Composition for drawn film, cold drawn film made of said composition and process for manufacture of said film
Assignee: Asahi Kasei Corp
•
Filing: 1981-07-17
•
Granted: 1982-06-22
•
Expires: 2001-07-17
Abstract
Abstract A composition for shrinkable film which excels in heat-sealability, transparency, strength, and particularly low-temperature quick shrinking property and, therefore, suits production chiefly of packaging materials, a film made of the composition and a process for the manufacture of the film are disclosed. Specifically, the composition comprises one of the specific combinations of components (A), (B) and (C), i.e. the combinations of (A)+(B), (B)+(C) and (A)+(B)+(C), wherein (A) is non-rigid polyolefine resins such as ethylene vinyl acetate, (B) is an elastomer comprising a specific ethylene-α-olefin copolymer, and (C) is rigid polyolefin resins such as polypropylene. The packaging film excelling particularly in optical property, mechanical strength and low-temperature shrinking property is obtained by converting a homogeneous blend of the aforementioned composition, either in its crosslinked form or in its non-crosslinked form, into a tubular raw film, which is stretched at a temperature low enough for imparting a high orientation to the film. The process for the manufacture of this packaging film is also disclosed.
Inventors
- 👤 Isao Yoshimura
- 👤 Hideo Hata
- 👤 Takashi Kaneko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 18:58
CPC Classifications
B; B29; B29C; B29C61/00; B29C61/003; C; C08; C08L; C08L23/00; C08L23/02; B29C48/00; B29C48/001; B29C48/0018; B29C48/0019; B29C48/0022; B29C48/03; B29C48/09; B29C48/10; C08L23/04; C08L23/08; C08L23/0846; C08L23/0853; C08L23/10; C08L23/16
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
181 words
A process for the manufacture of a cold drawn film having a tensile strength of not less that 5.00 kglmm2 and a haze of not more than 4.0%, which comprises mixing the specific combination of components, of (B)+(C),: wherein (B) is an elastomer having a density of not more than 0.91 g/cm 3 and made of an ethylene-α-olefin copolymer, and (C) is at least one selected from the group consisting of crystalline polypropylene, high-density polyethylene and crystalline polybutene-1, extruding the resultant blend through an annular die to produce a tubular sheet, suddenly solidifying the tubular sheet by means of a liquid refrigerant, passing the tubular sheet through two pairs of nip rollers and heating the sheet to a temperature of not exceeding 110° C., and then stretching the film at a cold stretching temperature in the range of from 20° to 100° C. while introducing air into the tubular sheet interior under pressure for thereby effecting cold orientation of the sheet into a film at an area stretching ratio in the range of from 5 to 30 times the original dimension.
Claim 2
Dependent Claim
181 words
A process for the manufacture of a cold drawn film having a tensile strength of not less that 5.00 kglmm2 and a haze of not more than 4.0%, which comprises mixing the specific combination of components, of (B)+(C),: wherein (B) is an elastomer having a density of not more than 0.91 g/cm 3 and made of an ethylene-α-olefin copolymer, and (C) is at least one selected from the group consisting of crystalline polypropylene, high-density polyethylene and crystalline polybutene-1, extruding the resultant blend through an annular die to produce a tubular sheet, suddenly solidifying the tubular sheet by means of a liquid refrigerant, passing the tubular sheet through two pairs of nip rollers and heating the sheet to a temperature of not exceeding 110° C., and then stretching the film at a cold stretching temperature in the range of from 20° to 100° C. while introducing air into the tubular sheet interior under pressure for thereby effecting cold orientation of the sheet into a film at an area stretching ratio in the range of from 5 to 30 times the original dimension.
Claim 3
Dependent Claim
22 words
The process according to claim 1, wherein the solidified tubular sheet is irradiated with high-energy ray before passing through the nip rolls.
Claim 4
Dependent Claim
30 words
The process according to claim 1, wherein the component (B) is a copolymer having an ethylene group content of not more than 90 mol% and not less than 20 mol%.
Claim 5
Dependent Claim
30 words
The process according to claim 1, wherein the component (B) is a copolymer having an ethylene group content of not more than 90 mol% and not less than 40 mol%.
