US4344476A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Supercool method for producing single crystal mercury cadmium telluride
Assignee: Raytheon Co
•
Filing: 1980-12-08
•
Granted: 1982-08-17
•
Expires: 2000-12-08
Abstract
Abstract A process for producing single crystal Hg 1-x Cd x Te is disclosed. An ingot of Hg 1-x cd x Te is prepared from a stoichiometric mixture of mercury, cadmium and tellurium by the supercooling of a heated mixture thereof from a point above liquidus to a point, a predetermined function of x, below liquidus. The ingot is then quenched in ambient air, producing a large amount of crystallites with small grain boundaries. The subsequent application of heat to the ingot yields a relatively large amount of single crystal material.
Inventors
- 👤 Edward Y. Sutcliffe
- 👤 Roger A. Cole
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:56
CPC Classifications
C; C01; C01B; C01B19/00; C01B19/007; C01P; C01P2006/00; C01P2006/32; C01P2006/33
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
224 words
A process for producing single crystal Hg 1-x Cd x Te comprising the steps of: (a) producing an ingot of Hg 1-x Cd x Te having a large number of crystallites with small grain boundaries by the steps of: (1) adding predetermined amounts of mercury, cadmium and tellurium to a container to produce a stoichiometric mixture thereof of cadmium telluride molefraction x, (2) heating said mixture to a predetermined temperature above liquidus, (3) rocking said container at the same time to produce a homogeneous mixture of Hg 1-x Cd x Te, (4) discontinuing the application of heat to said container, (5) terminating the rocking at +45° with respect to the vertical when the temperature of the mixture has dropped to about 8° C. above liquidus, (6) supercooling said mixture by maintaining said container at the vertical until the temperature of said mixture drops an amount below liquidus which is a predetermined function of x, and (7) quenching said mixture by exposing said container to ambient air temperature by rapidly withdrawing from the furnace so that there is produced an ingot of Hg 1-x Cd x Te having a large number of crystallites with small grain boundaries; and (b) applying heat to said ingot so that a solid state recrystallization process yielding a large amount of single crystal Hg 1-x Cd x Te is achieved.
Claim 2
Dependent Claim
224 words
A process for producing single crystal Hg 1-x Cd x Te comprising the steps of: (a) producing an ingot of Hg 1-x Cd x Te having a large number of crystallites with small grain boundaries by the steps of: (1) adding predetermined amounts of mercury, cadmium and tellurium to a container to produce a stoichiometric mixture thereof of cadmium telluride molefraction x, (2) heating said mixture to a predetermined temperature above liquidus, (3) rocking said container at the same time to produce a homogeneous mixture of Hg 1-x Cd x Te, (4) discontinuing the application of heat to said container, (5) terminating the rocking at +45° with respect to the vertical when the temperature of the mixture has dropped to about 8° C. above liquidus, (6) supercooling said mixture by maintaining said container at the vertical until the temperature of said mixture drops an amount below liquidus which is a predetermined function of x, and (7) quenching said mixture by exposing said container to ambient air temperature by rapidly withdrawing from the furnace so that there is produced an ingot of Hg 1-x Cd x Te having a large number of crystallites with small grain boundaries; and (b) applying heat to said ingot so that a solid state recrystallization process yielding a large amount of single crystal Hg 1-x Cd x Te is achieved.
Claim 3
Dependent Claim
19 words
The process of claim 1 in which said mixture is heated to about 20° to 30° C. above liquidus.
Claim 4
Dependent Claim
32 words
The process of claim 1 further characterized in that said container is placed in a rocking furnace whereby said mixture contained therein is rocked, heated and positioned according to the process herein.
Claim 5
Dependent Claim
171 words
A process for producing Hg 1-x Cd x Te ingots comprising the steps of: (a) adding predetermined amounts of mercury, cadmium and tellurium to a container to produce a stoichiometric mixture thereof of cadmium telluride mole-fraction x; (b) heating said mixture to a predetermined temperature above liquidus; (c) rocking said container at the same time to produce to a homogeneous mixture of Hg 1-x Cd x Te; (d) discontinuing the application of heat to said container; (e) terminating the rocking at +45° with respect to the vertical when the temperature of the mixture has dropped to about 8° C. above liquidus; (f) supercooling said mixture by maintaining said container at the vertical until the temperature of said mixture drops an amount below liquidus which is a predetermined function of x; and (g) quenching said mixture by exposing said container to ambient air conditions by rapidly withdrawing from the furnace, so there is produced an ingot of Hg 1-x Cd x Te having a large number of crystallites with small grain boundaries.
Claim 6
Dependent Claim
171 words
A process for producing Hg 1-x Cd x Te ingots comprising the steps of: (a) adding predetermined amounts of mercury, cadmium and tellurium to a container to produce a stoichiometric mixture thereof of cadmium telluride mole-fraction x; (b) heating said mixture to a predetermined temperature above liquidus; (c) rocking said container at the same time to produce to a homogeneous mixture of Hg 1-x Cd x Te; (d) discontinuing the application of heat to said container; (e) terminating the rocking at +45° with respect to the vertical when the temperature of the mixture has dropped to about 8° C. above liquidus; (f) supercooling said mixture by maintaining said container at the vertical until the temperature of said mixture drops an amount below liquidus which is a predetermined function of x; and (g) quenching said mixture by exposing said container to ambient air conditions by rapidly withdrawing from the furnace, so there is produced an ingot of Hg 1-x Cd x Te having a large number of crystallites with small grain boundaries.
Claim 7
Dependent Claim
19 words
The process of claim 1 in which said mixture is heated to about 20° to 30° C. above liquidus.
Claim 8
Dependent Claim
35 words
The process of claim 1 further characterized in that said container is placed in a rocking furnace whereby said mixture contained therein is rocked, heated and positioned according to the steps of the process herein.
References Cited (Backward Citations)
US3468363A
Cited
US3622399A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-16 | 1986-02-15 | 1986-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-16 | 1990-02-15 | 1990-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-16 | 1994-02-15 | 1994-08-17 | $7700.00 | Window Closed / Lapsed |