Blend of a carboxylated copolymer latex and of an acrylate copolymer latex for coating rubber and product

Claim 1

The method which comprises coating a hot, sticky rubber compound with a heat sensitized aqueous polymer composition comprising a blend of two latices, drying said coated rubber compound until at least 80% of the water has evaporated to form a gelled, non-tacky, water resistant and adherent polymeric coating from said composition on said rubber compound, cooling said coated rubber compound with water and drying the same to a temperature sufficiently low to prevent scorch of said rubber compound and stacking said coated rubber compound to provide layers of said rubber compound which do not stick together, (A) the polymer of one of said latices of said composition comprising a carboxylated copolymer of (1) at least 45% by weight of a monomer selected from the group consisting of styrene, vinyl toluene, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, methyl methacrylate and ethyl methacrylate and mixtures thereof, (2) a copolymerizable monomer selected from the group consisting of acrylic acid, methacrylic acid, ethacrylic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, sorbic acid and crotonic acid and mixtures thereof in an amount of up to 10% by weight and (3) the balance, in an amount sufficient to provide some flexibility to and for vulcanization of said copolymer, a copolymerizable monomer selected from the group consisting of butadiene-1,3, isoprene, 2,3-dimethyl-butadiene-1,3 and piperylene and mixtures thereof, said copolymer of (A) having a glass transition temperature of not less than about -30° C.; and (B) the polymer of the other of said latices of said composition consisting essentially of a copolymer of (1) from about 50 to 70% by weight of at least one acrylate selected from the group consisting of methyl acrylate and ethyl acrylate, (2) from about 25 to 40% by weight of at least one alkacrylate selected from the group consisting of methyl methacrylate, ethyl methacrylate and methyl ethacrylate and (3) from about 3 to 7% by weight of acrylamide, said copolymer of (B) having a glass transition temperature of not less than about +30° C., the parts by weight ratio of the copolymer of (A) to the copolymer of (B) being from about 50:50 to 85:15 on a dry weight basis.

Claim 2

The method which comprises coating a hot, sticky rubber compound with a heat sensitized aqueous polymer composition comprising a blend of two latices, drying said coated rubber compound until at least 80% of the water has evaporated to form a gelled, non-tacky, water resistant and adherent polymeric coating from said composition on said rubber compound, cooling said coated rubber compound with water and drying the same to a temperature sufficiently low to prevent scorch of said rubber compound and stacking said coated rubber compound to provide layers of said rubber compound which do not stick together, (A) the polymer of one of said latices of said composition comprising a carboxylated copolymer of (1) at least 45% by weight of a monomer selected from the group consisting of styrene, vinyl toluene, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, methyl methacrylate and ethyl methacrylate and mixtures thereof, (2) a copolymerizable monomer selected from the group consisting of acrylic acid, methacrylic acid, ethacrylic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, sorbic acid and crotonic acid and mixtures thereof in an amount of up to 10% by weight and (3) the balance, in an amount sufficient to provide some flexibility to and for vulcanization of said copolymer, a copolymerizable monomer selected from the group consisting of butadiene-1,3, isoprene, 2,3-dimethyl-butadiene-1,3 and piperylene and mixtures thereof, said copolymer of (A) having a glass transition temperature of not less than about -30° C.; and (B) the polymer of the other of said latices of said composition consisting essentially of a copolymer of (1) from about 50 to 70% by weight of at least one acrylate selected from the group consisting of methyl acrylate and ethyl acrylate, (2) from about 25 to 40% by weight of at least one alkacrylate selected from the group consisting of methyl methacrylate, ethyl methacrylate and methyl ethacrylate and (3) from about 3 to 7% by weight of acrylamide, said copolymer of (B) having a glass transition temperature of not less than about +30° C., the parts by weight ratio of the copolymer of (A) to the copolymer of (B) being from about 50:50 to 85:15 on a dry weight basis.

