Photopolymerizable compositions containing elastomers and photo-curable elements made therefrom
Assignee: BASF SE
•
Filing: 1980-10-17
•
Granted: 1982-03-16
•
Expires: 2000-10-17
Abstract
Abstract Photopolymerizable compositions based on an elastomeric styrene-diene block polymer, one or more photopolymerizable olefinically unsaturated monomers and one or more photopolymerization initiators exhibit improved properties if they contain, as an essential constituent, an elastomeric block copolymer of the general structure A-B-C, where A is a thermoplastic, non-elastomeric polymer block based on styrene compounds and having a second order transition point above +25° C., B is an elastomeric polymer block based on butadiene and/or isoprene and having a second order transition point below -20° C. and C is a polymer block, different from B, having a second order transition point of from -30° C. to +15° C., C being either a homopolymer or copolymer block based on butadiene or isoprene or a random copolymer block based on conjugated dienes and styrene compounds. The photopolymerizable compositions may be used, inter alia, for the production of photo-curable adhesives, resilient and flexible sheet material and, in particular, flexographic relief printing plates.
Inventors
- 👤 Gerhard Heinz
- 👤 Peter Richter
- 👤 Mong-Jon Jun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 03:42
CPC Classifications
C; C08; C08F; C08F287/00; G; G03; G03F; G03F7/00; G03F7/004; G03F7/027; G03F7/032; G03F7/033; Y; Y10; Y10S; Y10S430/00; Y10S430/1053; Y10S430/1055; Y10S430/106; Y10S430/111
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
279 words
A photopolymerizable composition which contains (a) not less than 40% by weight of at least one elastomeric block copolymer which is soluble in developer solutions and has the structure A-B-C, where A, B and C are different polymer blocks linked chemically to one another, in which (a1) the polymer block A, accounting for from 5 to 25% by weight of the block copolymer, is prepared by polymerizing at least one styrene monomer of the formula CH 2 ═CRR' where R is hydrogen or methyl and R' is phenyl or C 1 -C 4 -alkyl-substituted phenyl, and has a second order transition point above +25° C., (a2) the polymer block B which accounts for from 15 to 90% by weight of the block copolymer is prepared by polymerizing at least one aliphatic diene hydrocarbon of 4 or 5 carbon atoms and has a second order transition point below -20° C., and (a3) the polymer block C which accounts for from 5 to 60% by weight of the block copolymer is prepared by homopolymerization or copolymerization of aliphatic diene hydrocarbons of 4 or 5 carbon atoms or by random copolymerization of at least one aliphatic diene hydrocarbon of 4 or 5 carbon atoms with at least one styrene monomer of the formula CH 2 ═CRR', where R is hydrogen or methyl and R' is phenyl or C 1 -C 4 -alkyl-substituted phenyl, and has a second order transition point of from -20° C. to +15° C. (b) not less than 1% by weight of at least one photopolymerizable olefinically unsaturated monomer compatible with the block copolymer (a) and (c) from 0.1 to 10% by weight of at least one photopolymerization initiator.
Claim 2
Dependent Claim
279 words
A photopolymerizable composition which contains (a) not less than 40% by weight of at least one elastomeric block copolymer which is soluble in developer solutions and has the structure A-B-C, where A, B and C are different polymer blocks linked chemically to one another, in which (a1) the polymer block A, accounting for from 5 to 25% by weight of the block copolymer, is prepared by polymerizing at least one styrene monomer of the formula CH 2 ═CRR' where R is hydrogen or methyl and R' is phenyl or C 1 -C 4 -alkyl-substituted phenyl, and has a second order transition point above +25° C., (a2) the polymer block B which accounts for from 15 to 90% by weight of the block copolymer is prepared by polymerizing at least one aliphatic diene hydrocarbon of 4 or 5 carbon atoms and has a second order transition point below -20° C., and (a3) the polymer block C which accounts for from 5 to 60% by weight of the block copolymer is prepared by homopolymerization or copolymerization of aliphatic diene hydrocarbons of 4 or 5 carbon atoms or by random copolymerization of at least one aliphatic diene hydrocarbon of 4 or 5 carbon atoms with at least one styrene monomer of the formula CH 2 ═CRR', where R is hydrogen or methyl and R' is phenyl or C 1 -C 4 -alkyl-substituted phenyl, and has a second order transition point of from -20° C. to +15° C. (b) not less than 1% by weight of at least one photopolymerizable olefinically unsaturated monomer compatible with the block copolymer (a) and (c) from 0.1 to 10% by weight of at least one photopolymerization initiator.
Claim 3
Dependent Claim
30 words
A photopolymerizable composition as claimed in claim 1, which contains a block copolymer having the structure A-B-C, in which the polymer block C is incompatible with the polymer block A.
Claim 4
Dependent Claim
43 words
A photopolymerizable composition as claimed in claim 1, which contains a block copolymer A-B-C, in which the polymer block C is a polybutadiene block exhibiting more than 70% by weight of 1,2-configuration and having a mean molecular weight of from 10,000 to 90,000.
Claim 5
Dependent Claim
43 words
A photopolymerizable composition as claimed in claim 1, which contains a block copolymer A-B-C, in which the polymer block C is a polyisoprene block exhibiting more than 40% by weight of 3,4-configuration and having a mean molecular weight of from 10,000 to 90,000.
Claim 6
Dependent Claim
100 words
A photopolymerizable composition as claimed in claim 1, which contains a block copolymer A-B-C, in which the polymer block C is a random copolymer block which contains from 70 to 30% by weight of at least one diene hydrocarbon of 4 or 5 carbon atoms as copolymerized units and from 30 to 70% by weight of a styrene monomer of the formula CH 2 ═CRR', where R is hydrogen or methyl and R' is phenyl or C 1 -C 4 -alkyl-substituted phenyl, as copolymerized units, and which has a second order transition point of from -20° C. to +15° C.
Claim 7
Dependent Claim
26 words
A photopolymerizable composition as claimed in claim 5, wherein the polymer block C accounts for from 5 to 35% by weight of the block copolymer A-B-C.
Claim 8
Dependent Claim
45 words
A photopolymerizable composition as claimed in any of claims 1 to 6, in which the block copolymer A-B-C has an intrinsic viscosity in the range of from about 60 to 350 ml/g, measured on an 0.5% strength by weight solution in toluene at 25° C.
Claim 9
Dependent Claim
15 words
A photopolymerizable composition as claimed in claim 1, which additionally contains admixed compatible tackifying resins.
Claim 10
Dependent Claim
13 words
A photopolymerizable composition as claimed in claim 1, which additionally contains admixed plasticizer.
Claim 11
Dependent Claim
23 words
Photo-curable elements possessing a photopolymerizable layer on a base, wherein the photopolymerizable layer consists of a photopolymerizable composition as claimed in claim 1.
References Cited (Backward Citations)
US2948611A
Cited
US3024180A
Cited
US3674486A
Cited
DE2138582A1
Cited
DE2215090C3
Cited
DE2223808A1
Cited
US3798035A
Cited
DE2364873A1
Cited
US3951657A
Cited
US4162919A
Cited
DE2610206A1
Cited
DE2631837A1
Cited
DE2720228B2
Cited
DE2815678B2
Cited
US4179531A
Cited
DE2939989A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-15 | 1985-09-14 | 1986-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-15 | 1989-09-14 | 1990-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-15 | 1993-09-14 | 1994-03-16 | $7700.00 | Window Closed / Lapsed |