Alloy resistant to corrosion
Assignee: Carondelet Foundry Co
•
Filing: 1980-03-31
•
Granted: 1982-05-11
•
Expires: 2000-03-31
Abstract
Abstract An air-meltable, castable, weldable, nonmagnetic alloy resistant to corrosion in sulfuric acid over a wide range of acid strengths. The alloy consists essentially of between about 18 and about 22% by weight nickel, between about 16.8 and 19.2% by weight chromium, between about 0.35 and about 1.95% by weight molybdenum, between about 2.5 and about 3.9% by weight copper, between about 3.2 and about 4.7% by weight manganese, between about 0.35% and 0.80% by weight niobium, up to about 0.7% by weight titanium, up to about 0.4% by weight tantalum, up to about 0.01% by weight boron, up to about 0.5% by weight cobalt, up to about 0.7% by weight silicon, up to about 0.08% by weight carbon, up to about 0.6% by weight of a rare earth component selected from the group consisting of cerium, lanthanum, and misch metal, up to about 0.15% by weight nitrogen, and between about 51% and about 58% by weight iron. The nickel content exceeds the chromium content by about 0.85% to about 5.2% by weight.
Inventors
- 👤 John H. Culling
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:22
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/18; C22C38/40; C22C38/58
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
179 words
An air-meltable, castable, weldable, nonmagnetic alloy resistant to corrosion in sulfuric acid over a wide range of acid strengths, consisting essentially of between about 18 and about 22% by weight nickel, between about 16.8 and about 19.2% by weight chromium, between about 0.35 and about 1.95% by weight molybdenum, between about 2.5 and about 3.9% by weight copper, between about 3.2 and about 4.7% by weight manganese, between about 0.35 and about 0.80% by weight niobium, up to about 0.7% by weight titanium, up to about 0.4% by weight tantalum, up to about 0.01% by weight boron, up to about 0.5% by weight cobalt, up to about 0.7% by weight silicon, up to about 0.08% by weight carbon, up to about 0.6% by weight of a rare earth component selected from the group consisting of cerium, lanthanum and misch metal, up to about 0.15% by weight nitrogen, and between about 51 and about 58% by weight iron, and wherein the nickel content exceeds the chromium content by between about 0.85 and about 5.2% by weight (basis, the entire alloy).
Claim 2
Dependent Claim
179 words
An air-meltable, castable, weldable, nonmagnetic alloy resistant to corrosion in sulfuric acid over a wide range of acid strengths, consisting essentially of between about 18 and about 22% by weight nickel, between about 16.8 and about 19.2% by weight chromium, between about 0.35 and about 1.95% by weight molybdenum, between about 2.5 and about 3.9% by weight copper, between about 3.2 and about 4.7% by weight manganese, between about 0.35 and about 0.80% by weight niobium, up to about 0.7% by weight titanium, up to about 0.4% by weight tantalum, up to about 0.01% by weight boron, up to about 0.5% by weight cobalt, up to about 0.7% by weight silicon, up to about 0.08% by weight carbon, up to about 0.6% by weight of a rare earth component selected from the group consisting of cerium, lanthanum and misch metal, up to about 0.15% by weight nitrogen, and between about 51 and about 58% by weight iron, and wherein the nickel content exceeds the chromium content by between about 0.85 and about 5.2% by weight (basis, the entire alloy).
Claim 3
Dependent Claim
29 words
An alloy as set forth in claim 1 wherein the nickel content exceeds the chromium content by between about 0.87 and about 4.74% by weight (basis, the entire alloy).
Claim 4
Dependent Claim
94 words
An alloy as set forth in claim 2 wherein the nickel content is between about 18.66% and about 21.58% by weight, the chromium contact is between about 16.84 and about 19.01% by weight, the molybdenum content is between about 0.52 and about 1.93% by weight, the copper content is between about 2.51 and about 3.24% by weight, the manganese content is between about 3.29 and about 4.54% by weight, the niobium content is between about 0.45 and about 0.68% by weight and the iron content is between about 51.05 and about 55.14% by weight.
Claim 5
Dependent Claim
113 words
An alloy as set forth in claim 1 wherein the nickel content is between about 18.66 and about 21.58% by weight, the chromium content is between about 16.84 and about 18.76% by weight, the molybdenum content is between about 0.52 and about 1.93% by weight, the copper content is between about 2.82 and about 3.18% by weight, the manganese content is between about 3.30 and about 3.70% by weight, the niobium content is between about 0.56 and about 0.68% by weight, the iron content is between about 51.05 and 55.13% by weight and the nickel content exceeds the chromium content by between about 1.82 and about 4.11% by weight (basis, the entire alloy).
Claim 6
Dependent Claim
138 words
An alloy as set forth in claim 1 wherein the nickel content is between about 18.6 and about 21.6% by weight, the chromium content is between about 17.20 and about 18.76% by weight, the molydenum content is between about 0.52 and about 1.93% by weight, the copper content is between about 2.82 and about 3.17% by weight, the manganese content is between about 3.30 and about 3.51% by weight, the niobium content is between about 0.56 and about 0.68% by weight, the silicon content is between about 0.3 and about 0.5% by weight, the carbon content is between about 0.03 and about 0.05% by weight, the iron content is between about 51.05 and about 55.13% by weight, and the nickel content exceeds the chromium content by between about 2.18 and about 4.11% by weight (basis, the entire alloy).
Claim 7
Dependent Claim
21 words
An alloy as set forth in claim 1 wherein the carbon content does not exceed approximately one-eighth of the niobium content.
Claim 8
Dependent Claim
65 words
An air-meltable, castable, weldable, nonmagnetic alloy resistant to corrosion in sulfuric acid over a wide range of acid strengths, comprising approximately 21.0% by weight nickel, approximately 17.5% by weight chromium, approximately 1.2% by weight molybdenum, approximately 3.1% by weight copper, approximately 3.7% by weight manganese, approximately 0.6% by weight niobium, approximately 0.3% by weight silicon, approximately 0.03% by weight carbon, and the balance essentially iron.
Claim 9
Dependent Claim
65 words
An air-meltable, castable, weldable, nonmagnetic alloy resistant to corrosion in sulfuric acid over a wide range of acid strengths, comprising approximately 21.0% by weight nickel, approximately 17.5% by weight chromium, approximately 1.2% by weight molybdenum, approximately 3.1% by weight copper, approximately 3.7% by weight manganese, approximately 0.6% by weight niobium, approximately 0.3% by weight silicon, approximately 0.03% by weight carbon, and the balance essentially iron.
References Cited (Backward Citations)
US2633420A
Cited
US2553330A
Cited
US2777766A
Cited
US3048485A
Cited
US3044871A
Cited
US3168397A
Cited
GB1062658A
Cited
US3547625A
Cited
US3856516A
Cited
US3758294A
Cited
US3758296A
Cited
US3759704A
Cited
US3813239A
Cited
US4172716A
Cited
US3947266A
Cited
US4135919A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-10 | 1985-11-09 | 1986-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-10 | 1989-11-09 | 1990-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-10 | 1993-11-09 | 1994-05-11 | $7700.00 | Window Closed / Lapsed |