Method for producing an electrophotographic recording material having dual layer of amorphous and crystallized Se
Assignee: Licentia Patent Verwaltungs GmbH
•
Filing: 1980-12-30
•
Granted: 1982-08-10
•
Expires: 2000-12-30
Abstract
Abstract In a method for producing an electrophotographic recording material composed of a dual layer of amorphous and crystallized selenium applied to an electrically conductive substrate, tellurium is vapor-deposited in a vacuum onto the surface of the conductive substrate to a layer thickness of about 0.5 to about 5 nanometers to form a tellurium layer, and selenium is vapor-deposited onto the tellurium layer to a layer thickness of about 20 to about 100 microns to form the dual layer of amorphous and crystallized selenium.
Inventors
- 👤 Karl-Heinz Kassel
- 👤 Manfred Lutz
- 👤 Josef Stuke
- 👤 Hubert Walsdorfer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:52
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/02; G03G5/04; G03G5/08; G03G5/082; G03G5/08207; G03G5/043; G03G5/0433
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
87 words
In a method for producing an electrophotographic recording material composed of a dual layer of amorphous and crystallized selenium applied to an electrically conductive substrate, the improvement comprising the steps of: vapor-depositing tellurium in a vacuum onto the surface of the conductive substrate to a layer thickness of about 0.5 to about 5 nanometers to form a tellurium layer; and vapor-depositing selenium onto said tellurium layer to a layer thickness of about 20 to about 100 microns to form the dual layer of amorphous and crystallized selenium.
Claim 2
Dependent Claim
87 words
In a method for producing an electrophotographic recording material composed of a dual layer of amorphous and crystallized selenium applied to an electrically conductive substrate, the improvement comprising the steps of: vapor-depositing tellurium in a vacuum onto the surface of the conductive substrate to a layer thickness of about 0.5 to about 5 nanometers to form a tellurium layer; and vapor-depositing selenium onto said tellurium layer to a layer thickness of about 20 to about 100 microns to form the dual layer of amorphous and crystallized selenium.
Claim 3
Dependent Claim
23 words
The method as defined in claim 1, further comprising the step of: preheating the conductive substrate prior to said step of vapor-depositing tellurium.
Claim 4
Independent Claim
21 words
The method as defined in claims 1 or 2, wherein the tellurium is vapor-deposited to a layer thickness of 1 nanometer.
Claim 5
Independent Claim
25 words
The method as defined in claims 1 or 2, wherein said steps of vapor-depositing are performed at a pressure of less than 10 -4 millibars.
Claim 6
Independent Claim
23 words
The method as defined in claims 1 or 2, wherein said step of vapor-depositing tellurium is performed at the rate of 3 nanometers/minute.
Claim 7
Independent Claim
23 words
The method as defined in claims 1 or 2, wherein said step of vapor-depositing selenium is performed at the rate of 1 micron/minute.
Claim 8
Independent Claim
47 words
The method as defined in claims 1 or 2, further comprising the step of preheating the conductive substrate to a temperature of about 62° to about 75° C. prior to said step of vapor-depositing tellurium and wherein said steps of vapor-depositing are performed in a single operation.
Claim 9
Dependent Claim
75 words
The method as defined in claim 1, wherein said step of vapor-depositing tellurium is carried out at a temperature of about 20° to about 30° C., further comprising preheating the conductive substrate to a temperature of about 62° to about 75° C. after said step of vapor-depositing tellurium and before said step of vapor-depositing selenium, and wherein said step of vapor-depositing selenium is carried out at the temperature to which the substrate has been preheated.
Claim 10
Dependent Claim
97 words
The method as defined in claim 1 wherein said step of vapor-depositing selenium comprises, after said step of vapor-depositing tellurium: preheating the substrate to a temperature of about 60° to about 75° C.; vapor-depositing selenium onto the preheated substrate at a rate of about 0.05 to 0.5 micron/minute to a thickness of about 1 to about 3 microns; lowering the substrate temperature to between about 60° and about 65° C.; and additionally vapor-depositing selenium, with the substrate at the lowered temperature, at a rate of about 0.5 to about 5 microns/minute to the desired dual layer thickness.
Claim 11
Independent Claim
69 words
The method as defined in claims 1 or 2, wherein said step of vapor-depositing selenium is performed in two stages, the first stage being performed by evaporating selenium from a first evaporator to a layer thickness of about 1 to about 3 microns, and the second stage being performed by evaporating selenium from a second evaporator to achieve the dual layer thickness of about 20 to about 100 microns.
Claim 12
Independent Claim
50 words
A method as defined in claims 1 or 2, wherein said step of vapor-depositing tellurium is performed by evaporating tellurium from a surface which is so oriented relative to the substrate for causing streams of tellurium vapor to be emitted from the surface in a direction away from the substrate.
Claim 13
Dependent Claim
36 words
The method as defined in claim 11 wherein the surface is oriented for causing the streams of vapor to be emitted in a direction approximately perpendicular to the general direction from the surface to the substrate.
Claim 14
Dependent Claim
36 words
The method as defined in claim 11 wherein the surface is oriented for causing the streams of vapor to be emitted in a direction approximately opposite to the general direction from the surface to the substrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-09 | 1986-02-08 | 1986-08-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-09 | 1990-02-08 | 1990-08-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-09 | 1994-02-08 | 1994-08-10 | $7700.00 | Window Closed / Lapsed |