Composite material compositions using wastepaper and method of producing same

Assignee: Gunma Kasai Co Ltd
•
Filing: 1980-04-28
•
Granted: 1982-07-13
•
Expires: 2000-04-28
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract This invention provides composite material compositions comprising wastepaper, a thermoplastic resin and/or other additive(s), said compositions having higher heat resistance, flame retardancy and mechanical strength and smaller linear shrinkage in molding than the conventional compositions of synthetic resins alone or blended with woodmeal or an inorganic filler. There is also provided a method of producing said compositions comprising a wastepaper crushing step, a step of mixing crushed wastepaper with a thermoplastic resin and/or other additive(s) while drying said wastepaper, a blend melting step, a blend kneading step and a blend granulating step. In an embodiment of this invention, scraps of moldings from the composite material compositions using wastepaper may be mixed with wastepaper, a thermoplastic resin and/or other additive(s) and similarly treated and molded into a new composition.

Inventors

  • 👤 Yoshikazu Nakagima

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-02 15:31
CPC Classifications
C; C08; C08L; C08L1/00; C08L1/02; C08L101/00

Claims Analysis

Total Claims: 7
Claim 1
Independent Claim 102 words
A method of producing a granular molding composition that provides substantially reduced linear shrinkage and excellent mechanical strength, comprising the steps of cutting wastepaper into pieces of a size less than 30 mm., stirring 100 parts by weight of the wastepaper at high speed in a mixer with about 70 to 150 parts by weight of the thermoplastic resin to drive off moisture from the wastepaper, and to melt the thermoplastic resin, continuing high speed stirring to beat and knead the cut wastepaper with the molten resin and thereby impregnate the cut wastepaper with the molten resin, and then granulating the composition.
Claim 2
Independent Claim 102 words
A method of producing a granular molding composition that provides substantially reduced linear shrinkage and excellent mechanical strength, comprising the steps of cutting wastepaper into pieces of a size less than 30 mm., stirring 100 parts by weight of the wastepaper at high speed in a mixer with about 70 to 150 parts by weight of the thermoplastic resin to drive off moisture from the wastepaper, and to melt the thermoplastic resin, continuing high speed stirring to beat and knead the cut wastepaper with the molten resin and thereby impregnate the cut wastepaper with the molten resin, and then granulating the composition.
Claim 3
Dependent Claim 25 words
A method of claim 1, wherein the wastepaper cutting step comprises cutting wastepaper by a cutter and then crushing the cut wastepaper by a mill.
Claim 4
Dependent Claim 25 words
A method of claim 2, wherein the mixer used in the mixing and drying step and the melting step is preheated by a heating medium.
Claim 5
Dependent Claim 49 words
A method of claim 3, wherein before the kneading step is switched into the granulation step, the stirring rate of the mixer is reduced to a medium level for a short time after completion of the kneading step, to nucleate the material, and the granulation step is then started.
Claim 6
Dependent Claim 22 words
A method of claim 4, wherein the kneading step is switched into the nucleation step before carbonization of the wastepaper component occurs.
Claim 7
Dependent Claim 41 words
A method of claim 5, wherein the scraps of moldings formed from a composition of this invention are crushed into powder and mixed with wastepaper, a thermoplastic resin and/or other additive(s) and then subjected to the described steps in a mixer.

References Cited (Backward Citations)

US2416888A Cited
US4228116A Cited
US3969314A Cited
US4225640A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1985-07-12 1986-01-11 1986-07-13 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1989-07-12 1990-01-11 1990-07-13 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1993-07-12 1994-01-11 1994-07-13 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag