Apparatus for processing microwave electrical energy
Assignee: AT&T Inc
•
Filing: 1980-06-16
•
Granted: 1982-06-29
•
Expires: 2000-06-16
Abstract
Abstract A process is described for the preparation of ceramic dielectrics for microwave applications which yield high quality (Q) factors, high dielectric stability and excellent mechanical stability. The procedure is particularly useful where the size of the ceramic dielectric structures is large (average diameter greater than one inch).
Inventors
- 👤 Henry M. O'Bryan, Jr.
- 👤 John Thomson, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:20
CPC Classifications
H; H01; H01P; H01P7/00; H01P7/10; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4686; C04B35/622; C04B35/64
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
151 words
An apparatus for processing microwave electrical energy with frequency between 0.5 and 6.0 GHz comprising a dielectric material for interaction with the microwave electrical energy, means for introducing microwave electrical energy into the dielectric material, conducting member to contain the microwave electrical energy in the apparatus in which the dielectrical material comprises at least 80 weight percent ceramic with composition corresponding to nominal formula of Ba 2 Ti 9 O 20 characterized in that after sintering into a solid ceramic body the dielectric material is exposed to a heat treatment comprising the steps of (a) contacting the dielectric material to an oxygen enriched atmosphere consisting of at least 50 volume percent oxygen for at least 6 hours at a temperature between 1100 and 1300 degrees C.; and (b) cooling the dielectric material in the oxygen enriched atmosphere at a rate less than 200 degrees per hour down to 600 degrees C.
Claim 2
Independent Claim
151 words
An apparatus for processing microwave electrical energy with frequency between 0.5 and 6.0 GHz comprising a dielectric material for interaction with the microwave electrical energy, means for introducing microwave electrical energy into the dielectric material, conducting member to contain the microwave electrical energy in the apparatus in which the dielectrical material comprises at least 80 weight percent ceramic with composition corresponding to nominal formula of Ba 2 Ti 9 O 20 characterized in that after sintering into a solid ceramic body the dielectric material is exposed to a heat treatment comprising the steps of (a) contacting the dielectric material to an oxygen enriched atmosphere consisting of at least 50 volume percent oxygen for at least 6 hours at a temperature between 1100 and 1300 degrees C.; and (b) cooling the dielectric material in the oxygen enriched atmosphere at a rate less than 200 degrees per hour down to 600 degrees C.
Claim 3
Dependent Claim
17 words
The apparatus of claim 1 in which the atmosphere consists of at least 95 volume percent oxygen.
Claim 4
Dependent Claim
16 words
The apparatus of claim 1 in which the heat treatment is from 6 to 24 hours.
Claim 5
Dependent Claim
14 words
The apparatus of claim 3 in which the heat treatment is approximately 12 hours.
Claim 6
Dependent Claim
24 words
The apparatus of claim 1 in which the cooling rate is less than approximately 50 degrees C. per hour down to 600 degrees C.
Claim 7
Dependent Claim
19 words
The apparatus of claim 1 in which the microwave electrical energy has a frequency between 0.5 and 1.0 GHz.
Claim 8
Dependent Claim
22 words
The apparatus of claim 1 in which there is excess barium over the stoichiometric amount of between zero and 0.2 mole percent.
Claim 9
Dependent Claim
34 words
The apparatus of claim 1 in which the dielectric material is in the form of a right cylinder which is used to stabilize microwave frequency in the frequency range from 0.5 to 1.0 GHz.
References Cited (Backward Citations)
US4026811A
Cited
US3938064A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-28 | 1985-12-28 | 1986-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-28 | 1989-12-28 | 1990-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-28 | 1993-12-28 | 1994-06-29 | $7700.00 | Window Closed / Lapsed |