Process for preparing polymeric polyblends having a rubber phase as particles with a bimodal particle size distribution
Assignee: Monsanto Co
•
Filing: 1981-03-23
•
Granted: 1982-06-08
•
Expires: 2001-03-23
Abstract
Abstract This invention relates to a method for preparing improved monoalkenyl aromatic polyblends having a dispersed rubber phase as rubber particles having a bimodal particle size distribution and compositions thereof.
Inventors
- 👤 Carl R. Dupre
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 06:17
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
328 words
A continuous mass polymerization for preparing monoalkenyl aromatic polyblends having a dispersed rubber phase as rubber particles having a bimodal rubber particle size distribution comprising, A. continuously mass polymerizing a first solution of an alkenyl aromatic monomer having dissolved therein about 2 to 15% by weight of a first diene rubber in a first reaction zone to a conversion of about 10 to 40% forming a partially polymerized first solution with said first diene rubber being dispersed as rubber particles having an average diameter of about 0.1 to 1.0 microns, B. continuously feeding said partially polymerized first solution to a second reaction zone in series with said first reaction zone, simultaneously with a second solution of a monoalkenyl aromatic monomer having dissolved therein about 2 to 15% by weight of a second diene rubber, forming a partially polymerized second solution, C. continuously mass polymerizing said partially polymerized second solution in said second reaction zone to a conversion of about 20 to 50% forming a partially polymerized third solution having the second diene rubber dispersed as rubber particles having an average diameter of about 2 to 5 microns, D. continuously mass polymerizing said third solution in a third reaction zone to a conversion of about 60 to 95%, E. continuously removing an effluent from said third reaction zone and separating said polyblend from said effluent, said polyblend having a polyalkenyl aromatic polymer as a matrix polymer with said first diene rubber dispersed as rubber particles having a average diameter of about 0.1 to 1.0 microns and said second diene rubber dispersed as rubber particles having an average diameter of about 2 to 5 microns providing said polyblend with a rubber phase having said bimodal particle size distribution, wherein about 70-95% of the rubber particles have a particle size of about 0.5 to 1.0 microns and 5 to 30% of the rubber particles have a particle size of about 2.0 to 5.0 microns, said polyblend having superior toughness and gloss.
Claim 2
Dependent Claim
328 words
A continuous mass polymerization for preparing monoalkenyl aromatic polyblends having a dispersed rubber phase as rubber particles having a bimodal rubber particle size distribution comprising, A. continuously mass polymerizing a first solution of an alkenyl aromatic monomer having dissolved therein about 2 to 15% by weight of a first diene rubber in a first reaction zone to a conversion of about 10 to 40% forming a partially polymerized first solution with said first diene rubber being dispersed as rubber particles having an average diameter of about 0.1 to 1.0 microns, B. continuously feeding said partially polymerized first solution to a second reaction zone in series with said first reaction zone, simultaneously with a second solution of a monoalkenyl aromatic monomer having dissolved therein about 2 to 15% by weight of a second diene rubber, forming a partially polymerized second solution, C. continuously mass polymerizing said partially polymerized second solution in said second reaction zone to a conversion of about 20 to 50% forming a partially polymerized third solution having the second diene rubber dispersed as rubber particles having an average diameter of about 2 to 5 microns, D. continuously mass polymerizing said third solution in a third reaction zone to a conversion of about 60 to 95%, E. continuously removing an effluent from said third reaction zone and separating said polyblend from said effluent, said polyblend having a polyalkenyl aromatic polymer as a matrix polymer with said first diene rubber dispersed as rubber particles having a average diameter of about 0.1 to 1.0 microns and said second diene rubber dispersed as rubber particles having an average diameter of about 2 to 5 microns providing said polyblend with a rubber phase having said bimodal particle size distribution, wherein about 70-95% of the rubber particles have a particle size of about 0.5 to 1.0 microns and 5 to 30% of the rubber particles have a particle size of about 2.0 to 5.0 microns, said polyblend having superior toughness and gloss.
Claim 3
Dependent Claim
37 words
A method of claim 1 wherein said polyblend has dispersed rubber particles, said particles being grafted with and having occluded said polyalkenyl aromatic polymer in an amount of about 0.5 to 5 parts per part of rubber.
Claim 4
Dependent Claim
30 words
A method of claim 1 wherein said rubber is a diene rubber selected from the group consisting of polybutadiene, polypentenomer, polychloroprene copolymers of butadiene-styrene, butadiene-acrylonitrile, chloroprene-styrene, chloroprene-acrylonitrile and mixtures thereof.
