Method for forming a boss upon a thermoplastic polymer surface and resulting article
Assignee: Northern Engraving and Manuf Co
•
Filing: 1980-12-24
•
Granted: 1982-10-12
•
Expires: 2000-12-24
Abstract
Abstract An article comprising a thermoplastic polymer having an essentially planar surface provided with a surface pattern defined and encompassed by at least one continuous self-connecting retaining dam; at least a portion of the dam comprising at least one debossed region between at least two essentially parallel raised ridges; a further article comprising the foregoing article having a boss formed from a hardened resin over the surface pattern to a depth at least equal to the height of the highest of the raised ridges; and a method for manufacturing the articles by heating the surface to a temperature above the deformation temperature of the polymer and impressing the surface with a debossing die to form the portion of the article having the debossed region and raised ridges and introducing a liquid resin into the surface pattern followed by solidifying the resin to form the article having the boss.
Inventors
- 👤 Kenneth B. Gilleo
- 👤 Willard H. Kriebich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:31
CPC Classifications
B; B29; B29C; B29C59/00; B29C59/02; B29C59/026; B29C39/00; B29C39/02; B29C39/10; B29C70/00; B29C70/68; B29C70/78; B44; B44C; B44C1/00; B44C1/24; B29L; B29L2031/00; B29L2031/744; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1039; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24628; Y10T428/24736
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
230 words
A method for forming a boss upon an essentially planar thermoplastic polymer surface which comprises: (a) heating the thermoplastic polymer surface to a temperature above the deformation temperature of the thermoplastic polymer and below the decomposition and melt stick temperatures of the thermoplastic polymer; (b) impressing the thermoplastic surface, for from about 0.1 to about 10 seconds with a debossing die having at least one edge in the shape of a first pattern, to form a second pattern area on the surface defined and encompassed by at least one continuous self-connecting retaining dam on the surface, at least a portion of said dam being formed by said impressing by said die, said portion of said dam comprising at least one debossed region between at least two raised ridges having upper edges; (c) introducing into the second pattern area, a liquid resin in a quantity sufficient to fill the second pattern area and insufficient to overflow the continuous dam, the liquid resin being solidifiable at a temperature below the deformation temperature of the thermoplastic polymer, the thermoplastic polymer, having reaction and solubility rates with the liquid resin which are sufficiently slow to prevent significant weakening of said thermoplastic polymer prior to solidification of the liquid resin; and (d) while the upper edge of each such ridge is in an essentially horizontal plane, solidifying the liquid resin to form an elevated boss.
Claim 2
Independent Claim
230 words
A method for forming a boss upon an essentially planar thermoplastic polymer surface which comprises: (a) heating the thermoplastic polymer surface to a temperature above the deformation temperature of the thermoplastic polymer and below the decomposition and melt stick temperatures of the thermoplastic polymer; (b) impressing the thermoplastic surface, for from about 0.1 to about 10 seconds with a debossing die having at least one edge in the shape of a first pattern, to form a second pattern area on the surface defined and encompassed by at least one continuous self-connecting retaining dam on the surface, at least a portion of said dam being formed by said impressing by said die, said portion of said dam comprising at least one debossed region between at least two raised ridges having upper edges; (c) introducing into the second pattern area, a liquid resin in a quantity sufficient to fill the second pattern area and insufficient to overflow the continuous dam, the liquid resin being solidifiable at a temperature below the deformation temperature of the thermoplastic polymer, the thermoplastic polymer, having reaction and solubility rates with the liquid resin which are sufficiently slow to prevent significant weakening of said thermoplastic polymer prior to solidification of the liquid resin; and (d) while the upper edge of each such ridge is in an essentially horizontal plane, solidifying the liquid resin to form an elevated boss.
Claim 3
Independent Claim
212 words
A method for forming a boss upon an essentially planar non-porous thermoplastic polymer surface which comprises: (a) heating the thermoplastic polymer surface to a temperature above the deformation temperature of the thermoplastic polymer and below the decomposition and melt stick temperatures of the thermoplastic polymer; (b) impressing the thermoplastic surface, for from about 0.1 to about 10 seconds with a debossing die having at least one continuous edge defining and encompassing a first pattern area, to form a second pattern area on the surface defined and encompassed by at least one continuous self-connecting retaining dam on the surface, the dam comprising a continuous debossed region between two continuous raised ridges having upper edges; (c) introducing into the second pattern area, a liquid resin in a quantity sufficient to fill the second pattern area and insufficient to overflow the continuous dam, the liquid resin being solidifiable at a temperature below the deformation temperature of the thermoplastic polymer, the thermoplastic polymer, having reaction and solubility rates with the liquid resin which are sufficiently slow to prevent significant weakening of said thermoplastic polymer prior to solidification of the liquid resin; and (d) while the upper edge of each such ridge is in an essentially horizontal plane, solidifying the liquid resin to form an elevated boss.
