Alkali resistant glass fibres for cement reinforcement
Assignee: Pilkington Group Ltd
•
Filing: 1981-02-26
•
Granted: 1982-08-17
•
Expires: 2001-02-26
Abstract
Abstract Alkali-resistant glass fibres for use as reinforcement in cementitious products are formed from a composition comprising, in weight percentages: ______________________________________ SiO 2 55 to 75% R 2 O 11 to 23% ZrO 2 6 to 22% Cr 2 O 3 0.1 to 1% Al 2 O 3 0.1 to 7% Rare earth oxides + TiO 2 0.5 to 16% ______________________________________ where R 2 O is any one or more of Na 2 O, K 2 O or Li 2 O, the content of TiO 2 does not exceed 10%, and the total of the components recited above amounts to at least 88% by weight of the glass, the glass having been melted under non-oxidizing conditions such that all or a substantial proportion of the chromium in the glass is in the trivalent state. Cementitious products incorporating such fibres, e.g. in a proportion of 3 to 6 weight %, can be made using a Magnani-type asbestos cement machine or by a "spray-up" method.
Inventors
- 👤 Kenneth M. Fyles
- 👤 Peter Shorrock
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:31
CPC Classifications
D; D03; D03D; D03D37/00; C; C04; C04B; C04B14/00; C04B14/38; C04B14/42; C03; C03C; C03C13/00; C03C13/001; C03C13/002
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
124 words
Alkali-resistant glass fibres for use as reinforcement in cementitious products, formed from a composition comprising, in weight percentages: ______________________________________
SiO.sub.2 55 to 75%
R.sub.2 O 11 to 23%
ZrO.sub.2 6 to 22%
Cr.sub.2 O.sub.3 0.1 to 1%
Al.sub.2 O.sub.3 0.1 to 7%
Rare earth oxides + TiO.sub.2
0.5 to 16%
______________________________________ where R 2 O is any one or more of Na 2 O, K 2 O or Li 2 O, the content of TiO 2 does not exceed 10%, and the total of the components recited above amounts to at least 88% by weight of the glass, the glass having been melted under non-oxidising conditions such that all or a substantial proportion of the chromium in the glass is in the trivalent state.
Claim 2
Dependent Claim
124 words
Alkali-resistant glass fibres for use as reinforcement in cementitious products, formed from a composition comprising, in weight percentages: ______________________________________
SiO.sub.2 55 to 75%
R.sub.2 O 11 to 23%
ZrO.sub.2 6 to 22%
Cr.sub.2 O.sub.3 0.1 to 1%
Al.sub.2 O.sub.3 0.1 to 7%
Rare earth oxides + TiO.sub.2
0.5 to 16%
______________________________________ where R 2 O is any one or more of Na 2 O, K 2 O or Li 2 O, the content of TiO 2 does not exceed 10%, and the total of the components recited above amounts to at least 88% by weight of the glass, the glass having been melted under non-oxidising conditions such that all or a substantial proportion of the chromium in the glass is in the trivalent state.
Claim 3
Dependent Claim
36 words
Glass fibres according to claim 1 wherein the composition further comprises R'O up to 9% by weight, where R'O is any one or more of MgO, CaO, SrO, BaO, ZnO, FeO, MnO, CoO, NiO and CuO.
Claim 4
Dependent Claim
23 words
Glass fibres according to claim 1 wherein the content of Al 2 O 3 does not exceed 5% when ZrO 2 exceeds 13%.
Claim 5
Dependent Claim
20 words
Glass fibres according to claim 1 wherein the composition further comprises B 2 O 3 up to 5% by weight.
Claim 6
Dependent Claim
33 words
Glass fibres according to claim 1 wherein the composition further comprises PbO up to 2% by weight the glass having been melted under conditions which avoid formation of lead metal in the glass.
Claim 7
Dependent Claim
18 words
Glass fibres according to claim 1 wherein the composition further comprises ThO 2 up to 4% by weight.
Claim 8
Dependent Claim
17 words
Glass fibres according to claim 1 wherein the composition further comprises F up to 1% by weight.
Claim 9
Dependent Claim
38 words
Glass fibres according to claim 1 wherein the composition further comprises any one of V 2 O 5 , Ta 2 O 5 , MoO 3 or HfO 2 in an amount of up to 2% by weight.
Claim 10
Dependent Claim
17 words
Glass fibres according to claim 1 wherein the content of rare earth oxides does not exceed 10%.
Claim 11
Dependent Claim
25 words
Glass fibres according to claim 1 wherein the content of rare earth oxides exceeds 2.8% and the content of TiO 2 does not exceed 5%.
Claim 12
Dependent Claim
37 words
Glass fibres according to claim 1 wherein the amounts of the individual R 2 O components are within the ranges: ______________________________________
Na.sub.2 O 6 to 20%
K.sub.2 O 0 to 10%
Li.sub.2 O 0 to 3%
______________________________________
Claim 13
Dependent Claim
19 words
Glass fibres according to claim 1 wherein the total content of R 2 O is from 14 to 17%.
Claim 14
Dependent Claim
17 words
Glass fibres according to claim 1 wherein the content of SiO 2 is from 57 to 69%.
Claim 15
Dependent Claim
10 words
Cementitious products reinforced with glass fibres according to claim 1.
Claim 16
Dependent Claim
21 words
Cementitious products according to claim 14, comprising from 3 to 6 weight % of the glass fibres in a cementitious matrix.
References Cited (Backward Citations)
US3060041A
Cited
US3861926A
Cited
US3840379A
Cited
USRE29388E
Cited
US4090882A
Cited
US4062689A
Cited
US4008094A
Cited
US4067744A
Cited
US4140533A
Cited
JPS5499117A
Cited
US4243421A
Cited
EP0014160A1
Cited
GB2046726A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-16 | 1986-02-15 | 1986-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-16 | 1990-02-15 | 1990-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-16 | 1994-02-15 | 1994-08-17 | $7700.00 | Window Closed / Lapsed |