Method of forging spinel domes
Assignee: Raytheon Co
•
Filing: 1980-05-09
•
Granted: 1982-08-31
•
Expires: 2000-05-09
Abstract
Abstract A method of forging spinel into complex shapes in which a spinel plate is placed in a mold while the spinel plate is heated, in an atmosphere of helium, to a temperature below its melting point and above its solid two phases transition point that allows plastic deformation to take place. Forging stresses well above the yield point of the spinel are applied to the plate by the mold to reduce the forging time.
Inventors
- 👤 Edward A. Maguire
- 👤 Richard L. Gentilman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 03:30
CPC Classifications
C; C30; C30B; C30B33/00; C30B29/00; C30B29/10; C30B29/16; C30B29/22; C30B29/26
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
105 words
A method of comprising the steps of: placing a plate of spinel between two portion of a mold, said two portions having complementary shapes for forming a cavity of a predetermined complex shape; the composition of said spinel comprising a ratio of Al 2 O 3 :MgO in the range of greater than 1:1 to 3.5:1; heating said spinel to a temperature in the range below its melting point and above its single phase transition point; and applying a pressure to said mold for producing compound stresses in said spinel plate to plastically deform said spinel plate to the complex shape of the mold cavity.
Claim 2
Independent Claim
105 words
A method of comprising the steps of: placing a plate of spinel between two portion of a mold, said two portions having complementary shapes for forming a cavity of a predetermined complex shape; the composition of said spinel comprising a ratio of Al 2 O 3 :MgO in the range of greater than 1:1 to 3.5:1; heating said spinel to a temperature in the range below its melting point and above its single phase transition point; and applying a pressure to said mold for producing compound stresses in said spinel plate to plastically deform said spinel plate to the complex shape of the mold cavity.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said temperature is in the range of 1750° to 1850° C.
Claim 4
Independent Claim
168 words
A method comprising the steps of: forming an alumina-rich plate having a ratio of Al 2 O 3 :MgO in the range of greater than 1:1 to 3.5:1; placing said spinel plate over a lower portion of a mold having a cavity of a predetermined shape; placing a top portion of said mold over said spinel plate in mating relationship with said lower portion and preventing said top portion from applying significant pressure; heating said spinel plate to a forging temperature below its melting point at which plastic deformation of said spinel plate can take place; said forging temperature having a value higher than the phase transition point of said spinel for substantially preventing a change in said spinel from a single phase to a two-phase state; applying a pressure to said mold exceeding the yield stress in at least one portion of said spinel plate but not reaching the fracturing point of spinel; and said pressure and said mold shape producing compound stresses in said spinel plate.
Claim 5
Independent Claim
168 words
A method comprising the steps of: forming an alumina-rich plate having a ratio of Al 2 O 3 :MgO in the range of greater than 1:1 to 3.5:1; placing said spinel plate over a lower portion of a mold having a cavity of a predetermined shape; placing a top portion of said mold over said spinel plate in mating relationship with said lower portion and preventing said top portion from applying significant pressure; heating said spinel plate to a forging temperature below its melting point at which plastic deformation of said spinel plate can take place; said forging temperature having a value higher than the phase transition point of said spinel for substantially preventing a change in said spinel from a single phase to a two-phase state; applying a pressure to said mold exceeding the yield stress in at least one portion of said spinel plate but not reaching the fracturing point of spinel; and said pressure and said mold shape producing compound stresses in said spinel plate.
Claim 6
Dependent Claim
61 words
The method of claim 3 wherein forming said alumina-rich spinel plate further comprises: combining and dry blending predetermined amounts of aluminum oxide and magnesium oxide until thoroughly mixed; compressing said mixture to form a starting charge; heating said starting charge in a mold of predetermined shape until thoroughly molten; and creating a temperature gradient across the mold for providing directional cooling.
Claim 7
Dependent Claim
18 words
The method of claim 3 wherein said forging temperature is in the range of 1750° to 1850° C.
Claim 8
Dependent Claim
24 words
The method of claim 3 wherein the value of said forging temperature is a function of said Al 2 O 3 to MgO ratio.
Claim 9
Independent Claim
204 words
The method of hot forging a plate of alumina-rich spinel, having a ratio of Al 2 O 3 :MgO in the range of slightly over 1:1 to 3.5:1, into a complex shape comprising the steps of: placing said plate over a first portion of a mold, said first portion having a cavity therein substantially defining a first complex surface; placing a second portion of said mold over said spinel plate without causing said second portion to exert significant pressure on said plate, said second mold portion having a second complex surface and being capable of mating with said first mold portion; heating said spinel plate to a forging temperature below its melting point and within the temperature range in which said spinel can exist in its solid angle phase and at which plastic deformation can readily take place; and applying pressure to said mold for producing compound stresses in portions of said spinel plate that cause said spinel plate to conform to the first and second complex surfaces of said mold, said forging temperature and stresses having values producing a minimum temperature in said spinel plate higher than the transition point of said spinel for substantially keeping said spinel in its single phase state.
Claim 10
Independent Claim
204 words
The method of hot forging a plate of alumina-rich spinel, having a ratio of Al 2 O 3 :MgO in the range of slightly over 1:1 to 3.5:1, into a complex shape comprising the steps of: placing said plate over a first portion of a mold, said first portion having a cavity therein substantially defining a first complex surface; placing a second portion of said mold over said spinel plate without causing said second portion to exert significant pressure on said plate, said second mold portion having a second complex surface and being capable of mating with said first mold portion; heating said spinel plate to a forging temperature below its melting point and within the temperature range in which said spinel can exist in its solid angle phase and at which plastic deformation can readily take place; and applying pressure to said mold for producing compound stresses in portions of said spinel plate that cause said spinel plate to conform to the first and second complex surfaces of said mold, said forging temperature and stresses having values producing a minimum temperature in said spinel plate higher than the transition point of said spinel for substantially keeping said spinel in its single phase state.
Claim 11
Dependent Claim
18 words
The method of claim 7 wherein said forging temperature is in the range of 1750° to 1850° C.
Claim 12
Dependent Claim
19 words
The method of claim 8 wherein the forging temperature used is a function of said ratio in said spinel.
Claim 13
Dependent Claim
18 words
The method of claim 4 wherein said stresses in said spinel are bending stresses and include tensile stresses.
Claim 14
Dependent Claim
28 words
The method of claim 10 wherein said mold pressure produces maximum stresses in said spinel exceeding the yield stress but not exceeding the fracture stress of said spinel.
Claim 15
Dependent Claim
17 words
The method of claim 11 wherein said stresses are in the range of 7.5 to 15 ksi.
Claim 16
Dependent Claim
19 words
The method of claim 1 wherein: said temperature is selected as a function of the composition of said spinel.
Claim 17
Dependent Claim
12 words
The method of claim 1 wherein: said spinel plate comprises polycrystalline spinel.
Claim 18
Dependent Claim
13 words
The method of claim 1 wherein: said spinel plate comprises single crystal spinel.
References Cited (Backward Citations)
US2219423A
Cited
US3431326A
Cited
US3026210A
Cited
US3933970A
Cited
US3875277A
Cited
US3864808A
Cited
US4171400A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |