Non-pulsed electrochemical impregnation of flexible metallic battery plaques
Assignee: United States, ENERGY THE, Department of
•
Filing: 1981-08-14
•
Granted: 1982-06-29
•
Expires: 2001-08-14
Abstract
Abstract A method of loading active battery material into porous, flexible, metallic battery plaques, comprises the following steps: precipitating nickel hydroxide active material within the plaque, by making the plaque cathodic, at a high current density, in an electro-precipitation cell also containing a consumable nickel anode and a solution comprising nickel nitrate, having a pH of between 2.0 and 2.8; electrochemically oxidizing the precipitate in caustic formation solution; and repeating the electro-precipitation step at a low current density.
Inventors
- 👤 Nicholas J. Maskalick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:44
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/24; H01M4/32; C; C25; C25D; C25D11/00; C25D11/02; C25D9/00; C25D9/04; C25D9/08; H01M4/26; H01M4/28; H01M4/29; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
183 words
A method of loading porous, flexible, expansible metallic battery plaques with active material comprising the steps of: (a) immersing a porous, flexible, expansible metallic plaque and a consumable nickel electrode in an electrolyte solution comprising nickel nitrate having a pH of between 2.0 and 2.8, and then (b) making the plaque cathodic and the consumable nickel electrode aniodic and supplying sufficient continuous, non-pulsed current to the plaque to provide a current density of between about 20 mA./sq.cm. and 100 mA./sq.cm., to precipitate active material comprising bivalent nickel hydroxide within the plaque pores, and then (c) electrochemically oxidizing the active material in alkaline hydroxide formation solution, and then (d) immersing the plaque containing oxidized active material and a consumable nickel electrode in an electrolyte solution comprising nickel nitrate having a pH of between 2.0 and 2.8, and then (e) making the plaque cathodic and the consumable nickel electrode anodic and supplying sufficient continuous, non-pulsed current to the plaque to provide a current density of between about 2 mA./sq.cm. and 10 mA./sq.cm., to precipitate additional active material comprising bivalent nickel hydroxide within the plaque pores.
Claim 2
Independent Claim
183 words
A method of loading porous, flexible, expansible metallic battery plaques with active material comprising the steps of: (a) immersing a porous, flexible, expansible metallic plaque and a consumable nickel electrode in an electrolyte solution comprising nickel nitrate having a pH of between 2.0 and 2.8, and then (b) making the plaque cathodic and the consumable nickel electrode aniodic and supplying sufficient continuous, non-pulsed current to the plaque to provide a current density of between about 20 mA./sq.cm. and 100 mA./sq.cm., to precipitate active material comprising bivalent nickel hydroxide within the plaque pores, and then (c) electrochemically oxidizing the active material in alkaline hydroxide formation solution, and then (d) immersing the plaque containing oxidized active material and a consumable nickel electrode in an electrolyte solution comprising nickel nitrate having a pH of between 2.0 and 2.8, and then (e) making the plaque cathodic and the consumable nickel electrode anodic and supplying sufficient continuous, non-pulsed current to the plaque to provide a current density of between about 2 mA./sq.cm. and 10 mA./sq.cm., to precipitate additional active material comprising bivalent nickel hydroxide within the plaque pores.
Claim 3
Dependent Claim
41 words
The method of claim 1, wherein the current is supplied in step (b) for a time of between 1/2 hour and 4 hours and the current is supplied in step (e) for a time of between 4 hours and 40 hours.
Claim 4
Dependent Claim
26 words
The method of claim 1, wherein the nickel nitrate electrolyte solution in steps (a) and (d) has a concentration of between about 50% and about 83%.
Claim 5
Dependent Claim
21 words
The method of claim 1, wherein the plaque is washed between steps (b) and (c) and between steps (c) and (d).
Claim 6
Dependent Claim
26 words
The method of claim 1, wherein the plaque comprises metallurgically bonded, metallic fibers, said plaque having a density of between 5% and 25% of theoretical density.
Claim 7
Dependent Claim
20 words
The method of claim 1, wherein the electrolyte solution comprising nickel nitrate is at a temperature below about 30° C.
Claim 8
Dependent Claim
33 words
The method of claim 1, wherein the electrolyte solution in steps (a) and (d) also contains minor amounts of cobalt nitrate, and where cobalt hydroxide is also precipitated in steps (b) and (e).
Claim 9
Dependent Claim
23 words
The method of claim 1, wherein the plaque is flat, and the fibers are between about 0.0002 inch and 0.003 inch in diameter.
Claim 10
Dependent Claim
32 words
The method of claim 1, wherein the alkaline formation solution of step (c) is a 5% to 35% concentrated solution selected from the group consisting of KOH, NaOH, LiOH, and mixtures thereof.
Claim 11
Dependent Claim
46 words
The method of claim 1, wherein the electro-chemical oxidation of step (c) is carried out at a current density of about 5 mA./sq.cm. to 30 mA./sq.cm. to expand the metallic plaque and open pores within the plaque, and where step (c) is repeated after step (e).
References Cited (Backward Citations)
US3214355A
Cited
US3600227A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-28 | 1985-12-28 | 1986-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-28 | 1989-12-28 | 1990-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-28 | 1993-12-28 | 1994-06-29 | $7700.00 | Window Closed / Lapsed |