Optical waveguide containing P2 O5 and GeO2
Assignee: Corning Glass Works
•
Filing: 1975-09-08
•
Granted: 1982-07-13
•
Expires: 1995-09-08
Abstract
Abstract An optical waveguide having a cladding of high purity glass and a core of high purity glass doped with an amount of P2O5 and GeO2 to increase the refractive index thereof to a predetermined level. The ratio of P2O5 to GeO2 is such that the softening point temperature of the core is compatible with that of the cladding. The core glass has a cation impurity level not exceeding 10 parts per million.
Inventors
- 👤 Ishwar D. Aggarwal
- 👤 Eric N. Randall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 23:57
CPC Classifications
C; C03; C03C; C03C13/00; C03C13/04; C03C13/048; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01413; C03C13/045; C03C13/046; G; G02; G02B; G02B6/00; G02B6/02; C03B2201/00; C03B2201/06; C03B2201/20; C03B2201/28; C03B2201/30; C03B2201/31; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/225; C03B2203/24; C03B2203/26; C03B2207/00; C03B2207/46; C03B2207/50
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
59 words
An optical fiber comprising a cladding layer formed of high purity glass, and a core of high purity glass containing an amount of P 2 O 5 and GeO 2 to provide a refractive index greater than that of said cladding layer, said core glass having a cation impurity level not exceeding 10 parts per million of transition elements.
Claim 2
Dependent Claim
59 words
An optical fiber comprising a cladding layer formed of high purity glass, and a core of high purity glass containing an amount of P 2 O 5 and GeO 2 to provide a refractive index greater than that of said cladding layer, said core glass having a cation impurity level not exceeding 10 parts per million of transition elements.
Claim 3
Dependent Claim
19 words
The fiber of claim 1 wherein said core essentially consists of P 2 O 5 and GeO 2 .
Claim 4
Dependent Claim
43 words
The fiber of claim 1 wherein said cladding layer contains an amount of B 2 O 3 such that the expansion coefficient of said cladding layer is less than that of said core by an amount between 0 and 15×10 -7 per °C.
Claim 5
Dependent Claim
27 words
The fiber of claim 3 wherein the softening temperature of said core glass is less than that of said cladding layer by up to about 50° C.
Claim 6
Dependent Claim
13 words
The fiber of claim 1 wherein said core has a gradient refractive index.
Claim 7
Dependent Claim
14 words
The fiber of claim 1 wherein said core has a substantially constant refractive index.
Claim 8
Dependent Claim
120 words
The fiber of claim 1 wherein said core glass comprises P 2 O 5 , GeO 2 and SiO 2 and said cladding glass layer comprises B 2 O 3 and SiO 2 , said core containing an amount of P 2 O 5 that is sufficient to reduce the softening temperature of said core glass to a value which is less than that of said cladding glass by an amount between 0° and 50° C., and said cladding layer having an amount of B 2 O 3 that is sufficient to increase the expansion coefficient of said cladding layer to a value less than that of said core glass by an amount between 0 and 15×10 -7 per °C.
Claim 9
Dependent Claim
36 words
The fiber of claim 1 wherein the amount of P 2 O 5 present in said core glass is about 40-60 wt.% of the total amount of P 2 O 5 and GeO 2 present therein.
Claim 10
Dependent Claim
21 words
The fiber of claim 8 wherein the amount of SiO 2 present in said core glass is up to 70 wt.%.
Claim 11
Dependent Claim
29 words
An optical waveguide comprising a core of glass formed of phosphorous pentoxide, germania and silica and a cladding of a glass of a lower refractive index than the core.
Claim 12
Dependent Claim
29 words
An optical waveguide comprising a core of glass formed of phosphorous pentoxide, germania and silica and a cladding of a glass of a lower refractive index than the core.
Claim 13
Dependent Claim
14 words
The optical waveguide of claim 10 in which the cladding comprises a borosilicate glass.
Claim 14
Dependent Claim
14 words
The optical waveguide of claim 10 wherein said core has a gradient refractive index.
Claim 15
Dependent Claim
64 words
An optical waveguide fiber comprising a glass core surrounded by a cladding of glass having a refractive index less than that of said core glass, said core glass comprising SiO 2 and GeO 2 , said core glass including P 2 O 5 in an amount sufficient that the softening point temperature of said core glass is less than that of said cladding glass.
Claim 16
Dependent Claim
64 words
An optical waveguide fiber comprising a glass core surrounded by a cladding of glass having a refractive index less than that of said core glass, said core glass comprising SiO 2 and GeO 2 , said core glass including P 2 O 5 in an amount sufficient that the softening point temperature of said core glass is less than that of said cladding glass.
Claim 17
Dependent Claim
47 words
An optical waveguide fiber in accordance with claim 13 wherein said core glass includes P 2 O 5 in an amount sufficient that the softening point temperature of said core glass is less than that of said cladding glass by an amount between 0° and 50° C.
Claim 18
Dependent Claim
23 words
An optical waveguide fiber in accordance with claim 13 wherein said cladding glass comprises SiO 2 doped with B 2 O 3 .
Claim 19
Dependent Claim
47 words
An optical waveguide fiber in accordance with claim 15 wherein said core glass includes P 2 O 5 in an amount sufficient that the softening point temperature of said core glass is less than that of said cladding glass by an amount between 0° and 50° C.
Claim 20
Dependent Claim
51 words
An optical waveguide fiber in accordance with claim 16 wherein said cladding glass comprises SiO 2 doped with a sufficient amount of B 2 O 3 to increase the coefficient of expansion thereof to a value which is up to 15×10 -7 per °C. lower than that of said core glass.
Claim 21
Dependent Claim
51 words
An optical waveguide fiber in accordance with claim 13 wherein said cladding glass comprises SiO 2 doped with a sufficient amount of B 2 O 3 to increase the coefficient of expansion thereof to a value which is up to 15×10 -7 per °C. lower than that of said core glass.
References Cited (Backward Citations)
US3938974A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-12 | 1986-01-11 | 1986-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-12 | 1990-01-11 | 1990-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-12 | 1994-01-11 | 1994-07-13 | $7700.00 | Window Closed / Lapsed |