Abstract A process for controlling the dihydride and monohydride bond densities in hydrogenated amorphous silicon produced by reactive rf sputtering of an amorphous silicon target. There is provided a chamber with an amorphous silicon target and a substrate therein with the substrate and the target positioned such that when rf power is applied to the target the substrate is in contact with the sputtering plasma produced thereby. Hydrogen and argon are fed to the chamber and the pressure is reduced in the chamber to a value sufficient to maintain a sputtering plasma therein, and then rf power is applied to the silicon target to provide a power density in the range of from about 7 watts per square inch to about 22 watts per square inch to sputter an amorphous silicon hydride onto the substrate, the dihydride bond density decreasing with an increase in the rf power density. Substantially pure monohydride films may be produced.
A process for producing substantially pure amorphous silicon monohydride by reactive rf sputtering of a silicon target, comprising providing a chamber with an amorphous silicon target and a substrate therein, positioning said substrate and said target such that the adjacent edges of the substrate and the target are within about 2 cm, providing a partial pressure of hydrogen of at least 10 -3 torr to said chamber, providing argon to said chamber, reducing the pressure in said chamber to a value sufficient to maintain a sputtering plasma therein, and applying rf power to the silicon target to provide a power density of not less than about 15 watts per square inch to sputter substantially pure amorphous silicon monohydride onto said substrate while maintaining said partial pressure of hydrogen.
Claim 2
Dependent Claim
128 words
A process for producing substantially pure amorphous silicon monohydride by reactive rf sputtering of a silicon target, comprising providing a chamber with an amorphous silicon target and a substrate therein, positioning said substrate and said target such that the adjacent edges of the substrate and the target are within about 2 cm, providing a partial pressure of hydrogen of at least 10 -3 torr to said chamber, providing argon to said chamber, reducing the pressure in said chamber to a value sufficient to maintain a sputtering plasma therein, and applying rf power to the silicon target to provide a power density of not less than about 15 watts per square inch to sputter substantially pure amorphous silicon monohydride onto said substrate while maintaining said partial pressure of hydrogen.
Claim 3
Dependent Claim
19 words
The process of claim 1, wherein the adjacent edges of said substrate and said target are within 1.5 cm.
Claim 4
Dependent Claim
30 words
The process of claim 1, wherein the partial pressure of hydrogen in said chamber is maintained within the range of from about 10 -2 Torr to about 10 -3 Torr.
Claim 5
Dependent Claim
21 words
The process of claim 1, wherein the pressure in said chamber during sputtering is not less than about 2×10 -2 Torr.
Claim 6
Dependent Claim
29 words
The process of claim 1, wherein the pressure within said chamber during sputtering is maintained within the range of from about 2×10 -2 Torr to about 6×10 -2 Torr.
Claim 7
Dependent Claim
33 words
The process of claim 1, wherein said power density provided to said silicon target is in the range of from about 15 watts per square inch to about 20 watts per square inch.