Novel fluorinated copolymer with tridihydro fluorosulfonyl fluoride pendant groups and preparation thereof
Assignee: Asahi Kasei Corp
•
Filing: 1980-05-23
•
Granted: 1982-05-11
•
Expires: 2000-05-23
Abstract
Abstract A novel fluorinated copolymer is prepared by copolymerization of a fluorinated olefin with a novel sulfur containing fluorinated vinyl ether of the formula: ##STR1## wherein k is 0 or 1 and l is an integer of 3 to 5, which is prepared from starting materials which are also novel. Said copolymer is useful for preparation of a fluorinated cation exchange membrane having carboxylic acid groups and/or sulfonic acid groups which can be used advantageously in electrolysis of an aqueous alkali metal halide solution with improved electrolysis performance.
Inventors
- 👤 Kyoji Kimoto
- 👤 Hirotsugu Miyauchi
- 👤 Jukichi Ohmura
- 👤 Mikio Ebisawa
- 👤 Toshioki Hane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 13:15
CPC Classifications
C; C07; C07C; C07C309/00; C07C309/78; C07C309/79; C07C309/82; C07C309/84; C07C317/00; C07C317/16; C07C317/18; C07C323/00; C07C323/10; C07C323/11; C07C323/12; C07D; C07D327/00; C07D327/02; C07D327/04; C08; C08F; C08F214/00; C08F214/02; C08F214/04; C08F214/08; C08F214/18; C08F214/184; C08F214/26; C08F214/262; C08F216/00; C08F216/12; C08F216/14; C08F216/1466; C08F216/1475; C08F8/00; C08F8/04; C08F8/12; C08J; C08J5/00; C08J5/20; C08J5/22; C08J5/2206; C08J5/2218; C08J5/2231; C08J5/2237; C25; C25B; C25B13/00; C25B13/04; C25B13/08; C08J2327/00; C08J2327/02; C08J2327/12
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
151 words
A fluorinated copolymer, consisting essentially of the following recurring units (A) and (B): (A)--CA.sub.1 A.sub.2 --CA.sub.3 A.sub.4 -- (A) wherein each of A 1 and A 2 is F or H; A 3 is F, Cl or H; and A 4 is F, Cl, CF 3 , --OR F or CH 3 , R F being C 1 -C 5 perfluoroalkyl, ##STR60## wherein k is 0 or 1, l is an integer of 3 to 5, the molar ratio of units (A) (B) being from 1 to 16, said copolymer being substantially a random copolymer having a molecular weight generally in the range from 8,000 to 1,000,000 and having a melt index generally in the range from 0.001 g/10 min. to 500 g/10 min., as measured by the use of an orifice of 2.1 mm in diameter and 8 mm in length, under a load of 2.16 kg at 250° C.
Claim 2
Dependent Claim
151 words
A fluorinated copolymer, consisting essentially of the following recurring units (A) and (B): (A)--CA.sub.1 A.sub.2 --CA.sub.3 A.sub.4 -- (A) wherein each of A 1 and A 2 is F or H; A 3 is F, Cl or H; and A 4 is F, Cl, CF 3 , --OR F or CH 3 , R F being C 1 -C 5 perfluoroalkyl, ##STR60## wherein k is 0 or 1, l is an integer of 3 to 5, the molar ratio of units (A) (B) being from 1 to 16, said copolymer being substantially a random copolymer having a molecular weight generally in the range from 8,000 to 1,000,000 and having a melt index generally in the range from 0.001 g/10 min. to 500 g/10 min., as measured by the use of an orifice of 2.1 mm in diameter and 8 mm in length, under a load of 2.16 kg at 250° C.
Claim 3
Dependent Claim
36 words
A copolymer according to claim 1 wherein the recurring unit (A) has the following formula: ##STR61## wherein L is F, Cl, CF 3 , --R F or hydrogen, R F being C 1 -C 5 perfluoroalkyl.
Claim 4
Dependent Claim
13 words
A copolymer according to claim 1 or claim 2, wherein k is 0.
