Molding articles of thermoplastic rubber
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1980-05-16
•
Granted: 1982-06-08
•
Expires: 2000-05-16
Abstract
Abstract Articles having a relatively smooth and homogeneous surface appearance may be injection molded of thermoplastic rubber on relatively low-injection-speed-and-pressure equipment. To reduce or eliminate the hairy or frosted surface appearance which otherwise commonly occurs, the mold cavity is pressurized with a relatively moisture-free compressed gas before and during a majority of the injection phase of the molding cycle.
Inventors
- 👤 Gerald T. Young
- 👤 Michael R. Easterling
- 👤 Robert E. Dukeshire
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:43
CPC Classifications
B; B29; B29C; B29C45/00; B29C45/17; B29C45/1703
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
168 words
A method for providing a relatively smooth surface to an injection molded article of thermoplastic rubber comprising: (a) providing a source of relatively moisture-free pressurized gas and a cold mold that when closed defines a sealed mold cavity; (b) pressurizing the mold cavity with the relatively moisture-free gas prior to and during low pressure and speed injection of molten thermoplastic rubber into the mold cavity, the pressure of the gas being at least 50 pounds per square inch gauge but less than the pressure of the molten thermoplastic rubber as it is injected into the mold cavity; (c) maintaining said gas pressurization while injecting molten thermoplastic rubber into said mold cavity; (d) terminating the source of said gas pressurization about 1 to 2 seconds prior to completion of filling of the mold cavity with thermoplastic rubber; (e) completing filling of the mold cavity with thermoplastic rubber; and (f) allowing the thermoplastic rubber to solidify, then opening the mold and removing the thermoplastic rubber article from the mold cavity.
Claim 2
Independent Claim
168 words
A method for providing a relatively smooth surface to an injection molded article of thermoplastic rubber comprising: (a) providing a source of relatively moisture-free pressurized gas and a cold mold that when closed defines a sealed mold cavity; (b) pressurizing the mold cavity with the relatively moisture-free gas prior to and during low pressure and speed injection of molten thermoplastic rubber into the mold cavity, the pressure of the gas being at least 50 pounds per square inch gauge but less than the pressure of the molten thermoplastic rubber as it is injected into the mold cavity; (c) maintaining said gas pressurization while injecting molten thermoplastic rubber into said mold cavity; (d) terminating the source of said gas pressurization about 1 to 2 seconds prior to completion of filling of the mold cavity with thermoplastic rubber; (e) completing filling of the mold cavity with thermoplastic rubber; and (f) allowing the thermoplastic rubber to solidify, then opening the mold and removing the thermoplastic rubber article from the mold cavity.
Claim 3
Dependent Claim
39 words
The method of claim 1 wherein the thermoplastic rubber is a block polymer of styrene butadiene rubber, and the mold cavity has a temperature from about 65° F. to about 95° F. at the beginning of the molding cycle.
Claim 4
Independent Claim
162 words
A method of molding an article of thermoplastic rubber by low pressure and rate injection of a mass of molten thermoplastic rubber into a cold mold that defines a sealed mold cavity when closed comprising the following sequence of steps: (a) closing the mold to define a sealed mold cavity; (b) providing a source of compressed gas; (c) pressurizing the mold cavity with a compressed gas from the source of compressed gas; (d) beginning injection of molten thermoplastic rubber into the mold cavity while maintaining pressurization of the mold cavity with said compressed gas; (e) terminating the source of gas pressurization of the mold cavity shortly before completing injection of the molten thermoplastic rubber into the mold cavity; (f) completing injection of the molten thermoplastic rubber into the mold cavity; (g) allowing the thermoplastic rubber to cool and solidify into an article in the mold cavity; and (h) opening the mold and removing the solidified thermoplastic rubber article from the mold cavity.
Claim 5
Independent Claim
162 words
A method of molding an article of thermoplastic rubber by low pressure and rate injection of a mass of molten thermoplastic rubber into a cold mold that defines a sealed mold cavity when closed comprising the following sequence of steps: (a) closing the mold to define a sealed mold cavity; (b) providing a source of compressed gas; (c) pressurizing the mold cavity with a compressed gas from the source of compressed gas; (d) beginning injection of molten thermoplastic rubber into the mold cavity while maintaining pressurization of the mold cavity with said compressed gas; (e) terminating the source of gas pressurization of the mold cavity shortly before completing injection of the molten thermoplastic rubber into the mold cavity; (f) completing injection of the molten thermoplastic rubber into the mold cavity; (g) allowing the thermoplastic rubber to cool and solidify into an article in the mold cavity; and (h) opening the mold and removing the solidified thermoplastic rubber article from the mold cavity.
Claim 6
Dependent Claim
14 words
The method of claim 3 wherein the gas is relatively moisture free compressed air.
Claim 7
Dependent Claim
69 words
The method of claim 3 wherein gas pressurization of the mold cavity begins just prior to injection of the molten thermoplastic rubber into the mold cavity, injection of the thermoplastic rubber continues over a period of about 10 to 18 seconds, and termination of gas pressurization of the mold cavity occurs about 1 to 2 seconds prior to completion of injection of the thermoplastic rubber into the mold cavity.
Claim 8
Dependent Claim
29 words
The method of claim 3 wherein the mold cavity is pressurized via an orifice separate from that through which the molten thermoplastic rubber is injected into the mold cavity.
Claim 9
Dependent Claim
22 words
The method of claim 3 wherein the pressure of the gas is from about 50 to 100 pounds per square inch gauge.
Claim 10
Dependent Claim
37 words
The method of claim 3 wherein the pressure of the gas is at least 75 pounds per square inch gauge and less than the pressure with which the molten thermoplastic rubber is injected into the mold cavity.
References Cited (Backward Citations)
US3044118A
Cited
US3789093A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-07 | 1985-12-07 | 1986-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-07 | 1989-12-07 | 1990-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-07 | 1993-12-07 | 1994-06-08 | $7700.00 | Window Closed / Lapsed |