Claim 3

The method which comprises coating a hot, milled sticky rubber compound with a heat sensitized aqueous compounded polymer composition comprising a blend of two latices, drying said coated rubber compound to form a gelled, non-tacky, water resistant and adherent polymeric coating from said composition on said rubber compound, the amount of said coating being not over about 7% by weight of said rubber compound, cooling said coated rubber compound with water and drying the same to a temperature not above about 50° C., and stacking said coated rubber compound to provide layers of said rubber compound which do not stick together, (A) the polymer of one of said latices of said composition comprising a carboxylated copolymer of (1) at least 45% by weight of a monomer selected from the group consisting of styrene, vinyl toluene, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, methyl methacrylate and ethyl methacrylate and mixtures thereof, (2) a copolymerizable monomer selected from the group consisting of acrylic acid, methacrylic acid, ethacrylic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, sorbic acid and crotonic acid and mixtures thereof in an amount of up to 10% by weight and (3) the balance, in an amount sufficient to provide some flexibility to and for vulcanization of said copolymer, a copolymerizable monomer selected from the group consisting of butadiene-1,3, isoprene, 2,3-dimethyl-butadiene-1,3 and piperylene and mixtures thereof, said copolymer of (A) having a glass transition temperature of not less than about -30° C., and (B) the polymer of the other of said latices of said composition consisting essentially of a copolymer of (1) from about 50 to 70% by weight of at least one acrylate selected from the group consisting of methyl acrylate and ethyl acrylate, (2) from about 25 to 40% by weight of at least one alkacrylate selected from the group consisting of methyl methacrylate, ethyl methacrylate and methyl ethacrylate and (3) from about 3 to 7% by weight of acrylamide, said copolymer of (B) having a glass transition temperature of not less than about +30° C., the parts by weight ratio of the copolymer of (A) to the copolymer of (B) being from about 50:50 to 85:15 on a dry weight basis, said compounded polymer composition containing, based on 100 parts by weight total dry of the copolymer of (A) and the copolymer of (B), from about 100 to 1000 parts by weight of inorganic, non-black rubber compounding pigments, from about 1 to 30 parts by weight of stabilizers and wetting agents, from about 0.75 to 15 parts by weight of a heat sensitizer and from about 0.25 to 1.75 parts by weight of a chelating agent, and the total solids content of said composition being from about 7 to 75% by weight.

Claim 4

The method which comprises coating a hot, milled sticky rubber compound with a heat sensitized aqueous compounded polymer composition comprising a blend of two latices, drying said coated rubber compound to form a gelled, non-tacky, water resistant and adherent polymeric coating from said composition on said rubber compound, the amount of said coating being not over about 7% by weight of said rubber compound, cooling said coated rubber compound with water and drying the same to a temperature not above about 50° C., and stacking said coated rubber compound to provide layers of said rubber compound which do not stick together, (A) the polymer of one of said latices of said composition comprising a carboxylated copolymer of (1) at least 45% by weight of a monomer selected from the group consisting of styrene, vinyl toluene, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, methyl methacrylate and ethyl methacrylate and mixtures thereof, (2) a copolymerizable monomer selected from the group consisting of acrylic acid, methacrylic acid, ethacrylic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, sorbic acid and crotonic acid and mixtures thereof in an amount of up to 10% by weight and (3) the balance, in an amount sufficient to provide some flexibility to and for vulcanization of said copolymer, a copolymerizable monomer selected from the group consisting of butadiene-1,3, isoprene, 2,3-dimethyl-butadiene-1,3 and piperylene and mixtures thereof, said copolymer of (A) having a glass transition temperature of not less than about -30° C., and (B) the polymer of the other of said latices of said composition consisting essentially of a copolymer of (1) from about 50 to 70% by weight of at least one acrylate selected from the group consisting of methyl acrylate and ethyl acrylate, (2) from about 25 to 40% by weight of at least one alkacrylate selected from the group consisting of methyl methacrylate, ethyl methacrylate and methyl ethacrylate and (3) from about 3 to 7% by weight of acrylamide, said copolymer of (B) having a glass transition temperature of not less than about +30° C., the parts by weight ratio of the copolymer of (A) to the copolymer of (B) being from about 50:50 to 85:15 on a dry weight basis, said compounded polymer composition containing, based on 100 parts by weight total dry of the copolymer of (A) and the copolymer of (B), from about 100 to 1000 parts by weight of inorganic, non-black rubber compounding pigments, from about 1 to 30 parts by weight of stabilizers and wetting agents, from about 0.75 to 15 parts by weight of a heat sensitizer and from about 0.25 to 1.75 parts by weight of a chelating agent, and the total solids content of said composition being from about 7 to 75% by weight.