Claim 5
Dependent Claim
13 words
A copolymer according to claim 1 or claim 2, wherein l is 3.
Claim 6
Dependent Claim
17 words
A copolymer according to claim 1 or claim 2, wherein the ratio (A)/(B) is 1.5 to 14.
Claim 7
Dependent Claim
20 words
A copolymer according to claim 1 or claim 2, wherein the copolymer is shaped in the form of a membrane.
Claim 8
Dependent Claim
83 words
A process for producing a fluorinated copolymer as defined in claim 1, which comprises copolymerizing an olefin represented by the formula: CA.sub.1 A.sub.2 ═CA.sub.3 A.sub.4 wherein A 1 , A 2 , A 3 and A 4 have the same meanings as defined in claim 1 with a sulfur containing fluorinated vinylether represented by the formula: ##STR62## wherein k is 0 or 1 and l is an integer of 3 to 5, in a solvent in the presence of a free radical initiator.
Claim 9
Dependent Claim
29 words
A process according to claim 7, wherein the free radical initiator is selected from the group consisting of redox catalysts, organic peroxides, azo-bis type compounds and fluorine radical initiators.
Claim 10
Dependent Claim
16 words
A process according to claim 7, wherein the solvent is water of a fluorinated organic solvent.
Claim 11
Dependent Claim
31 words
A process according to claim 7, wherein the polymerization is carried out at a temperature of 20° to 100° C. and under a pressure of 1 to 50 kg/cm 2 .
Claim 12
Dependent Claim
196 words
A process for producing a fluorinated cation exchange membrane having both carboxylic acid groups and sulfonic acid groups, which comprises subjecting one surface layer of a membrane of a fluorinated copolymer comprising essentially the following recurring units (C) and (B): ##STR63## wherein L is F, Cl, CF 3 , -OR F or H, R F being C 1 -C 5 perfluoroalkyl, ##STR64## wherein k is 0 or 1, and l is an integer of 3 to 5, to treatment with an aqueous solution of at least one reducing agent selected from the group consisting of inorganic acids having reducing ability, salts thereof and hydrazines in the presence of at least one organic compound having 1 to 12 carbon atoms selected from the group consisting of alcohols, carboxylic acids, sulfonic acids, nitriles and ethers, said copolymer being substantially a random copolymer having a molecular weight generally in the range from 8,000 to 1,000,000 and having a melt index generally in the range from 0.001 g/10 min. to 500 g/10 min., as measured by the use of an orifice of 2.1 mm in diameter and 8 mm in length, under a load of 2.16 kg at 250° C.
Claim 13
Dependent Claim
196 words
A process for producing a fluorinated cation exchange membrane having both carboxylic acid groups and sulfonic acid groups, which comprises subjecting one surface layer of a membrane of a fluorinated copolymer comprising essentially the following recurring units (C) and (B): ##STR63## wherein L is F, Cl, CF 3 , -OR F or H, R F being C 1 -C 5 perfluoroalkyl, ##STR64## wherein k is 0 or 1, and l is an integer of 3 to 5, to treatment with an aqueous solution of at least one reducing agent selected from the group consisting of inorganic acids having reducing ability, salts thereof and hydrazines in the presence of at least one organic compound having 1 to 12 carbon atoms selected from the group consisting of alcohols, carboxylic acids, sulfonic acids, nitriles and ethers, said copolymer being substantially a random copolymer having a molecular weight generally in the range from 8,000 to 1,000,000 and having a melt index generally in the range from 0.001 g/10 min. to 500 g/10 min., as measured by the use of an orifice of 2.1 mm in diameter and 8 mm in length, under a load of 2.16 kg at 250° C.
Claim 14
Dependent Claim
28 words
A process according to claim 11, wherein said membrane surface layer is treated with a mixed solution containing the organic compound dissolved in the aqueous reducing agent solution.
Claim 15
Dependent Claim
13 words
A process according to claim 11, wherein the reducing agent is a hydrazine.
