US4323655A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Rubber-modified fire-retardant anhydride copolymers
Assignee: Lyondell Chemical Technology LP
•
Filing: 1981-02-17
•
Granted: 1982-04-06
•
Expires: 2001-02-17
Abstract
Abstract Rubber-modified copolymers of monovinyl aromatic monomers and the anhydride of ethylenically unsaturated dicarboxylic acid monomers are blended with water as a blowing agent, bromodiphenylethers as fire retardants, and metal oxides as synergist for the ethers to form a composition which can be foamed to densities of between 1 and 10 pounds per cubic foot, said foam composition having fire-retardant properties.
Inventors
- 👤 Adolph V. DiGiulio
- 👤 Jack N. Bauer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:49
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/125; C08J9/0061; Y; Y10; Y10S; Y10S264/00; Y10S264/05
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
160 words
A fire-retardant foam composition having a density of between 1 and 10 pounds per cubic foot and consisting of a rubber-modified copolymer, from 10 to 20 parts per hundred parts of copolymer of an at least tribrominated diphenylether, and 4 to 8 parts per hundred parts of copolymer of a metal oxide synergist for the ether; said rubber-modified copolymer consisting of (a) 5 to 40 weight percent of a rubber, selected from the group consisting of homopolymers of butadiene, isoprene, chloroprene and piperylene; copolymers of said conjugated diene with up to 50 weight percent of one or more monoolefinically unsaturated monomers selected from the group consisting of styrene, substituted styrenes, acrylonitrile, methacrylonitrile and isobutylene; ethylenepropylene-diene terpolymer rubbers; acrylate-diene copolymer rubbers; and mixtures thereof and (b) 60 to 95 weight percent of a copolymer of 50 to 95 mole percent of a monovinyl aromatic monomer and 5 to 50 mole percent of the anhydride of an ethylenically unsaturated dicarboxylic acid monomer.
Claim 2
Dependent Claim
160 words
A fire-retardant foam composition having a density of between 1 and 10 pounds per cubic foot and consisting of a rubber-modified copolymer, from 10 to 20 parts per hundred parts of copolymer of an at least tribrominated diphenylether, and 4 to 8 parts per hundred parts of copolymer of a metal oxide synergist for the ether; said rubber-modified copolymer consisting of (a) 5 to 40 weight percent of a rubber, selected from the group consisting of homopolymers of butadiene, isoprene, chloroprene and piperylene; copolymers of said conjugated diene with up to 50 weight percent of one or more monoolefinically unsaturated monomers selected from the group consisting of styrene, substituted styrenes, acrylonitrile, methacrylonitrile and isobutylene; ethylenepropylene-diene terpolymer rubbers; acrylate-diene copolymer rubbers; and mixtures thereof and (b) 60 to 95 weight percent of a copolymer of 50 to 95 mole percent of a monovinyl aromatic monomer and 5 to 50 mole percent of the anhydride of an ethylenically unsaturated dicarboxylic acid monomer.
Claim 3
Dependent Claim
33 words
The foam composition of claim 1 wherein the synergist for the ether is a metal oxide selected from the group consisting of antimony trioxide, bismuth oxide, molybdenum oxide, stannic oxide and tungsten oxide.
Claim 4
Dependent Claim
33 words
The foam composition of claim 1 wherein the monovinyl aromatic monomer of said copolymer is selected from the group consisting of styrene, alpha-methylstyrene, nuclear-methylstyrenes, ethylstyrenes, isopropylstyrenes, tert-butylstyrenes, chlorostyrenes, dichlorostyrenes, vinyl-naphthalene and mixtures thereof.
Claim 5
Dependent Claim
26 words
The foam composition of claim 1 wherein the diphenylether is selected from the group consisting of tribromodiphenylether, tetrabromodiphenylether, pentabromodiphenylether, tribromochlorodiphenylether, tribromodichlorodiphenylether, tribromotrichlorodiphenylether, tetrabromodichlorodiphenylether, octabromodiphenylether and decabromodiphenylether.
Claim 6
Dependent Claim
50 words
The foam composition of claim 1 wherein the anhydride consists of the anhydride of an ethylenically unsaturated dicarboxylic acid selected from the group consisting of maleic acid, fumaric acid, itaconic acid, citraconic acid, mesaconic acid, ethylmaleic acid, methylitaconic acid, chloromaleic acid, dichloromaleic acid, bromomaleic acid, dibromomaleic acid and mixtures thereof.
References Cited (Backward Citations)
US3676378A
Cited
US4207402A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-05 | 1985-10-05 | 1986-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-05 | 1989-10-05 | 1990-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-05 | 1993-10-05 | 1994-04-06 | $7700.00 | Window Closed / Lapsed |