Insulating engine exhaust port liner
Assignee: Motors Liquidation Co
•
Filing: 1980-05-12
•
Granted: 1982-08-31
•
Expires: 2000-05-12
Abstract
Abstract An insulating liner for use in an exhaust port of an internal combustion engine or the like consisting, in a preferred embodiment, of a formed thin wall tubular body of rigidized fibrous ceramic such as fibrous alumina-silica material (Fiberfrax) with an abrasion resistant ceramic coating fused onto the inner gas-exposed surface of the body. The coating comprises a mixture of fused silica cement and fine glass frit sintered in place on the body inner surface at a temperature below that which would damage the thin walls of the body.
Inventors
- 👤 Hal H. Rice
- 👤 Gary A. Kruger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 03:58
CPC Classifications
F; F02; F02B; F02B77/00; F02B77/02; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/1317
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
104 words
An insulating exhaust port liner for internal combustion engines and the like, said liner comprising a formed thin wall body of rigidized fibrous ceramic of relatively low mass and high insulating value, said body being shaped to define at least part of the inner wall of a high temperature exhaust gas passage, and an abrasion resistant ceramic coating fused onto at least the inner gas-exposed surface of said body, said coating comprising a mixture of fused silica cement and fine glass frit sintered in place on the body inner surface at a temperature below that which will damage the thin walls of the body.
Claim 2
Dependent Claim
104 words
An insulating exhaust port liner for internal combustion engines and the like, said liner comprising a formed thin wall body of rigidized fibrous ceramic of relatively low mass and high insulating value, said body being shaped to define at least part of the inner wall of a high temperature exhaust gas passage, and an abrasion resistant ceramic coating fused onto at least the inner gas-exposed surface of said body, said coating comprising a mixture of fused silica cement and fine glass frit sintered in place on the body inner surface at a temperature below that which will damage the thin walls of the body.
Claim 3
Dependent Claim
105 words
An insulating exhaust port liner for internal combustion engines and the like, said liner comprising a formed thin wall body of rigidized fibrous alumina-silica ceramic of relatively low mass and high insulating value, said body being shaped to define at least part of the inner wall of a high temperature exhaust gas passage, and an abrasion reistant ceramic coating fused onto at least the inner gas-exposed surface of said body, said coating comprising a mixture of fused silica cement and fine glass frit sintered in place on the body inner surface at a temperature below that which will damage the thin walls of the body.
Claim 4
Dependent Claim
105 words
An insulating exhaust port liner for internal combustion engines and the like, said liner comprising a formed thin wall body of rigidized fibrous alumina-silica ceramic of relatively low mass and high insulating value, said body being shaped to define at least part of the inner wall of a high temperature exhaust gas passage, and an abrasion reistant ceramic coating fused onto at least the inner gas-exposed surface of said body, said coating comprising a mixture of fused silica cement and fine glass frit sintered in place on the body inner surface at a temperature below that which will damage the thin walls of the body.
Claim 5
Dependent Claim
54 words
An exhaust port liner according to claim 2 wherein the walls of the formed alumina-silica body have a thickness on the order of 3.8 mm and the abrasion resistant silica glass coating thereon is a mixture in approximate proportions by weight of 56 parts fused silica cement and 50 parts fine glass frit powder.
References Cited (Backward Citations)
US2703486A
Cited
US3488723A
Cited
US3718497A
Cited
US3709772A
Cited
US3771967A
Cited
US3798903A
Cited
US3919755A
Cited
US3957519A
Cited
US4056399A
Cited
US4195478A
Cited
US4254621A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |