Process for the rapid sintering of ceramic components and a kiln for carrying out said process
Assignee: Thales SA
•
Filing: 1980-08-26
•
Granted: 1982-09-21
•
Expires: 2000-08-26
Abstract
Abstract A process for rapidly sintering ceramic components, in particular of the type utilized in electronics (ferrites), which reduces the sintering time by a factor of from ten to one hundred, reducing the volume of the kiln and resulting in a considerable saving in electric power. In this process the unbaked components previously shaped by pressing with a binder are sintered without carrying out the prior heat treatment of elimination of the binder. The sintering is made according an accurate curve of temperature as concerns the slopes of the rising and descending parts of the curve. The maximum of the curve exceeds by from 100° C. to 300° C. the normal temperature of sintering in the conventional method. The kiln, which is of the passage type with a conveyer belt sliding on rods of alumina, has six heating zones regulated by a thermocouple and a feedback loop pertaining to each zone so as to achieve a heating profile with a high accuracy.
Inventors
- 👤 Antoinette Morell
- 👤 Antonio Hermosin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:45
CPC Classifications
F; F27; F27B; F27B9/00; F27B9/14; F27B9/20; F27B9/24; F27B9/243; C; C04; C04B; C04B35/00; C04B35/01; C04B35/26; C04B35/265; C04B35/2658; C04B35/622; C04B35/64; Y; Y02; Y02P; Y02P40/00; Y02P40/60
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
145 words
A process for rapidly sintering ceramic components comprising oxides of iron, manganese and zinc mixed with a binder, wherein the unbaked components of the ceramic to be sintered, in the shape of half-cores for telecommunication pots, have a diameter in the range of 9-14 mm and a height in the range of 2.5-4 mm, in the state of unbaked component is subjected to a heat treatment in a nitrogen atmosphere wherein said treatment has a total duration of 16 to 33 minutes, during which treatment the curve of the temperature as a function of the time has a first part rising with a positive slope between 50° C./min. and 500° C./min., then a second part which rises then descends in passing through a maximum of 1300° C., and a third part descending with a negative slope of absolute value between 30° C./min. and 300° C./min.
Claim 2
Dependent Claim
145 words
A process for rapidly sintering ceramic components comprising oxides of iron, manganese and zinc mixed with a binder, wherein the unbaked components of the ceramic to be sintered, in the shape of half-cores for telecommunication pots, have a diameter in the range of 9-14 mm and a height in the range of 2.5-4 mm, in the state of unbaked component is subjected to a heat treatment in a nitrogen atmosphere wherein said treatment has a total duration of 16 to 33 minutes, during which treatment the curve of the temperature as a function of the time has a first part rising with a positive slope between 50° C./min. and 500° C./min., then a second part which rises then descends in passing through a maximum of 1300° C., and a third part descending with a negative slope of absolute value between 30° C./min. and 300° C./min.
Claim 3
Dependent Claim
137 words
A process for rapidly sintering ceramic components comprising oxides of iron, nickel and zinc mixed with a binder, wherein the unbaked components of the ceramic to be sintered, in the shape of half-cores for telecommunication pots, have a diameter in the range of 9-14 mm and a height in the range of 2.5-4 mm, in the state of unbaked component is subjected to a heat treatment having a total duration of about 471/2 minutes, during which treatment the curve of the temperature as a function of the time has a first part rising with a positive slope between 50° C./min. and 500° C./min., then a second part which rises then descends in passing through a maximum of 1380° C., and a third part descending with a negative slope of absolute value between 30° C./min. and 300° C./min.
Claim 4
Dependent Claim
137 words
A process for rapidly sintering ceramic components comprising oxides of iron, nickel and zinc mixed with a binder, wherein the unbaked components of the ceramic to be sintered, in the shape of half-cores for telecommunication pots, have a diameter in the range of 9-14 mm and a height in the range of 2.5-4 mm, in the state of unbaked component is subjected to a heat treatment having a total duration of about 471/2 minutes, during which treatment the curve of the temperature as a function of the time has a first part rising with a positive slope between 50° C./min. and 500° C./min., then a second part which rises then descends in passing through a maximum of 1380° C., and a third part descending with a negative slope of absolute value between 30° C./min. and 300° C./min.
References Cited (Backward Citations)
US3036009A
Cited
GB1173697A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-09-20 | 1986-03-22 | 1986-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-09-20 | 1990-03-22 | 1990-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-09-20 | 1994-03-22 | 1994-09-21 | $7700.00 | Window Closed / Lapsed |