Sizing composition and sized glass fibers and process
Assignee: PPG Industries Ohio Inc
•
Filing: 1980-06-04
•
Granted: 1982-07-27
•
Expires: 2000-06-04
Abstract
Abstract A sizing composition for use in a process of producing sized glass fiber strands that can be used in reinforcing polymers is provided. Also provided are the sized glass fiber strands, glass fiber reinforced polymers and processes for producing these materials. The sizing composition comprises one or more organo silane coupling agents, a major amount of the solids of the aqueous sizing composition is an epoxidized polar thermoplastic copolymer where there are three to about twelve parts of epoxy per 100 parts of the other comonomer and one or more nonionic, cationic or anionic lubricants. The sizing composition can also have one or more compatibilizing agents such as a polyvinyl-acetate-ethylene copolymer unsaturated polyester resins, polyvinylacetate homopolymer, epoxy polymers and epoxy polyester copolymers. The comonomers for the epoxidized polar thermoplastic copolymer are vinyl acetate, acrylates, polyurethane condensate monomer, polyester condensate monomer, and polyamide condensate monomer. The epoxidized polar thermoplastic copolymer has a Tg in the range of ambient temperatures to about 70° C. The glass fiber strands treated with this sizing composition can be made into roving for use in producing glass fiber reinforced polymers like polyester polymers, vinyl ester polymers and epoxy polymers.
Inventors
- 👤 Balbhadra Das
- 👤 Billie D. Tucker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:48
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26; C03C25/32; C03C25/36; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/2962
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
157 words
An aqueous sizing composition for glass fibers that is substantially soluble in polymeric materials the glass fibers are to reinforce, comprising: (a) a predominant amount of the solids of the composition being an epoxidized polar thermoplastic copolymer having 3 to about 12 parts of epoxy per 100 parts of copolymer, where the comonomer is selected from vinyl acetate, acrylate and polyurethane condensate monomer, and where the polymer has a Tg in the range of ambient temperatures to about 70° C.; (b) one or more compatibilizing agents selected from unsaturated polyester polymer, polyvinylacetate homopolymer or vinyl acetate-ethylene copolymer, in an amount of less than about 20 weight percent of the total amount of film former in the sizing composition; (c) one or more organo silane coupling agents; (d) one or more lubricants, (e) an amount of water sufficient to make the percent solids of the sizing composition in the range of about 2 to about 30 weight percent.
Claim 2
Dependent Claim
157 words
An aqueous sizing composition for glass fibers that is substantially soluble in polymeric materials the glass fibers are to reinforce, comprising: (a) a predominant amount of the solids of the composition being an epoxidized polar thermoplastic copolymer having 3 to about 12 parts of epoxy per 100 parts of copolymer, where the comonomer is selected from vinyl acetate, acrylate and polyurethane condensate monomer, and where the polymer has a Tg in the range of ambient temperatures to about 70° C.; (b) one or more compatibilizing agents selected from unsaturated polyester polymer, polyvinylacetate homopolymer or vinyl acetate-ethylene copolymer, in an amount of less than about 20 weight percent of the total amount of film former in the sizing composition; (c) one or more organo silane coupling agents; (d) one or more lubricants, (e) an amount of water sufficient to make the percent solids of the sizing composition in the range of about 2 to about 30 weight percent.
Claim 3
Dependent Claim
39 words
Aqueous sizing composition of claim 1 wherein the organo-silane coupling agent present is a silane having a free radical polymerizable reactive organo moiety in an amount of about 0.1 to about 5 weight percent of the aqueous sizing composition.
Claim 4
Dependent Claim
28 words
Aqueous sizing composition of claim 1 wherein the organo-silane coupling agents present are a silane having a free radical polymerizable reactive organo moiety and an aminofunctional organo silane.
Claim 5
Dependent Claim
20 words
Aqueous sizing composition of claim 1 wherein the one or more lubricants are selected from cationic, nonionic and anionic lubricants.
Claim 6
Dependent Claim
22 words
Aqueous sizing composition of claim 1 wherein the one or more lubricants are selected from amidated polyamine lubricants and alkylimidazoline derivative lubricants.
Claim 7
Dependent Claim
23 words
Aqueous sizing composition of claim 1 wherein the percent by weight of solids is in the range of about 18 to about 25.
Claim 8
Dependent Claim
17 words
The aqueous sizing composition of claim 1 wherein the expoxidized polar thermoplastic copolymer is epoxidized polyvinylacetate copolymer.
Claim 9
Dependent Claim
225 words
In a process of preparing sized glass fiber roving for use in preparing reinforced polymeric materials, the Improvement comprising: (a) treating the glass fibers during their formation with an aqueous sizing composition, comprising: (1) a major amount of the solids of the sizing composition in an epoxidized polar thermoplastic copolymer having 3 to about 12 parts of epoxy per 100 parts of the copolymer, where the comonomer is selected from vinyl acetate, acrylate, and polyurethane condensate monomer, where the copolymer has a Tg in the range of ambient temperatures to about 70° C., (2) one or more compatibilizing agents selected from unsaturated polyester polymers, polyvinylacetate homopolymer, or vinyl acetate-ethylene copolymers, in an amount of less than 20 weight percent of the film former, (3) one or more organo silane coupling agents, (4) one or more nonionic, cationic or anionic lubricants, and (5) an amount of water sufficient to make the percent solids of the sizing composition in the range of about 2 to about 30 weight percent, (b) gathering the treated glass fibers into one or more treated glass fiber strands, (c) drying the treated glass fiber strand or strands at a temperature above about 100° C. for more than one hour to remove most of the moisture from the strand or strands, (d) gathering a plurality of dried glass fiber strands into a roving.
