US4325987A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the production of an electrically conducting article
Assignee: Societa Italiana Vetro SIV SpA
•
Filing: 1981-01-08
•
Granted: 1982-04-20
•
Expires: 2001-01-08
Abstract
Abstract Substrate of glass or other mineral material covered with a coating of SnO2 whose electrical conductivity, transparency in the visible spectrum and thermal reflectivity are very high. This coating is obtained by the technique of vapor phase chemical deposition (CVD), by reacting a volatile tin compound with water vapor in the presence of hydrogen, on the heated substrate surface. The reaction mixture may also inclue HF. The coated substrate is suitable for electrically heated glazing.
Inventors
- 👤 Reinhard Kalbskopf
- 👤 Otto Baumberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:38
CPC Classifications
H; H05; H05B; H05B3/00; H05B3/84; C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/245; C03C17/2453; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/407; H10; H10F; H10F71/00; H10F71/138; H05B2203/00; H05B2203/017; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y10; Y10S; Y10S428/00; Y10S428/913; Y10S428/918; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
62 words
A process for forming on a mineral substrate an adherent coating of stannic oxide having a resistivity below 10 -2 Ω cm, comprising heating the substrate to at least 500° C. and reacting on the heated substrate's surface a volatile tin compound and water vapor diluted in a carrier gas containing at least 30% hydrogen, thereby depositing said coating on said substrate.
Claim 2
Dependent Claim
62 words
A process for forming on a mineral substrate an adherent coating of stannic oxide having a resistivity below 10 -2 Ω cm, comprising heating the substrate to at least 500° C. and reacting on the heated substrate's surface a volatile tin compound and water vapor diluted in a carrier gas containing at least 30% hydrogen, thereby depositing said coating on said substrate.
Claim 3
Dependent Claim
47 words
A process as claimed in claim 1 wherein the substrate is a laminar article and wherein the coating is deposited to a thickness of 1 to 3 μm and has a surface resistance of 1-10Ω, a transparency of 60-95% and an IR reflectivity not less than 50%.
Claim 4
Dependent Claim
31 words
A process according to claim 1 in which hydrogen fluoride gas is added to the reaction mixture to reduce stray dispersion and scattering of light in the stannic oxide coating formed.
Claim 5
Dependent Claim
27 words
A process according to claim 3 in which the hydrogen fluoride gas is provided in admixture with water in an amount of 0.1 to 5% by weight.
Claim 6
Dependent Claim
40 words
A process according to claim 1 in which after formation of a first layer of stannic oxide, the coating deposition is repeated at least one further time to form a coating comprising at least two superimposed layers of stannic oxide.
Claim 7
Dependent Claim
24 words
A process according to claim 5 in which the thickness of each of the individual layers forming the coating is 10 to 500 μm.
Claim 8
Dependent Claim
85 words
A process for forming on a mineral substrate an adherent coating of stannic oxide having a resistivity below 10 -2 Ω cm, comprising heating the substrate to at least 500° C. and reacting on the heated substrate's surface a volatile tin compound and water vapor diluted in a carrier gas, which carrier gas contains a compound capable of thermally decomposing in the presence of the heated substrate to provide at least 30% hydrogen relative to said carrier gas, thereby depositing said coating on said substrate.
Claim 9
Dependent Claim
85 words
A process for forming on a mineral substrate an adherent coating of stannic oxide having a resistivity below 10 -2 Ω cm, comprising heating the substrate to at least 500° C. and reacting on the heated substrate's surface a volatile tin compound and water vapor diluted in a carrier gas, which carrier gas contains a compound capable of thermally decomposing in the presence of the heated substrate to provide at least 30% hydrogen relative to said carrier gas, thereby depositing said coating on said substrate.
Claim 10
Dependent Claim
13 words
The process of claim 7, wherein the compound providing the hydrogen is methanol.
References Cited (Backward Citations)
FR1207231A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-19 | 1985-10-19 | 1986-04-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-19 | 1989-10-19 | 1990-04-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-19 | 1993-10-19 | 1994-04-20 | $7700.00 | Window Closed / Lapsed |