Claim 16
Dependent Claim
108 words
A process for producing a fluorinated cation exchange membrane according to claim 11 which is reinforced with a reinforcing material, wherein the membrane employed is a membrane of a fluorinated copolymer having a reinforcing material embedded therein by providing a pressure difference between both sides of the membrane, while maintaining the temperature of the surface of the membrane opposite to that contacted with a reinforcing material at no higher than 20° C. greater than the melting point of the membrane and the temperature of the surface of the membrane contacted with the reinforcing material at higher by at least 60° C. than the melting point of the membrane.
Claim 17
Dependent Claim
136 words
A process for producing a fluorinated cation exchange membrane having sulfonic acid groups, which comprises hydrolyzing the pendant terminal groups of a membrane of a fluorinated copolymer comprising essentially the following recurring units (C) and (B): ##STR65## wherein L is F, Cl, CF 3 , OR F or H, R F being C 1 -C 5 perfluoroalkyl, ##STR66## wherein k is 0 or 1, and l is an integer of 3 to 5, said copolymer being substantially a random copolymer having a molecular weight generally in the range from 8,000 to 1,000,000 and having a melt index generally in the range from 0.001 g/10 min. to 500 g/10 min., as measured by the use of an orifice of 2.1 mm in diameter and 8 mm in length, under a load of 2.16 kg at 250° C.
Claim 18
Dependent Claim
136 words
A process for producing a fluorinated cation exchange membrane having sulfonic acid groups, which comprises hydrolyzing the pendant terminal groups of a membrane of a fluorinated copolymer comprising essentially the following recurring units (C) and (B): ##STR65## wherein L is F, Cl, CF 3 , OR F or H, R F being C 1 -C 5 perfluoroalkyl, ##STR66## wherein k is 0 or 1, and l is an integer of 3 to 5, said copolymer being substantially a random copolymer having a molecular weight generally in the range from 8,000 to 1,000,000 and having a melt index generally in the range from 0.001 g/10 min. to 500 g/10 min., as measured by the use of an orifice of 2.1 mm in diameter and 8 mm in length, under a load of 2.16 kg at 250° C.
Claim 19
Dependent Claim
10 words
A copolymer according to claim 3, wherein l is 3.
Claim 20
Dependent Claim
14 words
A copolymer according to claim 3, wherein the ratio (A)/(B) is 1.5 to 14.
Claim 21
Dependent Claim
14 words
A copolymer according to claim 4, wherein the ratio (A)/(B) is 1.5 to 14.
Claim 22
Dependent Claim
17 words
A copolymer according to claim 3, wherein the copolymer is shaped in the form of a membrane.
Claim 23
Dependent Claim
17 words
A copolymer according to claim 4, wherein the copolymer is shaped in the form of a membrane.
Claim 24
Dependent Claim
17 words
A copolymer according to claim 5, wherein the copolymer is shaped in the form of a membrane.
Claim 25
Dependent Claim
21 words
A copolymer according to claim 3, wherein A 1 , A 2 , A 3 and A 4 are each F.
Claim 26
Dependent Claim
21 words
A copolymer according to claim 4, wherein A 1 , A 2 , A 3 and A 4 are each F.
Claim 27
Dependent Claim
21 words
A copolymer according to claim 5, wherein A 1 , A 2 , A 3 and A 4 are each F.
Claim 28
Dependent Claim
21 words
A copolymer according to claim 6, wherein A 1 , A 2 , A 3 and A 4 are each F.
Claim 29
Dependent Claim
21 words
A process according to claim 7, wherein A 1 , A 2 , A 3 and A 4 are each F.
Claim 30
Dependent Claim
10 words
A process according to claim 11, wherein L is F.
Claim 31
Dependent Claim
10 words
A process according to claim 15, wherein L is F.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-10 | 1985-11-09 | 1986-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-10 | 1989-11-09 | 1990-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-10 | 1993-11-09 | 1994-05-11 | $7700.00 | Window Closed / Lapsed |