Claim 10
Dependent Claim
225 words
In a process of preparing sized glass fiber roving for use in preparing reinforced polymeric materials, the Improvement comprising: (a) treating the glass fibers during their formation with an aqueous sizing composition, comprising: (1) a major amount of the solids of the sizing composition in an epoxidized polar thermoplastic copolymer having 3 to about 12 parts of epoxy per 100 parts of the copolymer, where the comonomer is selected from vinyl acetate, acrylate, and polyurethane condensate monomer, where the copolymer has a Tg in the range of ambient temperatures to about 70° C., (2) one or more compatibilizing agents selected from unsaturated polyester polymers, polyvinylacetate homopolymer, or vinyl acetate-ethylene copolymers, in an amount of less than 20 weight percent of the film former, (3) one or more organo silane coupling agents, (4) one or more nonionic, cationic or anionic lubricants, and (5) an amount of water sufficient to make the percent solids of the sizing composition in the range of about 2 to about 30 weight percent, (b) gathering the treated glass fibers into one or more treated glass fiber strands, (c) drying the treated glass fiber strand or strands at a temperature above about 100° C. for more than one hour to remove most of the moisture from the strand or strands, (d) gathering a plurality of dried glass fiber strands into a roving.
Claim 11
Dependent Claim
17 words
One or more glass fiber strands having the dried residue of the sizing composition of claim 1.
Claim 12
Dependent Claim
13 words
Glass fiber reinforced polymeric articles having the glass fiber strands of claim 9.
Claim 13
Dependent Claim
89 words
A sizing composition for treating glass fibers having a vinyl-containing organo functional silane, epoxidized polyvinylacetate copolymer present in a major amount of the solids of the aqueous sizing composition and in the range of 3 to about 20 weight percent of the aqueous sizing composition, the copolymer having about 3 to about 12 parts of epoxy per 100 parts of vinylacetate, and vinylacetate-ethylene copolymer present in an amount of water to give a solids content for the sizing composition in the range of 2 to about 30 weight percent.
Claim 14
Dependent Claim
89 words
A sizing composition for treating glass fibers having a vinyl-containing organo functional silane, epoxidized polyvinylacetate copolymer present in a major amount of the solids of the aqueous sizing composition and in the range of 3 to about 20 weight percent of the aqueous sizing composition, the copolymer having about 3 to about 12 parts of epoxy per 100 parts of vinylacetate, and vinylacetate-ethylene copolymer present in an amount of water to give a solids content for the sizing composition in the range of 2 to about 30 weight percent.
Claim 15
Dependent Claim
33 words
The composition according to claim 11 having an unsaturated polyester resin compatabilizing agent present in an amount less than 10 weight percent of the amount of film former in the aqueous sizing composition.
Claim 16
Dependent Claim
16 words
Sized glass fiber strands have the dried residue of the aqueous sizing composition of claim 13.
Claim 17
Dependent Claim
13 words
Glass fiber reinforced polymer having the sized glass fiber strands of claim 11.
Claim 18
Dependent Claim
20 words
The article according to claim 14. wherein the reinforced polymer is selected from unsaturated polyesters, vinyl esters and epoxy polymers.
Claim 19
Dependent Claim
144 words
A process for preparing an aqueous sizing composition for treating glass fibers for use as reinforcement in polymeric materials, comprising: (a) combining an organo silane coupling agent having the free radical polymerizable organo moiety with water and acetic acid, (b) combining an epoxidized polyvinylacetate copolymer present in a major amount of the solids of the aqueous sizing composition with an unhydrolyzed or partially hydrolyzed aminofunctional organo silane coupling agent present in an amount in the range of about 0.1 to about 5 weight percent of the aqueous sizing composition, (c) adding vinyl acetate-ethylene copolymer to the organo silane mixture of step a), (d) adding the mixture of step c) to the water diluted mixture of step b), (e) adding water diluted amidated polyamine lubricant to the mixture of step d), (f) diluting the mixture of step e) with water to obtain the desired volume.
Claim 20
Dependent Claim
144 words
A process for preparing an aqueous sizing composition for treating glass fibers for use as reinforcement in polymeric materials, comprising: (a) combining an organo silane coupling agent having the free radical polymerizable organo moiety with water and acetic acid, (b) combining an epoxidized polyvinylacetate copolymer present in a major amount of the solids of the aqueous sizing composition with an unhydrolyzed or partially hydrolyzed aminofunctional organo silane coupling agent present in an amount in the range of about 0.1 to about 5 weight percent of the aqueous sizing composition, (c) adding vinyl acetate-ethylene copolymer to the organo silane mixture of step a), (d) adding the mixture of step c) to the water diluted mixture of step b), (e) adding water diluted amidated polyamine lubricant to the mixture of step d), (f) diluting the mixture of step e) with water to obtain the desired volume.
Claim 21
Dependent Claim
9 words
Sizing composition produced by the method of claim 16.
References Cited (Backward Citations)
US3245938A
Cited
GB955080A
Cited
US3437517A
Cited
US3449281A
Cited
GB1138528A
Cited
GB1136548A
Cited
US3459585A
Cited
GB1250194A
Cited
GB1271500A
Cited
GB1253936A
Cited
US3827230A
Cited
GB1375035A
Cited
US4049597A
Cited
US4110094A
Cited
US3997306A
Cited
GB1550661A
Cited
US4126729A
Cited
US4235764A
Cited
US4241136A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-26 | 1986-01-25 | 1986-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-26 | 1990-01-25 | 1990-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-26 | 1994-01-25 | 1994-07-27 | $7700.00 | Window Closed / Lapsed |