Method for characterizing the oxygen contents of Czochralski grown silicon rods
Assignee: International Business Machines Corp
•
Filing: 1980-06-09
•
Granted: 1982-08-17
•
Expires: 2000-06-09
Abstract
Abstract The oxygen content of Czochralski grown silicon rods is characterized by annealing portions of the rods at selected times and temperatures and measuring the resistivity shift which is then related to the oxygen content of that portion of the rod. The rod can be selected for use in unipolar or bipolar device manufacture prior to cutting the rod into wafers.
Inventors
- 👤 Victor Cazarra
- 👤 Andre Schwab
- 👤 Patrick Zunino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:29
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/02; C30B29/06; C30B33/00; G; G01; G01N; G01N27/00; G01N27/02; G01N27/04; G01N27/041; H; H10; H10D; H10D62/00; H10D62/80; H10D62/83; H10D62/834; H10P; H10P36/00; H10P36/03; H10P36/20; H10P95/00; H10P95/40; H10P95/402; Y; Y10; Y10S; Y10S148/00; Y10S148/024
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
139 words
A method for characterizing the oxygen content of a Czochralski grown silicon rod which is to be cut into wafers, comprising the following steps: (A) stabilizing the rod by heating; (B) cutting a first portion of the rod close to a first end of the rod and measuring its resistivity; (C) annealing said portion in a neutral atmosphere at a temperature in the range of approximately 600° to 900° C. for a period of time sufficient to generate donors; and (D) cleaning said portion and measuring the resistivity increment to characterize the oxygen concentration from the resistivity increment. wherein said first end is the rod head and, if the resistivity increment is lower than the critical value corresponding to a significant donor generation, the remaining portion of the rod is selected to be used on bipolar device production lines.
Claim 2
Independent Claim
139 words
A method for characterizing the oxygen content of a Czochralski grown silicon rod which is to be cut into wafers, comprising the following steps: (A) stabilizing the rod by heating; (B) cutting a first portion of the rod close to a first end of the rod and measuring its resistivity; (C) annealing said portion in a neutral atmosphere at a temperature in the range of approximately 600° to 900° C. for a period of time sufficient to generate donors; and (D) cleaning said portion and measuring the resistivity increment to characterize the oxygen concentration from the resistivity increment. wherein said first end is the rod head and, if the resistivity increment is lower than the critical value corresponding to a significant donor generation, the remaining portion of the rod is selected to be used on bipolar device production lines.
Claim 3
Dependent Claim
28 words
The method according to claim 1 in which the temperature range is from 650° to 850° C. and the annealing duration range is from 1 to 6 hours.
Claim 4
Dependent Claim
48 words
The method according to claim 1 where if the resistivity increment is higher than this critical value, steps A to D are repeated with a new portion of the remaining portion of the rod approximately adjacent to the first portion and farther from the head of the rod.
Claim 5
Dependent Claim
33 words
The method according to claim 1 wherein for selecting the rods with an oxygen concentration lower than 36 ppmA, the annealing temperature is about 825° C. and the annealing duration about 2 hours.
Claim 6
Dependent Claim
49 words
The method according to claim 1 in which said first end is the tail of the rod and if the resistivity increment exceeds the critical value which corresponds to a significant donor generation, the remaining portion, of the rod is selected to be used on unipolar device production lines.
Claim 7
Dependent Claim
41 words
The method according to claim 5 where if the resistivity increment is lower than this critical value, steps A to D are repeated with another portion of the rod approximately adjacent to the first portion and farther from the rod tail.
Claim 8
Dependent Claim
33 words
The method according to claim 5 wherein characterized for selecting the rods with an oxygen concentration exceeding 30 ppmA, the annealing temperature is about 750° C. and the annealing duration about 6 hours.
Claim 9
Dependent Claim
21 words
The method according to claim 1, characterized in that the rod is stabilized at 600° C. for 1 to 3 hours.
Claim 10
Dependent Claim
41 words
The method according to claim 1 wherein the neutral atmosphere is nitrogen and in the cleaning step includes the removal of the thin layer of surface oxide by rinsing in an acid bath of a mixture of HNO 3 and HF.
Claim 11
Dependent Claim
22 words
The method according to claim 1 wherein significant donor generation corresponds to the generation of 10 14 donors per cm 3 .
Claim 12
Dependent Claim
30 words
The method according to claim 10 wherein a significant donor generation corresponds to a resistivity increment equal to 3 ohms for a P wafer with a resistivity of 10 ohms-cm.
Claim 13
Dependent Claim
15 words
The method according to claim 1 wherein the first portion is about 1 cm thick.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-16 | 1986-02-15 | 1986-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-16 | 1990-02-15 | 1990-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-16 | 1994-02-15 | 1994-08-17 | $7700.00 | Window Closed / Lapsed |