Claim 4
Independent Claim
212 words
A method for forming a boss upon an essentially planar non-porous thermoplastic polymer surface which comprises: (a) heating the thermoplastic polymer surface to a temperature above the deformation temperature of the thermoplastic polymer and below the decomposition and melt stick temperatures of the thermoplastic polymer; (b) impressing the thermoplastic surface, for from about 0.1 to about 10 seconds with a debossing die having at least one continuous edge defining and encompassing a first pattern area, to form a second pattern area on the surface defined and encompassed by at least one continuous self-connecting retaining dam on the surface, the dam comprising a continuous debossed region between two continuous raised ridges having upper edges; (c) introducing into the second pattern area, a liquid resin in a quantity sufficient to fill the second pattern area and insufficient to overflow the continuous dam, the liquid resin being solidifiable at a temperature below the deformation temperature of the thermoplastic polymer, the thermoplastic polymer, having reaction and solubility rates with the liquid resin which are sufficiently slow to prevent significant weakening of said thermoplastic polymer prior to solidification of the liquid resin; and (d) while the upper edge of each such ridge is in an essentially horizontal plane, solidifying the liquid resin to form an elevated boss.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein the thermoplastic polymer is a linear polycarbonate, modified cellulose, polyester, acrylic, polyamide, thermosetting prepolymer or polyvinyl polymer.
Claim 6
Dependent Claim
63 words
The method of claim 3 wherein the liquid resin is selected from the group consisting of catalyzed urethanes, catalyzed epoxies, radiation curable polymers, heat curable polymers which are cured at a temperature below the deformation temperature of the thermoplastic polymer of the surface, and thermoplastic polymers which solidify at a temperature below the deformation temperature of the thermoplastic polymer of the polymer surface.
Claim 7
Dependent Claim
23 words
The method of claim 2 wherein the thermoplastic polymer is a linear polycarbonate, modified cellulose, polyester, acrylic, polyamide, thermosetting prepolymer or polyvinyl polymer.
Claim 8
Dependent Claim
63 words
The method of claim 5 wherein the liquid resin is selected from the group consisting of catalyzed urethanes, catalyzed epoxies, radiation curable polymers, heat curable polymers which are cured at a temperature below the deformation temperature of the thermoplastic polymer of the surface, and thermoplastic polymers which solidify at a temperature below the deformation temperature of the thermoplastic polymer of the polymer surface.
Claim 9
Dependent Claim
21 words
The method of claim 2 wherein the debossing die has an edge thickness of from about 0.025 to about 0.4 mm.
Claim 10
Dependent Claim
37 words
The method of claim 2 wherein the heating temperature is between about 3° C. above the deformation temperature of the thermoplastic polymer and about 3° C. below the decomposition and melt stick temperatures of the thermoplastic polymer.
Claim 11
Dependent Claim
13 words
The method of claim 1 wherein the heating occurs simultaneously with the impressing.
Claim 12
Dependent Claim
13 words
The method of claim 2 wherein the heating occurs simultaneously with the debossing.
Claim 13
Dependent Claim
25 words
The method of claim 10 wherein the heating and impressing is accomplished with a debossing die heated to from about 175° to about 250° C.
Claim 14
Dependent Claim
12 words
The method of claim 11 wherein the thermoplastic surface is a polycarbonate.
Claim 15
Dependent Claim
21 words
The method of claim 12 wherein the liquid resin is a radiation curable prepolymer containing radiation linkable polythiol and polyene groups.
Claim 16
Dependent Claim
30 words
The method of claim 2 wherein said liquid resin is sufficiently soluble or reactive with said thermoplastic surface to create good adhesion between the solidified resin and the thermoplastic surface.
Claim 17
Dependent Claim
25 words
The method of claim 2 wherein said thermoplastic surface is coated with an adhesive primer to increase adhesion between said surface and the solidified resin.
Claim 18
Dependent Claim
33 words
The method of claim 1 wherein said thermoplastic surface is coated with a thermoplastic polymer primer which forms a non-porous surface which is insoluble in and is not reactive with the liquid resin.
Claim 19
Dependent Claim
26 words
The method of claim 2 wherein one of said ridges is from about 0.3 to about 1 times the height of the other of said ridges.
Claim 20
Dependent Claim
26 words
The method of claim 2 wherein one of said ridges is from about 0.05 to about 0.3 times the height of the other of said ridges.
Claim 21
Dependent Claim
37 words
The method of claim 2 wherein the minimum quantity of liquid resin sufficient to fill the second pattern area is a volume calculated by multiplying the height of the highest ridge times the area of the pattern.
References Cited (Backward Citations)
US2306256A
Cited
US2370028A
Cited
US2704211A
Cited
US3217617A
Cited
US3963847A
Cited
US3953910A
Cited
US4307527A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-11 | 1986-04-12 | 1986-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-11 | 1990-04-12 | 1990-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-11 | 1994-04-12 | 1994-10-12 | $7700.00 | Window Closed / Lapsed |