Sand-blasting abrasive materials and method of producing the same

Claim 1

A method of producing pulverized abrasive materials for sand blasting, comprising the steps of: carrying out a first phase by adding two parts of a thermosetting resin, to which one part of a setting catalyst has been added, to 100 parts of a pulverized material of grade No. 4, selected from the group that consists of silica sand and slag; uniformly mixing them while blowing heated air thereinto at about 80° to 100° C., constituting a first heat treatment, so as to coat the resulting pulverized sand-blasting abrasive material with the resin in a fixed thickness, to dry and to thermally set the resin coating on the abrasive material; and carrying out a second, separate phase by a subsequent re-heating treatment at about 300° C. while stirring up, so as to change chemically the resin coating, obtained on the abrasive material in the first heat treatment, and to render the coating unsoluble and unmeltable while leaving the abrasive material in the pulverized condition; the coating increasing the strength of the abrasive material by penetrating into cracks inherent in the abrasive material so that a substantial proportion of the pulverized abrasive material can be recovered after the sand blasting for re-use; whereby the heat, generated by impact when the abrasive material is blown against a surface, to be cleaned by the sand blasting, leaves the unsoluble and unmeltable coating in this state, and actually continues the setting of that coating so that sand-blasting efficiency is increased; and whereby dust formation during the sand blasting is reduced, thereby increasing environmental protection.

Claim 2

A method of producing pulverized abrasive materials for sand blasting, comprising the steps of: carrying out a first phase by adding two parts of a thermosetting resin, to which one part of a setting catalyst has been added, to 100 parts of a pulverized material of grade No. 4, selected from the group that consists of silica sand and slag; uniformly mixing them while blowing heated air thereinto at about 80° to 100° C., constituting a first heat treatment, so as to coat the resulting pulverized sand-blasting abrasive material with the resin in a fixed thickness, to dry and to thermally set the resin coating on the abrasive material; and carrying out a second, separate phase by a subsequent re-heating treatment at about 300° C. while stirring up, so as to change chemically the resin coating, obtained on the abrasive material in the first heat treatment, and to render the coating unsoluble and unmeltable while leaving the abrasive material in the pulverized condition; the coating increasing the strength of the abrasive material by penetrating into cracks inherent in the abrasive material so that a substantial proportion of the pulverized abrasive material can be recovered after the sand blasting for re-use; whereby the heat, generated by impact when the abrasive material is blown against a surface, to be cleaned by the sand blasting, leaves the unsoluble and unmeltable coating in this state, and actually continues the setting of that coating so that sand-blasting efficiency is increased; and whereby dust formation during the sand blasting is reduced, thereby increasing environmental protection.