Method of forming a urethane prepolymer and its use in consolidating aggregate material
Assignee: GRAVI-MECHANICS Co A CORP OF ILL
•
Filing: 1981-05-08
•
Granted: 1982-05-11
•
Expires: 2001-05-08
Abstract
Abstract A method of forming a hydrophilic urethane prepolymer useful in consolidating aggregate material comprises the steps of adding an isocyanate compound to a hydrophilic polyether or polyester compound which has been heated to such a temperature that the temperature of the reactants after addition of isocyanate is at least as high as about 120° C. The resulting urethane prepolymer may be reacted with an aqueous slurry of unconsolidated aggregate material, such as peat, to form a consolidated aggregate product, such as a plant growth-supporting rooting medium.
Inventors
- 👤 Richard R. Dedolph
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:26
CPC Classifications
C; C09; C09K; C09K17/00; C09K17/14; C09K17/18; C09K17/30; A; A01; A01G; A01G24/00; A01G24/20; A01G24/28; A01G24/30; A01G24/40; A01G24/42; A01G24/48; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G2310/00; Y; Y10; Y10S; Y10S521/00; Y10S521/905; Y10S528/00; Y10S528/903; Y10S528/904
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
139 words
A method of consolidating aggregate material to form an integral, resilient, water-permeable mass, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with excess isocyanate groups in said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 2
Independent Claim
139 words
A method of consolidating aggregate material to form an integral, resilient, water-permeable mass, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with excess isocyanate groups in said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 3
Dependent Claim
35 words
The method of claim 1 wherein said polyether or polyester compound is heated to a temperature sufficient to drive off any water therein prior to adding said isocyanate compound to said polyether or polyester compound.
Claim 4
Dependent Claim
45 words
The method of claim 2 wherein said polyether or polyester compound comprises polyethylene glycol (PEG) having a molecular weight of between about 1000 and 3000, and said PEG is heated to at least about 175° C. before said isocyanate compound is added to said PEG.
Claim 5
Dependent Claim
37 words
The method of claim 3 wherein said isocyanate compound comprises tolylene diisocyanate and said heated PEG is allowed to cool to between about 120° C. and 235° C. before said tolylene diisocyanate is added to said PEG.
Claim 6
Independent Claim
188 words
A method of consolidating aggregate material to form an integral, resilient, water-permeable mass, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate are formed; (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with excess isocyanate groups in said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 7
Independent Claim
188 words
A method of consolidating aggregate material to form an integral, resilient, water-permeable mass, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate are formed; (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with excess isocyanate groups in said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 8
Dependent Claim
42 words
The method of claim 5 wherein the surface area of the interface between said polyether or polyester layer and said isocyanate layer is controlled in order to control the rate of reaction between said isocyanate compound and said polyether or polyester compound.
Claim 9
Dependent Claim
12 words
The product of the method of claim 2, 3, 4 or 6.
Claim 10
Independent Claim
95 words
A method of forming a hydrophilic urethane prepolymer, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; and, (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer.
Claim 11
Independent Claim
95 words
A method of forming a hydrophilic urethane prepolymer, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; and, (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer.
Claim 12
Dependent Claim
34 words
The method of claim 8 wherein said polyester or polyether compound is heated to a temperature sufficient to drive off any water therein prior to adding said isocyanate compound to said polyether or polyester.
Claim 13
Dependent Claim
45 words
The method of claim 9 wherein said polyether or polyester compound comprises polyethylene glycol (PEG) having a molecular weight of between about 1000 and 3000, and said PEG is heated to at least about 175° C. before said isocyanate compound is added to said PEG.
Claim 14
Dependent Claim
37 words
The method of claim 10 wherein said isocyanate compound comprises tolylene diisocyanate and said heated PEG is allowed to cool to between about 120° C. and 235° C. before said tolylene diisocyanate is added to said PEG.
Claim 15
Independent Claim
145 words
A method of forming a hydrophilic urethane prepolymer, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; and, (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer.
Claim 16
Independent Claim
145 words
A method of forming a hydrophilic urethane prepolymer, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; and, (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer.
Claim 17
Dependent Claim
42 words
The method of claim 12 wherein the surface area of the interface between said polyester or polyether layer and said isocyanate layer is controlled in order to control the rate of reaction between said isocyanate compound and said polyether or polyester compound.
Claim 18
Dependent Claim
12 words
The product of the method of claim 9, 10, 11 or 13.
Claim 19
Dependent Claim
141 words
A consolidated aggregate material in the form of an integral, resilient, water-permeable mass prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with excess isocyanate groups in said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 20
Dependent Claim
141 words
A consolidated aggregate material in the form of an integral, resilient, water-permeable mass prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with excess isocyanate groups in said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 21
Dependent Claim
172 words
A consolidated aggregate material in the form of an internal, resilient, water-permeable mass prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate is greater than about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate are formed; (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with excess isocyanate groups in said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 22
Dependent Claim
172 words
A consolidated aggregate material in the form of an internal, resilient, water-permeable mass prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate is greater than about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate are formed; (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with excess isocyanate groups in said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 23
Dependent Claim
93 words
A hydrophilic urethane prepolymer prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; and, (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer.
Claim 24
Dependent Claim
93 words
A hydrophilic urethane prepolymer prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; and, (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer.
Claim 25
Dependent Claim
142 words
A hydrophilic urethane prepolymer prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without adding mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlapping said isocyanate layer are formed (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer.
Claim 26
Dependent Claim
142 words
A hydrophilic urethane prepolymer prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is greater than about 120° C.; the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without adding mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlapping said isocyanate layer are formed (b) allowing said reaction to proceed in order to form a hydrophilic urethane prepolymer.
References Cited (Backward Citations)
US3373009A
Cited
US3479325A
Cited
US3814736A
Cited
US3805532A
Cited
US3805531A
Cited
US3805532B1
Cited
US3723393A
Cited
US3812619A
Cited
US4241537A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-10 | 1985-11-09 | 1986-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-10 | 1989-11-09 | 1990-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-10 | 1993-11-09 | 1994-05-11 | $7700.00 | Window Closed / Lapsed |