Process for the manufacture of ferromagnetic chromium dioxide
Assignee: Emtec Magnetics GmbH
•
Filing: 1980-10-21
•
Granted: 1982-07-20
•
Expires: 2000-10-21
Abstract
Abstract A process for the manufacture of ferromagnetic chromium dioxide modified with foreign elements, by reacting oxides of trivalent and hexavalent chromium under superatmospheric pressure at an elevated temperature in the presence of water and of antimony(III) oxide as modifier, with or without other modifiers in an amount not exceeding 15% by weight, wherein the antimony(III) oxide employed as modifier is, to the extent of more than one-third, present as the senarmontite cubic modification, has a specific surface area, measured by the BET method, of from 1.5 to 15 m 2 /g, and is added in a total amount of up to 0.5% by weight, based on the resulting chromium dioxide.
Inventors
- 👤 Manfred Ohlinger
- 👤 Guenter Vaeth
- 👤 Norbert Mueller
- 👤 Eugen Wettstein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:05
CPC Classifications
C; C01; C01G; C01G37/00; C01G37/02; C01G37/027; G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70636; C01P; C01P2006/00; C01P2006/11; C01P2006/12; C01P2006/42; C01P2006/80
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
118 words
A process for the manufacture of ferromagnetic chromium dioxide by reacting oxides of trivalent and hexavalent chromium under a pressure of from 100 to 700 bar at a temperature from 200°-600° C. in the presence of water and of antimony(III) oxide as modifier, with or without other modifiers in an amount not exceeding 15% by weight, wherein the antimony(III) oxide employed as modifier is, to the extent of more than one-third of the antimony(III) oxide, present as the senarmontite cubic modification, has a specific surface area, measured by the BET method, of from 2.5 to 15 m 2 /g, and is added in an amount of from 0.1 to 0.5% by weight, based on the resulting chromium dioxide.
Claim 2
Dependent Claim
118 words
A process for the manufacture of ferromagnetic chromium dioxide by reacting oxides of trivalent and hexavalent chromium under a pressure of from 100 to 700 bar at a temperature from 200°-600° C. in the presence of water and of antimony(III) oxide as modifier, with or without other modifiers in an amount not exceeding 15% by weight, wherein the antimony(III) oxide employed as modifier is, to the extent of more than one-third of the antimony(III) oxide, present as the senarmontite cubic modification, has a specific surface area, measured by the BET method, of from 2.5 to 15 m 2 /g, and is added in an amount of from 0.1 to 0.5% by weight, based on the resulting chromium dioxide.
Claim 3
Dependent Claim
42 words
A process as claimed in claim 1, wherein the antimony(III) oxide employed as modifier consists to the extent of at least 98% of senarmontite having a specific surface area, measured by the BET method, of from 3 to 10 m 2 /g.
Claim 4
Dependent Claim
38 words
A process as claimed in claim 1 or 2, wherein acicular iron oxide particles in the form of alpha-FeOOH are employed, as additional modifier, in an amount of from 0.5 to 15% by weight, based on chromium dioxide.
Claim 5
Dependent Claim
41 words
A process as claimed in claim 1 or 2, wherein acicular iron oxide particles in the form of gamma-Fe 2 O 3 are employed, as additional modifier, in an amount of from 0.5 to 15% by weight, based on chromium dioxide.
References Cited (Backward Citations)
US3034988A
Cited
US3117093A
Cited
US3278263A
Cited
NL6617476A
Cited
DE2022820A1
Cited
US3687851A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-19 | 1986-01-18 | 1986-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-19 | 1990-01-18 | 1990-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-19 | 1994-01-18 | 1994-07-20 | $7700.00 | Window Closed / Lapsed |