Process for producing three-dimensional, mirrored acrylic articles
Assignee: RAM PRODUCTS Inc
•
Filing: 1981-05-11
•
Granted: 1982-07-13
•
Expires: 2001-05-11
Abstract
Abstract A process for producing three-dimensional, mirrored acrylic products using forming techniques eliminates micro-fracturing of a vacuum deposited reflective metal coating by preshrinking a sheet of acrylic before the sheet is mirrorized and formed into the desired three-dimensional shape. Preshrinking is accomplished by heating the sheet to forming temperature and allowing the heated sheet to cool at room temperature before the sheet is formed. Deposition of the metallic reflective coating is performed after the preshrinking step.
Inventors
- 👤 Paul A. Sorko-Ram
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:01
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/00596
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
90 words
A process for producing a three-dimensional thermoplastic object having a mirror-like reflective finish, comprising the steps of: (A) heating a sheet of thermoplastic material to a temperature sufficient to form said sheet but less than the melting temperature of said sheet; (B) then, cooling said sheet substantially to room temperature; (C) then, depositing a layer of reflective metal on the surface of said sheet; (D) then, heating said sheet to a temperature sufficient to form said sheet; and, (E) then, forming said sheet into the shape of said three-dimensional object.
Claim 2
Dependent Claim
90 words
A process for producing a three-dimensional thermoplastic object having a mirror-like reflective finish, comprising the steps of: (A) heating a sheet of thermoplastic material to a temperature sufficient to form said sheet but less than the melting temperature of said sheet; (B) then, cooling said sheet substantially to room temperature; (C) then, depositing a layer of reflective metal on the surface of said sheet; (D) then, heating said sheet to a temperature sufficient to form said sheet; and, (E) then, forming said sheet into the shape of said three-dimensional object.
Claim 3
Dependent Claim
14 words
The process of claim 1, wherein said material is of a substantially methylmethacrylate base.
Claim 4
Dependent Claim
16 words
The process of claim 2, wherein step (A) is performed for approximately five to ten minutes.
Claim 5
Dependent Claim
20 words
The process of claim 2, wherein said temperature of step (A) is in the range of 250° to 400° F.
Claim 6
Dependent Claim
14 words
The process of claim 2, wherein step (B) is carried out at room temperature.
Claim 7
Dependent Claim
28 words
The process of claim 2, wherein said temperature of step (D) is at least approximately 250° F. and step (D) is continued for at least approximately five minutes.
Claim 8
Dependent Claim
17 words
The process of claim 2, wherein step (E) is performed by subjecting said sheet to a vacuum.
Claim 9
Dependent Claim
20 words
The process of claim 2, including the step of applying an abrasion resistant coating on said layer of reflective metal.
Claim 10
Dependent Claim
44 words
A process for producing a three-dimensional reflective object from thermo-plastic material, comprising the steps of: (A) preshrinking a sheet of said thermo-plastic material; (B) then, vapor depositing a reflective layer on said sheet; (C) then, forming said sheet into the shape of said object.
Claim 11
Dependent Claim
44 words
A process for producing a three-dimensional reflective object from thermo-plastic material, comprising the steps of: (A) preshrinking a sheet of said thermo-plastic material; (B) then, vapor depositing a reflective layer on said sheet; (C) then, forming said sheet into the shape of said object.
Claim 12
Dependent Claim
32 words
The process of claim 9, wherein step (A) is performed by heating said sheet to a temperature sufficient to form said sheet and then cooling the heated sheet to substantially room temperature.
Claim 13
Dependent Claim
22 words
The process of claim 10, wherein said sheet is heated at said temperature for a period of approximately five to ten minutes.
References Cited (Backward Citations)
GB614459A
Cited
US2740732A
Cited
US3000057A
Cited
US3094430A
Cited
US3431135A
Cited
US3914471A
Cited
US4154788A
Cited
US3967992A
Cited
US4139586A
Cited
US4255364A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-12 | 1986-01-11 | 1986-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-12 | 1990-01-11 | 1990-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-12 | 1994-01-11 | 1994-07-13 | $7700.00 | Window Closed / Lapsed |