fiber material, and then separating the hardened composite fiber component and the thin covering from the mold surface wherein the separating layer is applied onto the surface of the glass mold by cathodic sputtering.
Claim 4
Dependent Claim
98 words
A process for the manufacture of a composite heat hardenable fiber component having a high surface quality comprising coating the surface of a glass mold, having a smoothly worked surface, uniformly with a thin covering of a separating layer which can be loosened from the mold surface, applying a hardenable composite fiber material in the unhardened state onto the separating layer, hardening the composite fiber material, and then separating the hardened composite fiber component and the thin covering from the mold surface wherein the separating layer is applied onto the surface of the glass mold by cathodic sputtering.
Claim 5
Dependent Claim
80 words
A process for the manufacture of a composite fiber component having a high surface quality comprising coating the surface of a glass mold, having a smoothly worked surface, uniformly with a thin covering of a separating layer which can be loosened from the mold surface, applying a hardenable composite fiber material in the unhardened state onto the separating layer, hardening the composite fiber material, and then separating the hardened composite fiber component and the thin covering from the mold surface.
Claim 6
Dependent Claim
80 words
A process for the manufacture of a composite fiber component having a high surface quality comprising coating the surface of a glass mold, having a smoothly worked surface, uniformly with a thin covering of a separating layer which can be loosened from the mold surface, applying a hardenable composite fiber material in the unhardened state onto the separating layer, hardening the composite fiber material, and then separating the hardened composite fiber component and the thin covering from the mold surface.
Claim 7
Dependent Claim
20 words
The process of claim 3 wherein the mold, after separation from the composite fiber material is cleaned with a solvent.
Claim 8
Dependent Claim
21 words
The process of claim 3 wherein the separating layer has a thickness in the range from approximately 200 to 400 A.
Claim 9
Dependent Claim
11 words
A composite fiber component produced by the process of claim 3.
Claim 10
Dependent Claim
11 words
A composite fiber component produced by the process of claim 1.
Claim 11
Dependent Claim
24 words
The process of claim 3 wherein the separating layer has a thickness not greater than the maximum surface roughness of the composite fiber material.
Claim 12
Dependent Claim
29 words
The process of claim 3 wherein any separating layer which adheres to the composite fiber material after separation from the mold is removed therefrom by washing with a solvent.
Claim 13
Dependent Claim
19 words
The process of claim 3 wherein the fibers are arranged in a single direction in the composite fiber material.
Claim 14
Dependent Claim
24 words
The process of claim 3 wherein the composite fiber material is hardened in an autoclave and the surface adjacent the fiber material is evacuated.
Claim 15
Dependent Claim
16 words
The process of claim 11 wherein the pressure in the autoclave is 0.5 to 1.0 bar.
Claim 16
Dependent Claim
29 words
The process of claim 3 wherein a thin layer of a fiber-free hardenable synthetic resin is applied onto the separating layer prior to application of the composite fiber material.
Claim 17
Dependent Claim
21 words
The process of claim 13 wherein the hardenable fiber-free synthetic resin is hardened and the composite fiber material is applied thereto.
Claim 18
Dependent Claim
29 words
The process of claim 13 or 14 wherein the thickness of the fiber-free synthetic resin layer is less than the diameter of the fibers in the composite fiber material.
Claim 19
Dependent Claim
17 words
The process of claim 13 wherein said fiber-free hardenable synthetic resin contains up to about 30% graphite.
Claim 20
Dependent Claim
24 words
The process of claim 13 wherein the thermal coefficient of expansion of the synthetic resin and the composite fiber material are essentially the same.
Claim 21
Dependent Claim
25 words
The process of claim 3 wherein the composite fiber component, after separation, is optically reflecting and has a peak-to-valley height of less than 0.2 μm.
Claim 22
Dependent Claim
23 words
The process of claim 3 wherein the surface of the glass mold has a peak-to-valley height of not greater than about 0.008 μm.
Claim 23
Dependent Claim
21 words
The process of claim 3 wherein the separating layer is applied onto the surface of the glass mold by cathodic sputtering.
Claim 24
Dependent Claim
16 words
The process of claim 3, 18 or 19 wherein the separating layer is a precious metal.
Claim 25
Dependent Claim
28 words
The process of claim 3 wherein the thermal coefficient of expansion of the glass mold is approximately equal to that of the fibers of the composite fiber material.
Claim 26
Dependent Claim
26 words
The process of claim 3 or 22 wherein the mold is a glass ceramic mold and the fibers in the composite fiber material are carbon fibers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-11 | 1986-04-12 | 1986-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-11 | 1990-04-12 | 1990-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-11 | 1994-04-12 | 1994-10-12 | $7700.00 | Window Closed / Lapsed |