Claim 6
Dependent Claim
62 words
The process according to claim 1, wherein the elastomer as the component (B) is a non-rigid copolymer having a Vicat softening point of not more than 80° C. and a degree of crystallization of not more than 30%, wherein the α-olefin component contained therein is at least one selected from the group consisting of α-olefins having from 3 to 12 carbon atoms.
Claim 7
Dependent Claim
33 words
The process according to claim 5, wherein the elastomer as the component (B) is a random copolymer wherein the α-olefin component contained therein is selected from the group consisting of propylene and butene-1.
Claim 8
Dependent Claim
28 words
The process according to claim 1, wherein the ethylene-α-olefin copolymer as the component (B) has a polyene copolymerized in addition to the main components of ethylene and α-olefin.
Claim 9
Dependent Claim
29 words
The process according to claim 7, wherein the polyene contains not more than 5 mol% of a non-conjugate diene selected from the group consisting of hexadiene and norbornene derivatives.
Claim 10
Dependent Claim
25 words
The process according to claim 1, wherein the component (C) is a rigid polymer having a Vicat softening point of not less than 100° C.
Claim 11
Dependent Claim
41 words
The process according to claim 1 wherein the component (C) is one selected from the group consisting of a crystalline polypropylene, a crystalline copolymer of propylene with ethylene contained in an amount of not more than 10 mol% and combinations thereof.
Claim 12
Dependent Claim
25 words
The process according to claim 1, wherein the components of the composition are in amounts such as to satisfy 0.90≧B/(B+C)≧0.30 in terms of weight ratio.
Claim 13
Dependent Claim
25 words
The process according to claim 1, wherein the components of the composition are in amount such as to satisfy 0.87≧B/(B)+(C)≧0.40 in terms of weight ratio.
Claim 14
Dependent Claim
50 words
The process according to claim 2, wherein the irradiation of the film with the high-energy ray is conducted so as to cause the film to acquire an insoluble gel content of from 60 to nearly 0% by weight in boiling xylene and a melt index of not more than 1.0.
Claim 15
Dependent Claim
50 words
The process according to claim 2, wherein the irradiation of the film with the high-energy ray is conducted so as to cause the film to acquire an insoluble gel content of from 40 to nearly 0% by weight in boiling xylene and a melt index of not more than 0.5.
Claim 16
Dependent Claim
39 words
The process according to claim 1, wherein the tubular sheet is heated at a temperature not exceeding the melting point of the main crystalline polymer and the stretching temperature is in the range of from 30° to 90° C.
Claim 17
Dependent Claim
20 words
The process according to claim 1, wherein the stretching temperature is in the range of from 30° to 80° C.
Claim 18
Dependent Claim
28 words
The process according to claim 1, wherein the stretching temperature is not higher than the Vicat softening point of the mixed composition of which the film is made.
Claim 19
Dependent Claim
24 words
The process according to claim 1, wherein the area stretching ratio is in the range of from 7 to 25 times the original dimension.
Claim 20
Dependent Claim
24 words
The process according to claim 1, wherein the transverse stretching ratio is in the range of from 2 to 7 times the original dimension.
Claim 21
Dependent Claim
26 words
The process according to claim 1, wherein the molten mixture is co-extruded with other resins and the resultant tubular sheet is subjected to the cold orientation.
Claim 22
Dependent Claim
31 words
The process according to claim 20, wherein said other resins are selected from the group consisting of polyvinylidene chloride, copolymers of polyvinylidene chloride with other monomers, polyamides, polyesters and other polyolefins.
References Cited (Backward Citations)
GB924243A
Cited
GB1046254A
Cited
US3412189A
Cited
GB992897A
Cited
GB1037819A
Cited
US3299194A
Cited
GB1163053A
Cited
GB1224035A
Cited
GB1402049A
Cited
GB1523447A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-21 | 1985-12-21 | 1986-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-21 | 1989-12-21 | 1990-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-21 | 1993-12-21 | 1994-06-22 | $7700.00 | Window Closed / Lapsed |