Claim 5
Dependent Claim
10 words
A method of claim 3 wherein said rubber is polybutadiene.
Claim 6
Dependent Claim
26 words
A method of claim 4 wherein said polybutadiene has a cis-isomer content of 30 to 98% and a Tg of about -50° C. to -105° C.
Claim 7
Dependent Claim
27 words
A method of claim 1 wherein said monoalkenyl aromatic monomer is selected from the group consisting of styrene, a-methylstyrene, chlorostyrene, dichlorostyrene, bromostyrene, and dibromostyrene and mixtures thereof.
Claim 8
Dependent Claim
30 words
A method of claim 1 wherein said monoalkenyl aromatic polymer has an average molecular weight of 40,000 to 70,000 Staudinger and a molecular weight dispersion index of 2.2 to 3.5.
Claim 9
Dependent Claim
20 words
A method of claim 1 wherein said rubber particles are crosslinked having a swelling index of about 7 to 30.
Claim 10
Dependent Claim
43 words
A method of claim 1 wherein step (A) is carried out at temperatures of about 110° to 140° C., with shearing agitation sufficient to size and disperse said diene rubber as rubber particles having an average diameter of about 0.1 to 1.0 microns.
Claim 11
Dependent Claim
23 words
A method of claim 9 wherein said shearing agitation is carried out at an agitator tip speed of about 675 to 2600 ft./min.
Claim 12
Dependent Claim
42 words
A method of claim 1 wherein step (C) is carried out at temperatures of 130° to 150° C., with shearing agitation sufficient to size and disperse said second diene rubber as rubber particles having an average diameter of 2 to 5 microns.
Claim 13
Dependent Claim
17 words
A method of claim 11 wherein said shearing agitator tip speed of about 100 to 300 ft./min.
Claim 14
Dependent Claim
42 words
A process of claim 1 wherein step (B) is carried out such that 70 to 95 parts of said first partially polymerized solution is mixed with about 5 to 30 parts of said second solution to form said second partially polymerized solution.
Claim 15
Dependent Claim
210 words
A process of claim 1 wherein step (D) is carried out by charging continuously said third partially polymerized solution to a first stage of a continuous staged isobaric stirred reaction zone having a plurality of stages so as to produce substantially linear flow through said stages downstream to a final stage, each of said stages operating at substantially constant gravimetric fillage of from about 15 to 90% of its volume of said polymerizing third partially polymerized solution, maintaining conditions in said continuous staged isobaric stirred reaction zone as said third reaction zone so as to polymerize said third partially polymerized solution by progressive multistage substantially linear flow polymerization, all said stages operating with shearing agitation and common evaporative vapor phase cooling under isobaric condition in said third zone, providing each said stage with steady state polymerization at a controlled temperature of from 130° to 180° C. with a pressure of from about 7 to 28 psia and interfacial liquid contact stage to stage establishing a pressure gradient from the first stage downstream to the final stage causing substantially linear flow through said third zone, each said stage operating at a predetermined higher conversion level to a conversion of 60 to 95% in said final stage of said third reaction zone.
Claim 16
Dependent Claim
46 words
A process of claim 1 wherein step (E) is carried out by continuously heating the effluent from the third reaction zone to about 180° to 250° C. for a time sufficient to crosslink said rubber phase moiety to a swelling index of about 7 to 30.
Claim 17
Dependent Claim
73 words
A process of claim 1 wherein the separating of (E) step is carried out continuously in a devolatilizer operating below atmospheric pressure at a temperature of about 180° to 250° C. to provide said polyblend having a bimodal rubber particle size distribution where 70-95% of the rubber particles have a particle size of 0.5 to 1.0 microns and 5 to 30% of the rubber particles have a particle size of 2.0 to 5.0.
Claim 18
Dependent Claim
42 words
A process of claim 1 wherein the polymerization carried out in step (A) and step (C) is such that said first and second solutions have present about 0.001 to 3.0% by weight of a free radial generating catalyst based on said monomers.
Claim 19
Dependent Claim
37 words
A process of claim 17 wherein said free radical catalyst is selected from the group consisting of di-tert-butyl peroxide, tert-butyl peracetate, benzoyl peroxide, lauroyl peroxide, tert-butyl perbenzoate, dicumyl peroxide, tert-butyl peroxide and isopropyl carbonate or mixtures thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-07 | 1985-12-07 | 1986-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-07 | 1989-12-07 | 1990-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-07 | 1993-12-07 | 1994-06-08 | $7700.00 | Window Closed / Lapsed |