Composite propellant with differentially cured area at initial burn surface
Assignee: Northrop Grumman Innovation Systems LLC
•
Filing: 1968-12-04
•
Granted: 1982-06-29
•
Expires: 1988-12-04
Abstract
Abstract Composite rocket propellants, in which the base component is a functionally terminated rubber, and case-bonded rocket motors containing same, are provided, wherein cross-link density at, and adjacent at least a portion of the initial propellant burning surface is lower than that throughout the remainder of the propellant to provide greater strain capability at the initial burning surface together with greater propellant strength for higher mass ratio and improved case bonding than possible utilizing a single "compromise" propellant cross-link density of the prior art. Method is provided which involves initially curing the entire propellant mass, alone or as a rocket motor component, to the initial low cross-link density and thereafter applying to said initial burning surface, an interferent capable of interfering with the cure process to substantially stop same, and then again subjecting the entire propellant to curing conditions to cure the remaining curable propellant portion to the higher cross-link density.
Inventors
- 👤 Donald E. Elrick
- 👤 Harry Gilbert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:47
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/68; C08G59/681; C08G59/685; C06; C06B; C06B45/00; C06B45/04; C06B45/06; C06B45/10; C08G59/20; C08G59/32; C08G59/38; C08L; C08L63/00
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
152 words
A process for the manufacture of a cured, rubber base composite rocket propellant having a lower cross-link density at and adjacent at least a portion of its initial burning surface than throughout the remainder of the propellant, which process comprises (a) partially curing in its entirety an uncured composite propellant composition comprising solid oxidizer and a binder system containing a carboxy terminated rubber, hydroxy terminated rubber, mercapto terminated rubber or amine terminated rubber and a curing agent therefor until sufficient cross-linking has occurred to provide a predetermined strain capability at the initial burning surface; (b) applying to at least a portion of said initial burning surface sufficient of a monofunctional interferrent material reactive with said binder system to prevent further curing from occurring at said surface; and (c) then completing the cure of said propellant composition whereby the cross-link density and strength of the remaining curable portion of the propellant has increased.
Claim 2
Dependent Claim
152 words
A process for the manufacture of a cured, rubber base composite rocket propellant having a lower cross-link density at and adjacent at least a portion of its initial burning surface than throughout the remainder of the propellant, which process comprises (a) partially curing in its entirety an uncured composite propellant composition comprising solid oxidizer and a binder system containing a carboxy terminated rubber, hydroxy terminated rubber, mercapto terminated rubber or amine terminated rubber and a curing agent therefor until sufficient cross-linking has occurred to provide a predetermined strain capability at the initial burning surface; (b) applying to at least a portion of said initial burning surface sufficient of a monofunctional interferrent material reactive with said binder system to prevent further curing from occurring at said surface; and (c) then completing the cure of said propellant composition whereby the cross-link density and strength of the remaining curable portion of the propellant has increased.
Claim 3
Dependent Claim
84 words
The process of claim 1 wherein the partial curing step (a) imparts to the propellant at the initial burning surface a modulus of from 200 to 600 psi and an elongation at maximum stress of 40 to 100 percent, and the final curing step (c) imparts to the remainder of the propellant a modulus of from 400 to 2000 psi and an elongation at maximum stress of from 15 to 40 percent, each of said modulus and said elongation being measured at 77° F.
Claim 4
Dependent Claim
35 words
The process of claim 2 wherein the composite propellant contains on a weight basis from 70 to 90 percent of ammonium perchlorate, 5 to 10 percent of particulate aluminum and 5 to 20 percent binder.
Claim 5
Dependent Claim
55 words
The process of claim 3 wherein the binder system contains a carboxy terminated polybutadiene and, as curing agent therefor, a mixture of diepoxides and triepoxides in a diepoxide/triepoxide mole ratio of 15:1 to 1:1, the mole ratio of epoxy groups to carboxy groups in said binder being within the range of from 0.9:1 to 2:1.
Claim 6
Dependent Claim
14 words
The cured rubber base composite rocket propellant produced by the process of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-28 | 1985-12-28 | 1986-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-28 | 1989-12-28 | 1990-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-28 | 1993-12-28 | 1994-06-29 | $7700.00 | Window Closed / Lapsed |